ANÁLISE COMPARATIVA DAS PROPRIEDADES MECÂNICAS E FÍSICAS DO CONCRETO COM ADIÇÃO DE POLÍMEROS – REVISÃO BIBLIOGRÁFICA

Historically, concrete, understood as a construction material, is described as an artificial stone resulting from the junction of a binder with stone materials. Nevertheless, it can still be said that it may be as old as the very concept of civilization. When concrete is used as a structural material, it is called structural concrete, which can be of three different types: plain concrete without any kind of reinforcement; reinforced concrete when there is a non-pre-trained reinforcement. As for the general objective, it proposed to analyze the main mechanical and physical properties of concrete with the addition of vinyl acetate and polypropylene. The partial replacement of sand by polypropylene had an excellent performance regarding compressive strength due to the good densification of the polymer with the cement paste, low porosity. This is due to the good homogenization that the vibrating table provided to the specimens used in the test. The widely used correlation that the tensile strength of concrete corresponds to 10% of its compressive strength cannot be made freely. One of the main factors affecting the workability conditions of the mixture is the percentage of ethylene vinyl acetate (EVA) aggregate. The mixtures with 60% EVA showed the best results, and the 1:3 mixture presented a plastic consistency without segregation or floating of the aggregate. There is a sustainable potential in the search for alternative resources for making raw materials for civil construction.Históricamente, el hormigón, entendido como material de construcción, se describe como una piedra artificial resultante de la unión de un aglutinante con materiales pétreos. No obstante, puede decirse que puede ser tan antigua como el propio concepto de civilización. Cuando el hormigón se utiliza como material estructural, se denomina hormigón estructural, que puede ser de tres tipos diferentes: hormigón simple sin ningún tipo de refuerzo; hormigón armado cuando hay un refuerzo no preformado. En cuanto al objetivo general, se propuso analizar las principales propiedades mecánicas y físicas del hormigón con adición de acetato de vinilo y polipropileno. La sustitución parcial de la arena por polipropileno tuvo un excelente rendimiento en cuanto a la resistencia a la compresión debido a la buena densificación del polímero con la pasta de cemento, baja porosidad. Esto se debe a la buena homogeneización que la mesa vibratoria proporcionó a las probetas utilizadas en el ensayo. La correlación ampliamente utilizada de que la resistencia a la tracción del hormigón corresponde al 10% de su resistencia a la compresión no puede hacerse libremente. Uno de los principales factores que afectan a las condiciones de trabajabilidad de la mezcla es el porcentaje de agregado de etileno-acetato de vinilo (EVA). Las mezclas con un 60% de EVA mostraron los mejores resultados, presentando la mezcla 1:3 una consistencia plástica sin segregación ni flotación del árido. Existe un potencial sustentable en la búsqueda de recursos alternativos para la confección de materia prima para la construcción civil.Historicamente, o concreto, entendido como um material de construção, é descrito como uma pedra artificial resultante da junção de um ligante com materiais pétreos. Não obstante, ainda se pode afirmar que ele possa ser tão antigo quanto o próprio conceito de civilização. Quando a utilização do concreto é a de material estrutural recebe a denominação de concreto estrutural que pode ser de três tipos diferentes: concreto simples sem qualquer tipo de armadura; concreto armado quando há uma armadura não pré-tracionada. Quanto ao objetivo geral, ele se propôs a analisar as principais propriedades mecânicas e físicas do concreto com adição de acetato de vinila e polipropileno. A substituição parcial da areia pelo polipropileno teve um excelente desempenho quanto à resistência a compressão devido ao bom adensamento do polímero com a massa de cimento, baixa porosidade. Isso se deve a boa homogeneização que a mesa vibratória forneceu aos corpos de prova utilizados no teste. A correlação amplamente utilizada de que a resistência à tração do concreto corresponde a 10% da sua resistência à compressão não pode ser feita livremente. Um dos principais fatores que afetam as condições de trabalhabilidade da mistura é a percentagem de agregado de etileno acetato de vinila (EVA). As misturas com 60% de EVA evidenciaram os melhores resultados, sendo que o traço 1:3 apresentou uma consistência plástica sem segregação nem flutuação do agregado. Existe um potencial sustentável na busca de recursos alternativos para confecção de matéria prima de construção civil.Historicamente, o concreto, entendido como um material de construção é descrito como uma pedra artificial resultante da junção de um ligante com materiais pétreos, não obstante, ainda pode se afirmar que o mesmo possa ser tão antigo quanto o próprio conceito de civilização. Quando a utilização do concreto é a de material estrutural recebe a denominação de concreto estrutural que pode ser de três tipos diferentes: concreto simples sem qualquer tipo de armadura; concreto armado e concreto armado quando há uma armadura não pré-tracionada. Quanto ao objetivo geral o mesmo se propôs a analisar as principais propriedades mecânicas e físicas do concreto com adição de acetato de vinila e polipropileno. A substituição parcial da areia pelo polipropileno teve um excelente desempenho quanto à resistência à compressão devido ao bom adensamento do polímero com a massa de cimento, baixa porosidade, isso se deve a boa homogeneização que a mesa vibratória forneceu aos corpos de prova utilizados no teste. A correlação amplamente utilizada de que a resistência à tração do concreto corresponde a 10% da sua resistência à compressão não pode ser feita livremente. Um dos principais fatores que vem a afetar as condições de trabalhabilidade da mistura é a percentagem de agregado de etileno acetato de vinila (EVA). As misturas com 60% de EVA evidenciaram os melhores resultados, sendo que o traço 1:3 apresentou uma consistência plástica sem segregação nem flutuação do agregado (Garlet,1998). Existe um potencial sustentável na busca de recursos alternativos para confecção de matéria prima de construção civil

ANÁLISE COMPARATIVA DAS PROPRIEDADES MECÂNICAS E FÍSICAS DO CONCRETO COM ADIÇÃO DE POLÍMEROS – REVISÃO BIBLIOGRÁFICA

Historically, concrete, understood as a construction material, is described as an artificial stone resulting from the junction of a binder with stone materials. Nevertheless, it can still be said that it may be as old as the very concept of civilization. When concrete is used as a structural material, it is called structural concrete, which can be of three different types: plain concrete without any kind of reinforcement; reinforced concrete when there is a non-pre-trained reinforcement. As for the general objective, it proposed to analyze the main mechanical and physical properties of concrete with the addition of vinyl acetate and polypropylene. The partial replacement of sand by polypropylene had an excellent performance regarding compressive strength due to the good densification of the polymer with the cement paste, low porosity. This is due to the good homogenization that the vibrating table provided to the specimens used in the test. The widely used correlation that the tensile strength of concrete corresponds to 10% of its compressive strength cannot be made freely. One of the main factors affecting the workability conditions of the mixture is the percentage of ethylene vinyl acetate (EVA) aggregate. The mixtures with 60% EVA showed the best results, and the 1:3 mixture presented a plastic consistency without segregation or floating of the aggregate. There is a sustainable potential in the search for alternative resources for making raw materials for civil construction.Históricamente, el hormigón, entendido como material de construcción, se describe como una piedra artificial resultante de la unión de un aglutinante con materiales pétreos. No obstante, puede decirse que puede ser tan antigua como el propio concepto de civilización. Cuando el hormigón se utiliza como material estructural, se denomina hormigón estructural, que puede ser de tres tipos diferentes: hormigón simple sin ningún tipo de refuerzo; hormigón armado cuando hay un refuerzo no preformado. En cuanto al objetivo general, se propuso analizar las principales propiedades mecánicas y físicas del hormigón con adición de acetato de vinilo y polipropileno. La sustitución parcial de la arena por polipropileno tuvo un excelente rendimiento en cuanto a la resistencia a la compresión debido a la buena densificación del polímero con la pasta de cemento, baja porosidad. Esto se debe a la buena homogeneización que la mesa vibratoria proporcionó a las probetas utilizadas en el ensayo. La correlación ampliamente utilizada de que la resistencia a la tracción del hormigón corresponde al 10% de su resistencia a la compresión no puede hacerse libremente. Uno de los principales factores que afectan a las condiciones de trabajabilidad de la mezcla es el porcentaje de agregado de etileno-acetato de vinilo (EVA). Las mezclas con un 60% de EVA mostraron los mejores resultados, presentando la mezcla 1:3 una consistencia plástica sin segregación ni flotación del árido. Existe un potencial sustentable en la búsqueda de recursos alternativos para la confección de materia prima para la construcción civil.Historicamente, o concreto, entendido como um material de construção, é descrito como uma pedra artificial resultante da junção de um ligante com materiais pétreos. Não obstante, ainda se pode afirmar que ele possa ser tão antigo quanto o próprio conceito de civilização. Quando a utilização do concreto é a de material estrutural recebe a denominação de concreto estrutural que pode ser de três tipos diferentes: concreto simples sem qualquer tipo de armadura; concreto armado quando há uma armadura não pré-tracionada. Quanto ao objetivo geral, ele se propôs a analisar as principais propriedades mecânicas e físicas do concreto com adição de acetato de vinila e polipropileno. A substituição parcial da areia pelo polipropileno teve um excelente desempenho quanto à resistência a compressão devido ao bom adensamento do polímero com a massa de cimento, baixa porosidade. Isso se deve a boa homogeneização que a mesa vibratória forneceu aos corpos de prova utilizados no teste. A correlação amplamente utilizada de que a resistência à tração do concreto corresponde a 10% da sua resistência à compressão não pode ser feita livremente. Um dos principais fatores que afetam as condições de trabalhabilidade da mistura é a percentagem de agregado de etileno acetato de vinila (EVA). As misturas com 60% de EVA evidenciaram os melhores resultados, sendo que o traço 1:3 apresentou uma consistência plástica sem segregação nem flutuação do agregado. Existe um potencial sustentável na busca de recursos alternativos para confecção de matéria prima de construção civil.Historicamente, o concreto, entendido como um material de construção é descrito como uma pedra artificial resultante da junção de um ligante com materiais pétreos, não obstante, ainda pode se afirmar que o mesmo possa ser tão antigo quanto o próprio conceito de civilização. Quando a utilização do concreto é a de material estrutural recebe a denominação de concreto estrutural que pode ser de três tipos diferentes: concreto simples sem qualquer tipo de armadura; concreto armado e concreto armado quando há uma armadura não pré-tracionada. Quanto ao objetivo geral o mesmo se propôs a analisar as principais propriedades mecânicas e físicas do concreto com adição de acetato de vinila e polipropileno. A substituição parcial da areia pelo polipropileno teve um excelente desempenho quanto à resistência à compressão devido ao bom adensamento do polímero com a massa de cimento, baixa porosidade, isso se deve a boa homogeneização que a mesa vibratória forneceu aos corpos de prova utilizados no teste. A correlação amplamente utilizada de que a resistência à tração do concreto corresponde a 10% da sua resistência à compressão não pode ser feita livremente. Um dos principais fatores que vem a afetar as condições de trabalhabilidade da mistura é a percentagem de agregado de etileno acetato de vinila (EVA). As misturas com 60% de EVA evidenciaram os melhores resultados, sendo que o traço 1:3 apresentou uma consistência plástica sem segregação nem flutuação do agregado (Garlet,1998). Existe um potencial sustentável na busca de recursos alternativos para confecção de matéria prima de construção civil