1 research outputs found
Simultaneous application of conventional and experimental silanes on the adhesive strength and marginal infiltration in radicular canal with fiberglass post
Orientador: Rafael Leonardo Xediek ConsaniDissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de PiracicabaResumo: O objetivo neste estudo in vitro foi avaliar o efeito da aplicação simultânea de silanos convencional e experimental na resistência adesiva e micro infiltração marginal em raÃzes de dentes humanos restauradas com pinos de fibra de vidro (PFV) e submetidas à s ciclagens térmica e mecânica. Dois oligômeros foram sintetizados em solução com quantidades catalÃticas de trietilamina. O tiol-pentaeritritol tetra-3-mercaptopropionato multifuncional (PETMP) foi combinado com isocianatos di-funcionais - 1,6-hexanodioldiissocyante (HDDI) (alifático) ou 1,3-bis (1-isocianato-1- metiletil) benzeno (BDI) (aromático). Sessenta pré-molares unirradiculares foram seccionados 2 mm acima da junção cemento-esmalte, receberam tratamento endodôntico convencional e obturação com cones de guta-percha. As raÃzes receberam preparo padronizado em 10 mm de profundidade com brocas de diâmetro 1,4 mm e separadas aleatoriamente em seis grupos (n=10): silanos convencionais (RelyX CP ou Angelus) e experimentais (PETMP-HDDI ou PETMP-BDI). Nos condutos foi aplicado adesivo e nos pinos silanos convencionais conforme recomendado pelos fabricantes, seguido pela aplicação de silanos experimentais. Após cimentação, as raÃzes receberam núcleos de preenchimento em resina composta, coroas de resina indireta e foram submetidas a 1,2 x 106 ciclos mecânicos, seguidos por 500 ciclos térmicos (5 e 55ºC). Duas fatias com 1 mm de espessura foram obtidas de cada terço radicular (cervical, médio e apical). Uma fatia de cada terço foi submetida ao teste de cisalhamento (push-out) e o padrão de fratura analisado (%) e outra fatia submetida à análise de infiltração marginal por corante (imersão em azul de metileno a 2% por sete dias) e a penetração classificada em escores (%). Fatias representativas de cada grupo foram analisadas em MEV quanto a formação de fendas marginais. Os resultados foram analisados com ANOVA dois-fatores (silano e terço), seguido pelo teste de Tukey (push-out) e teste de Kruskal-wallis (micro infiltração marginal) com nÃvel de significância de ?=0,05. A aplicação simultânea de silanos convencional e experimental aumentou a resistência da união adesiva de PFV (p<0,001), com valores similares entre terços radiculares (p=0,199), reduziu as falhas adesivas dentina-cimento e aumentou as coesivas em dentina. Não houve diferença significante nos escores de micro infiltração por corante entre os grupos (p=0,176). Todos os grupos apresentaram micro infiltração similar ou superior a 2/3 da espessura da fatia. Em conclusão, a aplicação simultânea de silanos convencionais e experimentais proporcionou maior resistência adesiva, reduziu as falhas adesivas dentina-cimento e os nÃveis de micro infiltração marginal foram similares em canais radiculares tratados com PFVAbstract: The aim of this in vitro study was to evaluate the effect of simultaneous application of conventional and experimental silanes on adhesive resistance and marginal micro-infiltration in human tooth roots restored with fiberglass posts (FGP) and subjected to thermal and mechanical cycling. Two oligomers were synthesized in solution with catalytic amounts of triethylamine. Multi-functional thiol - pentaerythritol tetra-3-mercaptopropionate (PETMP) was combined with di-functional isocyanates - 1,6-hexanedioldiissocyante (HDDI) (aliphatic) or 1,3-bis (1-isocyanato-1- methylethyl) benzene (BDI) (aromatic). Sixty uniradicular premolars were sectioned 2 mm above the cemento-enamel junction, received conventional endodontic treatment and filled with gutta-percha cones. The roots received standardized preparation in 10 mm of depth with drills of diameter 1.4 mm and were randomly separated in six groups (n = 10) according to the variables: conventional silanes (RelyX CP or Angelus) and experimental silanes (PETMP-HDDI or PETMP-BDI). In the root canal, it was applied a three-step adhesive and the post silanized according to the manufacturer's recommendations, followed by the application of experimental silanes. After cementation, the roots received filling cores in composite resin, crowns of indirect resin and were submitted to 1.2 x 106 mechanical cycles, followed by 500 thermal cycles (5 and 55ºC). Two 1-mm thick slices were obtained from each root third (cervical, middle and apical). One slice of each third was submitted to the shear bond test (push-out) and the fracture pattern was analyzed (%), and other subjected to analysis of marginal infiltration by dye (immersion in 2% methylene blue for seven days) and the penetration classified into scores (%). The remaining slices of each group were analyzed in SEM for the gaps formation. The results were analyzed with two-way ANOVA (silane and third), followed by the Tukey's test (push-out) and the Kruskal-wallis' test (micro marginal infiltration) with a significance level of ?=0.05. The simultaneous application of conventional and experimental silanes on FGPs increased the bond strength (p<0.001) with similar values between root thirds (p=0.199), reduced dentin-cement adhesive failures and increased the dentin cohesive failure. There was no significant difference in the micro infiltration scores by dye between the groups (p=0.176). All groups showed micro infiltration similar to or greater than 2/3 of the slice thickness. In conclusion, the simultaneous application of conventional and experimental silanes provided greater adhesive strength, reduced the dentin-cement adhesive failures and the levels of marginal micro infiltration were similar in root canal treated with FGPsMestradoProtese DentalMestre em ClÃnica OdontológicaCAPE