Active Mg Estimation Using Thermal Analysis: A Rapid Method to Control Nodularity in Ductile Cast Iron Production

Appropriate nodularity in ductile iron castings is strongly associated with the presence of high enough not combined Mg dissolved in the melt to cast. However, the residual Mg which is commonly measured for production control accounts for both dissolved Mg and Mg combined as oxides and sulfides. To account for the uncertainties associated with such a control, it is quite usual to over treat the melt with the risk of porosity appearance. A new methodology based on thermal analysis has been developed in the present work so as to estimate the amount of free Mg dissolved in the melt ready for pouring. A combination of Te mixture and a new “reactive mixture” composed of sulfur plus a commercial inoculant has been prepared for this purpose. This reactive mixture is able to transform the magnesium remaining dissolved in the melt to combined forms of this element. Experiments performed both during start of production (when Mg overtreatment is usual) and during normal mass production indicate that important variations of free Mg occur without relevant changes in residual Mg content as determined by spectrometry. The method developed in the present work has shown to be highly effective to detect those melt batches where active Mg content is not high enough for guaranteeing a correct nodularity of castings. Selection of proper active Mg thresholds and a correct inoculation process are critical to avoid “false”-negative results when using this new method

Graphite and Solid Fraction Evolutions during Solidification of Nodular Cast Irons

Ductile iron casting production is strongly affected by austenite and graphite distribution obtained after the solidification process. At the same time it is accepted that solidification behavior can be considered as hypo-, hyper- or eutectic depending on the chemical composition; there is still some misconception about the growth evolution of graphite nodules and about solid fraction progression. Quenching experiments were performed on two different carbon equivalent compositions using inoculated and non-inoculated thermal analysis standard samples with the aim of freezing the existing phases at different solid fractions for each alloy. As a result of these experiments, it was possible to study the structural features found at different locations of each sample and at different stages of solidification. Additionally nodule evolution during the liquid-solid transformation was also analyzed and discussed regarding the chemical and processing characteristics of the prepared alloys

Statistical study to determine the effect of carbon, silicon, nickel and other alloying elements on the mechanical properties of as-cast ferritic ductile irons

International audienceThere is a great interest in fully ferritic ductile irons due to their structural homogeneity, remarkable ductility and good response when machining. On the other hand the wide variety of raw materials available in foundry plants becomes a problem when controlling the chemical composition of the manufactured alloys. The present work shows a statistical study about the effect of different C, Si, Ni contents and other minor elements on structural and mechanical properties of a group of ferritic ductile iron alloys. A set of equations are finally presented to predict room temperature mechanical properties of ferritic ductile irons by means of their chemical composition and pearlite content