Investigation of Graded La2NiO4+ Cathodes to Improve SOFC Electrochemical Performance
Mixed ionic and electronic conducting MIEC oxides are promising materials for use as cathodes in solid oxide fuel cells SOFCs due to their enhanced electrocatalytic activity compared with electronic conducting oxides. In this paper, the MIEC oxide La2NiO4+ was prepared by the sol-gel route. Graded cathodes were deposited onto yttria-stabilized zirconia YSZ pellets by dip-coating, and electrochemical impedance spectroscopy studies were performed to characterize the symmetrical cell performance. By adapting the slurries, cathode layers with different porosities and thicknesses were obtained. A ceria gadolinium oxide CGO barrier layer was introduced, avoiding insulating La2Zr2O7 phase formation and thus reducing resistance polarization of the cathode. A systematic correlation between microstructure, composition, and electrochemical performance of these cathodes has been performed. An improvement of the electrochemical performance has been demonstrated, and a reduction in the area specific resistance ASR by a factor of 4.5 has been achieved with a compact interlayer of La2NiO4+ between the dense electrolyte and the porous La2NiO4+ cathode layer. The lowest observed ASR of 0.11 cm2 at 800°C was obtained from a symmetrical cell composed of a YSZ electrolyte, a CGO interlayer, an intermediate compact La2NiO4+ layer, a porous La2NiO4+ electrode layer, and a current collection layer of platinum paste
Nanosized Sodium-Doped Lanthanum Manganites: Role of the Synthetic Route on their Physical Properties
In this paper we present the results of the synthesis and characterisation of
nanocrystalline La1-xNaxMnO3+delta samples. Two synthetic routes were employed:
polyacrylamide-based sol-gel and propellant synthesis. Pure, single phase
materials were obtained with grain size around 35 nm for the sol-gel samples
and around 55 nm for the propellant ones, which moreover present a more broaden
grain size distribution. For both series a superparamagnetic behaviour was
evidenced by means of magnetisation and EPR measurements with peculiar features
ascribable to the different grain sizes and morphology. Preliminary
magnetoresistivity measurements show enhanced low-field (< 1 T)
magnetoresistance values which suggest an interesting applicative use of these
manganites.Comment: 31 Pages 10 Figures to appear in Chem. Mate
Influence of synthesis and processing parameters of the columbite precursor on the amount of Perovskite PMN
SÃntese, caracterização e propriedades de sistemas contendo óxidos de lantânio, cério e nÃquel obtidos pelo método dos precursores poliméricos
- …