Análise da espessura da película de cimentos de ionômero vítreo e fosfato de zinco, empregados na cimentação de coroas totais metálicas, preparadas in vivo

This study evaluated the film thicknesses of two GIC cements (Vidrion C, SS WHITE, Brazil; Ketac Cem, ESPE, Germany) and one zinc phosphate cement (Lee Smith, TELEDYNE, USA), used for final cementation of complete metal crowns. Twenty-one teeth scheduled for extraction due to orthodontic treatment were prepared for complete metal crowns. Dies were relieved with 5 layers of die varnish spacer. The crowns were manufactured by a commercial laboratory (with standardized procedures as much as possible) and cemented first with finger pressure and later by occlusion pressure using orange wood sticks. Results submitted to an ANOVA test showed that all cements had a similar behavior showing no significant statistical differences (p<0.01). A film thickness analysis of 7 selected preparations sites, showed that only axial positions, presented differences between Lee Smith and Vidrion C cements, the latter presenting lower significant values. For other positions studied, the three cements showed no significant statistical differences (p<0.05). Technical exploratory analysis of data by a BOX PLOT graphic showed for the ZPC a broad film thickness value distributions (from the highest to the lowest values) related to type of cement and measurement values. For glass ionomer cement the graphic presented values concentrating at lower levels than zinc phosphate cement. This was still more evident for the Vidrion C cementA presente pesquisa consistiu em analisar a espessura da película de cimentos de ionômero vítreo (Vidrion C, SS WHITE, Brasil; Ketac Cem, ESPE, Alemanha) in vivo, comparando os resultados com um cimento de fosfato de zinco (Lee Smith, TELEDYNE WATER PIK, USA), na cimentação de coroas totais metálicas. Foram utilizados 21 dentes íntegros, com exodontia indicada para fins ortodônticos, que foram preparados para receber coroa total metálica. O processamento laboratorial das fundições, foi feito em laboratório comercial, de forma padronizada. Todas as coroas foram aliviadas internamente, através da prévia aplicação de cinco camadas de verniz espaçador sobre os troquéis. As cimentações, foram feitas, inicialmente sob pressão digital, seguida por pressão de assentamento pela oclusão, com um mordente de madeira de laranjeira, interposto entre a coroa e a arcada antagonista. Os resultados mostraram, pelo teste estatístico ANOVA, valores semelhantes para os três cimentos, ao nível de 1%. Entretanto, quando a espessura da película do cimento foi analisada sob as variáveis cimento e posição de mensuração na superfície do dente preparado, encontrou-se que nas paredes axiais, havia diferença entre o cimento Lee Smith e o Vidrion C, onde os valores para o Vidrion foram significativamente menores. Nas demais posições analisadas, não houve diferença significante ao nível de 5%. Quando esses mesmos valores foram apreciados através de representação gráfica (diagrama, do tipo BOX-PLOT), do cimento em função da posição de mensuração, observou-se, no caso do cimento de fosfato de zinco, uma tendência de distribuição dos valores, por toda a faixa compreendida entre o valor máximo e o valor mínimo da película. Os cimentos de ionômero vítreo, tenderam a concentrar seus valores, em relação à faixa de distribuição, a níveis mais baixos que o cimento de fosfato de zinco. O Vidrion C, em particular, foi o que..

Estudo da resistência à tração de cápsulas e troqueis metálicos cimentados, em função de alívio e retenção para o cimento

The objective of this study was to verify tensile strength of metallic capsules and dies, in stainless steel, cemented with zinc phosphate cement, representative of crowns and full crowns preparations. One hundred and forty four dies and respective capsules were made in Lathe CNC (Computer Numeric Control). The dimensions of the dies were: 9mm of diameter ín the base (gingival); 8mm of height; cervical line in shoulder with one millimeter of width and 135 degrees of inclination; and tapered of 10 degrees. The capsules were excavated in the interior of other cylinders, with the tapered form, identical and negative in relation to the form of the dies. Forty-eight experimental conditions, in three rejoinders each, were made. The changeable were: internal relief in the capsules; and horizontal sulcus in the capsules and the dies. The relief varied between 2µm (in the condition without relief), 30µm and 60µm (in the conditions with relief). The sulcus varied between no sulcus and three sulcus, as much in the capsules as in the dies, with 200 µm depth, in equal amounts of specimens for each condition of sulcus. The capsules and dies were cemented. The experimental conditions were not repeated, except in the rejoinders. The specimens were submitted to traction test in universal test machine of Emic (ltaquaquecetuba-SP) in the Department of Materials and Technology of the College of Engineering of Guaratinguetá, UNESP. The data were submitted to statistic analysis for methods ANOVA and Tukey, showing significant dífference for the variable relief and sulcus in the capsules, and interacting individually and among then. They had not presented difference statistics for changeable the sulcus in the dies. The tensile strength increased with the relief and the amount of sulcus in the capsules, but it remained in the same level with the sulcus in the diesO objetivo desta pesquisa foi estudar resistência à tração de cápsulas cimentadas sobre troqueis metálicos, com cimento fosfato de zinco, variando quantidade de alívio interno nas cápsulas e sulcos horizontais nas cápsulas e nos troqueis. Foram torneados duzentos e oitenta e oito cilindros de aço inoxidável, representativos de cento e quarenta e quatro troqueis e igual quantidade de cápsulas, semelhantes a preparos e respectivas coroas totais, em Torno tipo CNC (Controle Numérico Computadorizado). As dimensões padronizadas dos troqueis foram: 9mm de diâmetro na base maior (cervical); 8mm de altura cérvico-oclusal: terminação em ombro com um milímetro de largura e 135° de inclinação; e 10° de conicidade nas paredes axiais. As cápsulas foram obtidas por usinagem do interior de outros cilindros, com a forma idêntica e negativa em relação à forma dos troqueis. Quarenta e oito condições experimentais foram estabelecidas e cimentadas, em três réplicas para cada condição. O alívio das cápsulas foi de 2µm (na condição sem alívio), 30µm e 60µm (nas condições com alívio). A confecção de sulcos variou entre zero e três sulcos, nas cápsulas e nos troqueis, com 200µm de profundidade e em quantidades iguais de espécimes para cada condição estudada. Assim, as condições experimentais somente se repetiram nas réplicas. Os corpos-de-prova obtidos das cimentações foram submetidos a teste de tração em máquina universal de ensaios Emic (ltaquaquecetuba-SP), no Departamento de Materiais e Tecnologia da Faculdade de Engenharia de Guaratinguetá, UNESP. Os resultados receberam tratamento estatístico pelos métodos de, Análise de Variância e de Tukey, mostrando diferença significativa ao nível de 5% para as variáveis alívio e sulco nas cápsulas individualmentee quando esses fatores interagiram. Não houve diferença estatística para a variável sulco nos troqueis. A permaneceu sem alteração com os..

Mechanical and thermal cycling effects on the flexural strength of glass ceramics fused to titanium

This study evaluated the effects of mechanical and thermal cycling on the flexural strength (ISO 9693) of three brands of ceramics fused to commercially pure titanium (cpTi). Metallic frameworks of 25 x 3 x 0.5 mm dimensions (N = 84) were cast in cpTi, followed by 150-mu m aluminum oxide airborne particle abrasion at a designated area of the frameworks (8 x 3 mm). Bonder and opaque ceramic were applied on the frameworks, and then the corresponding ceramic (Triceram, Super Porcelain Ti-22, Vita Titankeramik) was fired onto them (thickness: 1 mm). Half of the specimens from each ceramic-metal combination were randomly tested without aging (only water storage at 37 degrees C for 24 hours), while the other half were mechanically loaded (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and thermocycled (3,000 cycles, between 5-55 degrees C, dwell time of 13 seconds). After the flexural strength test, failure types were noted. Mechanical and thermal cycling decreased the mean flexural strength values significantly (p<0.05) for all the three ceramic-cpTi combinations tested when compared to the control group. In all the three groups, failure type was exclusively adhesive at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface except for a visible oxide layer