3 research outputs found
Synthesis and caracterization of sensor element of kalSi3O8 matrix, doped with mn and gd, obtained by sol-gel method, for application in ionizing radiation dosimetry by thermoluminescence and optically stimulated luminescence.
Neste trabalho, estudou-se as propriedades termoluminescentes e fotoluminescentes (em processo anti-Stokes), além de algumas propriedades químicas e físicas, de amostras sintéticas de KAlSi3O8, dopadas com Mn ou Gd, obtidas por meio da técnica sol-gel. O objetivo principal do estudo foi a obtenção de um novo material, com possibilidades reais de aplicação em dosimetria das radiações ionizantes, como elemento sensor de dosímetros luminescentes. As amostras foram obtidas e trabalhadas na forma de pós com tamanho médio de partícula em 600 nm e suas estruturas composta por uma matriz amorfa e com presença de nano partículas, presente apenas nas amostras dopadas. Os resultados de EPR mostraram que os dopantes incorporaram na matriz sob a valência de Mn2+ e Gd3+ respectivamente. As curvas de emissão TL apresentaram formatos semelhantes para todas as regiões estudadas, com a presença de um pico principal de intensidade alta e reprodutível em torno de 170°C. As curvas de decaimento da LOE da amostra não dopada e dopada com Mn exibiram um decaimento total da luminescência para 40 s de estimulação centrada em 470 nm; por outro lado, a amostra dopada com Gd, exibiu um rápido decaimento da LOE (aproximadamente 71,4 % da intensidade inicial), para os primeiros 40 s de estimulação, seguida por um decaimento mais lento e persistente para o restante do período de estimulação, o que indica claramente a presença de duas componentes de decaimento. As amostras dopadas com Mn apresentaram emissão TL mais intensa em torno 570 nm, sendo mais eficientes para os estudos de TL no VIS; enquanto que, as dopadas com Gd, exibiram emissão mais intensa em 470 nm, porém, devido ao formato dos sinais (presença de um único pico aparente), mostraram-se melhor para os estudos de LOE e TL no UV. As amostras dopadas com 0,5% e 8% em mol de Mn e Gd, respectivamente, apresentaram os sinais luminescentes mais intensos, tanto para LOE quanto para TL. No estudo da dependência energética para diferentes energias de raios-X, o tipo de dopante influenciou no padrão de resposta obtido, tendo sido observado um decréscimo da intensidade luminescente com o aumento da energia para a amostra dopada com Mn; para a amostra não dopada e dopada com Gd, não se observou um padrão de decréscimo ou aumento da intensidade com a energia. As curvas de calibração foram ajustadas por meio de retas com grau de confiabilidade alto (fator R2 próximo a 1), e as menores doses detectáveis variaram entre 20 e 60 mGy aproximadamente. Todas as amostras apresentaram perdas consideráveis de intensidade luminescente com o passar do tempo após irradiação, e que foi de aproximadamente 80%, em média, para os 10 primeiros dias. Concluiu-se que, a princípio, os materiais têm maior possibilidade de aplicação na dosimetria em tempo real do que na dosimetria convencional ou passiva por TLDs, devido a sua alta resposta luminescente. Contudo, estudos futuros a respeito de tratamento térmico prévio, podem viabilizá-los a esta última aplicação. Com relação ao campo de aplicação, sugere-se a dosimetria ambiental, devido aos valores Z obtidos, que estão mais próximos do dos materiais que compões rochas e sedimentos.In this work the thermoluminescent and photoluminescent properties (in the anti-Stokes process), and some other chemical and physical properties of KAlSi3O8 synthetic samples, doped with Mn or Gd, obtained by sol-gel method, were studied. The main goal of this study was to obtain a new material, with real possibility of application in ionizing radiation dosimetry as sensor element in luminescent dosimeters. The obtained samples were composed of powders with average particle size around 600 nm and they structures were composed of an amorphous matrix with presence of nanoparticles, observed only in the doped samples. The EPR results showed that the dopants incorporated in the matrix in the Mn2+ and Gd3+ valences, respectively. The TL glow curves exhibited a similar pattern for all the studied regions, composed of a main high-intensity and reproducible peak around 170 °C. The OSL shine-down curves for the undoped and Mn doped samples exhibited a total decay of luminescence for 40 s of stimulation centered at 470 nm; on the other hand, Gd doped sample exhibited an quick OSL decay (approximately 71.4 % of the initial intensity), for the first 40 s of stimulation, followed by a slower and more persistent decay, which clearly indicates the presence of two decay components. Mn doped samples showed the highest TL emission around 570 nm, being more efficient for the TL studies in the VIS, while the Gd doped samples exhibited the highest emission at 470 nm; however, due to the obtained curve pattern (with an apparent single peak), they had shown more efficient results for the applications in the UV. The samples doped with 0.5 and 8 mol% of Mn and Gd, respectively, showed the highest luminescent response improvement for OSL and TL. Energetic dependence on different X-rays energies study showed that the dopants changed the obtained response pattern. The Mn doped sample exhibited a decrease in luminescent response, while the Gd and the undoped samples do not show a pattern of decrease or increase in luminescence. The calibration curves were fitted by straight lines with high reliability degree (R2 near to 1), and the lowest detectable doses were between 20 and 60 mGy. All the samples exhibited considerable losses in luminescent intensity with the time after irradiation (about 80% for the firsts 10 days). From the results it was concluded that the studied materials are more applicable to real time than to passive TLD dosimetry, due to their high luminescent response. However, studies about previous heating treatment could make them feasible for the last application. The use of these materials in environmental dosimetry is suggested due to the obtained Z values, which are closer to those which form rocks and sediments
Protonic conductor BaCe1-xYxO3-δ with and without sintering aid : synthesis and structural, microstructural and electrical characterization
The study of solid electrolytes (SE) is important to the scientific and technological development of materials used in application related to clean energy generation, such as Solid Oxide Fuel Cells (SOFCs). Yttrium-doped Barium Cerate is a SE with perovskite structure and great potential for this application because of its high values of protonic conductivity in temperatures between 350 and 600°C, which would allow the replacement of the currently used Zirconia based SE that operate above 800 °C, reducing the manufacturing cost of SOFCs. In the present work, eighteen compositions of BaCe1-xYxO3-δ system with x ranging from 0 to 0.2 were synthesized via modified citrate process and for half of the compositions an addition of 1 wt% ZnO as sintering aid was made. With the goal of establishing a correlation between structure, microstructure and electrical conductivity with the yttrium concentration and in the presence or absence of the sintering aid, all compositions were characterized with X-ray Powder Diffraction, Raman Spectroscopy, Scanning and Transmission Electron Microscopy (TEM), Energy-dispersive X-ray Spectroscopy (EDS) and Impedance Spectroscopy. Secondary phases were characterized using TEM, EDS and Electron Diffraction. All samples presented relative bulk density values above 95%. The bulk electrical conductivity is proportional to the yttrium concentration in the grain and, in general, the ZnO addition promoted grain growth, increasing its average size up to five times in some compositions. The ZnO acts mainly at the grain boundary region and it is effective as sintering aid only when the composition has some yttrium content. Among all synthesized compositions, BaCe0.8Y0.2O3-δ without ZnO addition showed the highest electrical conductivity value at 600°C (≈ 31.5 mS/cm). In the group of samples with ZnO, the highest values (close to 18.4 mS/cm), were obtained for compositions with Yttrium content above 14 at.%.Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)O estudo de eletrólitos sólidos (ES) é importante para o desenvolvimento científico e técnológico de materiais para aplicações relacionadas à geração de energia limpa, como por exemplo, células a combustível de óxido sólido (CaCOS). O cerato de bário dopado com ítrio é um ES com estrutura perovskita com grande potencial de aplicação por apresentar valores altos de condutividade protônica em temperatura entre 350 e 600 °C, o que possibilitaria substituir os atuais ES à base de Zircônia que operam acima de 800 °C, reduzindo o custo de fabricação das CaCOS. Neste trabalho, dezoito composições do sistema BaCe1-xYxO3-δ com x variando entre 0 e 0,2 foram sintetizadas via processo citrato modificado e para metade das composições, uma adição de 1% em massa de ZnO como aditivo de sinterização foi feita. Visando estabelecer uma correlação entre estrutura, microestrura e condutividade elétrica com a concentração de ítrio e a presença ou não de aditivo de sinterização, todas as composições foram caracterizadas por meio de difração de raios X, espectroscopia Raman, microscopia eletrônica de varredura e transmissão (MET), espectroscopia de raios X por dispersão em energia (EDS) e espectroscopia de impedância. Fases secundárias foram caracterizadas por MET, EDS e difração de elétrons. Todas as composições apresentaram valores de densidade relativa acima de 95%. A condutividade elétrica do grão é proporcional a concentração de ítrio na matriz e, no geral, a adição de ZnO favoreceu o crescimento de grão, aumentando o seu tamanho médio em até cinco vezes. O ZnO atua principalmente na região de contorno de grão e é eficiente como aditivo apenas na presença ítrio. Dentre as composições sintetizadas, a BaCe0,8Y0,2O3-δ sem ZnO apresentou o maior valor de condutividade a 600°C (≈ 31,5 mS/cm). No grupo das amostras com ZnO, os valores mais altos, próximos a 18,4 mS/cm, foram obtidos para composições com teor de Y acima de 14% at.CNPq: 207073/2014-7CNPq: 160534/2012-
TL and OSL properties of KAlSi(3)O(8):Mn, obtained by sol-gel process
Thermoluminescence (TL) and Optically Stimulated Luminescence (OSL) properties of KAlSi(3)O(8):Mn glasses obtained through the sol gel technique were investigated. Samples were obtained with five different molar concentrations of 0.25, 0.5, 1, 2 and 5 mol% of manganese. Transmission Electronic Microscopy (TEM) indicated the occurrence of nanoparticles composed by glass matrix elements with Mn. Best results for TL response were obtained with 0.5 mol% Mn doped sample, which exhibits a TL peak at 180 degrees C. The TL spectrum of this sample presents a broad emission band from 450 to 700 nm with a peak at 575 nm approximately. The emission band fits very well with the characteristic lines of the Mn(2+) emission features. According to this fact, the band at 410 nm can be ascribed to (6)A(1)(S) -> (4)A(1)(G), (4)E(G) transition, while the 545 nm band can be attributed to the superposition of the transitions (6)A(1)(S) -> (4)T(2)(G) and (6)A(1)(S) -> (4)T(1)(G). The dependence of the TL response with the energy of X-rays (27-41 keV) showed a small decrease of the TL intensity in the high energy region. Excitation with blue LEDs showed OSL in the UV region with a fast decay component. (C) 2011 Elsevier Ltd. All rights reserved