Ligand exchange in gold-coated FePt nanoparticles

In this work we present the magnetic properties of gold coated FePt nanoparticles and the study of stable aqueous dispersions of FePt@Au and FePt synthesized after ligand exchange with mercaptoundecanoic acid. The particle size determined from TEM micrographs goes from 4 nm for the uncoated nanoparticles to a maximum of 10 nm for the gold coated ones indicating that the thickness of the shell ranges from 1 to 3 nm. The magnetic characterization consists in hysteresis cycles at 10 and 300 K. The results show that, at low field and room temperature, the magnetic behavior of uncoated and coated nanoparticles are surprisingly quite similar. Since the gold coated nanoparticles keep the magnetic properties of FePt and the presence of gold improves the functionalization of nanoparticles, the system is suitable for biological application. Mercaptoundecanoic ligand transfer was used to render water stable nanoparticles in a wide pH range. Transmission electron microscopy and dynamic light scattering results show the nanoparticles slightly agglomerate after ligand exchange. Fourier transform infrared spectroscopy results suggest that thiol bind to the gold atoms of the surface.Comment: Intermag 2008, conference pape

Perturbed Angular Correlation Studies in SrTi0₃ Single Crystals

The quadrupole hyperfine interactions of ^111Cd/^111 probe nuclei in single-crystalline SrTiO₃ perovskite samples were investigated using Perturbed Angular Correlation spectroscopy. Three electric field gradients were detected and their fractions and hyperfine parameters were measured in the temperature range from 26 to 700 K. The fraction f₀ having a vanishing quadrupole frequency, as expected for ^111Cd on substitutional sites in a cubic lattice, starts to develop around 300 K and reaches 100% at 700 K. Two well-defined EFG's having closely lying quadrupole frequencies and asymmetry parameters of ω_(Q1) = 49.1(3) Mrad/s, η_(1) = 0.10(2) and ω_(Q2) = 51 8(3) Mrad/s, η_(2)= 0.12(2), at room temperature, were identified in the temperature range from 250 to 530 K, and their (100) orientation in the lattice was determined. They are associated with electronic defects at the probe atoms

Ligand exchange in gold-coated FePt nanoparticles

In this work, we present the magnetic properties of gold-coated FePt nanoparticles and the study of stable aqueous dispersions of FePt@Au and FePt synthesized after ligand exchange with mercaptoundecanoic acid. The particle size determined from transmission electron microscopy (TEM) micrographs goes from 4 nm for the uncoated nanoparticles to a maximum of 10 nm for the gold-coated ones indicating that the thickness of the shell ranges from 1 to 3 nm. The magnetic characterization consists in hysteresis cycles at 10 and 300 K. The results show that, at low field and room temperature, the magnetic behavior of uncoated and coated nanoparticles are surprisingly quite similar. Because the gold-coated nanoparticles keep the magnetic properties of FePt and the presence of gold improves the functionalization of nanoparticles, the system is suitable for biological application. Mercaptoundecanoic ligand transfer was used to render water stable nanoparticles in a wide pH range. Transmission electron microscopy and dynamic light scattering (DLS) results show the nanoparticles slightly agglomerate after ligand exchange. Fourier transform infrared spectroscopy results suggest that thiol binds to the gold atoms of the surface

Improving the magnetic heating by disaggregating nanoparticles

Recently, potential applications of the magnetic heating for heterogeneous catalysis or organic synthesis have been reported. As these new applications are not limited by biocompatibility requirements, a wide range of possibilities for non-aqueous colloidal nanoparticles with enhanced magnetic properties is open. In this work, manganese and cobalt ferrite nanoparticles are synthesized by co-precipitation method with average particle size around 12 nm. The particles are either coated with tetramethylammonium hydroxide (TMAOH) and dispersed in water or with oleic acid (OA) and dispersed in hexane to produce aggregated or disaggregated nanoparticles, respectively. It is observed that the particle disaggregation improves significantly the heating efficiency from 12 to 96 W/g in the case of cobalt ferrite, and from 120 to 413 W/g for the manganese ferrite. The main responsible for this improvement is the reduction of hydrodynamic volume that allows a faster Brownian relaxation. This work also discusses the relevance of the size distribution