Surface Grafting of Poly(L-glutamates). 3. Block Copolymerization

This paper describes for the first time the synthesis of surface-grafted AB-block copolypeptides, consisting of poly(γ-benzyl L-glutamate) (PBLG) as the A-block and poly(γ-methyl L-glutamate) (PMLG) as the B-block. Immobilized primary amine groups of (γ-aminopropyl)triethoxysilane (APS) on silicon wafers initiated the ring-opening polymerization of N-carboxyanhydrides of glutamic acid esters (NCAs). After removal of the BLG-NCA monomer solution after a certain reaction time, the amine end groups of the formed PBLG blocks acted as initiators for the second monomers. This method provides the possibility of making layered structures of surface-grafted block copolymers with tuned properties. Ellipsometry and small-angle X-ray reflection (SAXR) measurements revealed the thickness of the polypeptide layers ranging from 45-100 Å of the first block to 140-270 Å for the total block copolypeptides. The chemical composition of the blocks was determined by X-ray photoelectron spectroscopy (XPS). In addition, Fourier transform infrared transmission spectroscopy (FT-IR) revealed that the polypeptide main chains of both blocks consisted of pure R-helices. The average orientation of the helices ranging from 22-42° with respect to the substrate within the first block to 31-35° in the second block could be derived with FT-IR as well.

Surface Grafting of Poly(L-glutamates). 2. Helix Orientation

In this paper the average helix orientation of surface-grafted poly(γ-benzyl L-glutamate) (PBLG), poly(γ-methyl L-glutamate) (PMLG), and poly(γ-methyl L-glutamate)-co-(γ-n-stearyl L-glutamate) (PMLGSLG 70/30) was investigated by means of FT-IR transmission spectroscopy. The theoretical relation between the average tilt angle (θ) and the absorption peak areas of three different backbone amide bands could be calculated because their transition dipole moment directions with respect to the helix axis were known. From the normalized absorptions, the average tilt angles of grafted helices of PBLG, PMLG, and PMLGSLG 70/30 were determined. The somewhat larger average angle of PMLG helices of 35 ± 5° with respect to the substrate compared to the value of 32 ± 5° of PBLG was due to the higher grafting density of PMLG. Because of the smaller helix diameter as a result of the smaller size of the methyl side group, more PMLG helices grew on the same surface area. Sterical hindrance and unfavorable polar interactions between unidirectional aligned helices forced the PMLG helices in a more upright arrangement. The even more perpendicular orientation of PMLGSLG 70/30 (48 ± 6°) could be the result of incorporation of mainly γ-methyl L-glutamate N-carboxyanhydride (MLG-NCA) monomers during the initiation step. Incorporation of the much larger γ-n-stearyl L-glutamate N-carboxyanhydride (SLG-NCA) monomers afterward lead to enlarged angles with respect to the substrate. Due to swelling, a pronounced change in helix orientation of grafted PMLGSLG 70/30 in n-hexadecane was observed, resulting in an almost perpendicular helix orientation.

Randomized Controlled Trial of the Focus Parent Training for Toddlers with Autism: 1-Year Outcome

This randomized controlled trial compared results obtained after 12 months of nonintensive parent training plus care-as-usual and care-as-usual alone. The training focused on stimulating joint attention and language skills and was based on the intervention described by Drew et al. (Eur Child Adolesc Psychiatr 11:266–272, 2002). Seventy-five toddlers with autism spectrum disorder (65 autism, 10 PDD-NOS, mean age = 34.4 months, SD = 6.2) were enrolled. Analyses were conducted on a final sample of 67 children (lost to follow-up = 8). No significant intervention effects were found for any of the primary (language), secondary (global clinical improvement), or mediating (child engagement, early precursors of social communication, or parental skills) outcome variables, suggesting that the ‘Focus parent training’ was not of additional value to the more general care-as-usual