2 research outputs found
Recommended from our members
Fabrication and characterizations of hydrogels for cartilage repair
YesArticular cartilage is a vascular tissue with limited repair capabilities, leaving an afflicted person in extreme pain. The tissue experiences numerous forces throughout its lifetime. This study focuses on development of a novel hydrogel composed of chitosan and β-glycerophosphate for articular cartilage repair. The aim of this study was to investigate the mechanical properties and swelling behaviour of a novel hydrogel composed of chitosan and β-glycerophosphate for cartilage repair. The mechanical properties were measured for compression forces. Mach-1 mechanical testing system was used to obtain storage and loss modulus for each hydrogel sample to achieve viscoelastic properties of fabricated hydrogels. Two swelling tests were carried out to compare water retaining capabilities of the samples. The hydrogel samples were made of five different concentrations of β-glycerophosphate cross-linked with chitosan. Each sample with different β-glycerophosphate concentration underwent sinusoidal compression forces at three different frequencies -0.1Hz, 0.316Hz and 1Hz. The result of mechanical testing was obtained as storage and loss modulus. Storage modulus represents the elastic component and loss modulus represents the viscosity of the samples. The results obtained for 1Hz were of interest because the knee experiences frequency of 1Hz during walking
Recommended from our members
Fabrication Characterisation and Optimisation of Electrospun Scaffolds for Ligament Tissue Reconstruction. The Development of an Anterior Cruciate Ligament (ACL) Analogue using Electrospun PCL, PVA Hydrogel and Polyester Sutures
Year 2019, football, rugby, netball and skiing had most occurring ACL injuries, listed by United Kingdom National Ligament Report (NLR). The standard procedure treatment of complete laceration of the ACL, is performed by tissue autograft implantation designed from a patellar tendon, for replacement of damaged tissue using orthopaedic surgery. The aim of this thesis is to design and fabricate an ACL graft, attempting to mimic the natural ACL, for the purpose of tissue reconstruction. The desired graft analogues exhibited properties imitating native connective tissue, reducing pain through drug delivery with great biocompatibility and enhance suture mechanical strength. Various biomaterials were implemented into this study, utilising strategies; polymer solution fabrication, electrospinning, hydrogel synthesis, mechanical braiding and graft assembly to fabricate an ACL graft. The polymeric material poly (E- caprolactone) (PCL) was researched, utilising its ability to fabricate scaffolds. Results showed, three analogue ACL grafts (Braided PCL-BP, Braided PCL + Hydrogel-BPH & Braided PCL + Sutures-BPS) created utilising the properties of braiding, hydrogels and sutures, ultimately improving the versatility of electrospinning for tissue engineering and reconstruction. Graft analogues were tested and compared against patellar tendons producing similar tensile properties. Poly vinyl alcohol (PVA) hydrogels successfully held ibuprofen, revealing drug delivery characteristics, polyester threads improved mechanical properties of electrospun grafts and dry degradation showed that PCL did not lose significant mass over two months. Conclusion, tensile strength of patella tendon was 395x, 790x & 56x of analogue grafts (BP, BPH & BPS) respectively, having potential for improvement of tensile parameters for ligament reconstruction