МЕХАНИЗМ ОБРАЗОВАНИЯ, СТРОЕНИЕ И МИКРОСТРУКТУРА ПЕРЕХОДНОЙ ЗОНЫ МЕЖДУ НАПЫЛЕННЫМ СЛОЕМ И ПОДЛОЖКОЙ
The mechanism of formation, structure and microstructure of the transition zone between the deposited layer and the substrate is presented. It was found, that in the case of a common framework the boundary is a thin line, which is clearly seen from the melted-tops initial roughness. In this case, destruction posesses adhesive-cohesive character, about 50/50. And in the case of spraying the material of different basis as compared to the substrate basis border connection is characterized by a clear intermetallic layer of different thickness with a jump in the value of microhardness. In this case, the weak point is interface section of substrate-sprayed layer, so that the destruction possesses adhesive nature. Представлен механизм образования, строение и микроструктура переходной зоны между напыленным слоем и подложкой. Установлено, что в случае общей основы граница раздела представляет тонкую линию, на которой отчетливо видны оплавленные вершины первоначальной шероховатости. В этом случае разрушение носит адгезионно-когезионный характер, примерно 50/50. А в случае напыления материалом другой основы по сравнению с основой подложки граница соединения характеризуется четкой интерметаллидной прослойкой различной толщины со скачком величины микротвердости. В этом случае слабым местом оказывается граница раздела подложка-напыленный слой, так что разрушение носит адгезионный характер.