Mixed conductivity, thermal expansion and defect chemistry of A-site deficient LaNi(0.5)Ji(0.5)O(3-delta).

This work is focused on the analysis of defect chemistry and partial electronic and oxygen ionic conductivities of A-site deficient La1-xNi0.5Ti0.5O3-delta (x = 0.05 and 0.10). The orthorhombic-to-rhombohedral phase transition was monitored by means of dilatometry and high-temperature X-ray diffractometry. The average thermal expansion coefficients vary in the range (8.5-13.0) x 10(-6) K-1, increasing with temperature and A-site deficiency. The ion transference numbers determined by the Faradaic efficiency measurements are lower than 0.1% at 900-975 degrees C in air. Activation energies of the oxygen ionic conductivity at 897-977 degrees C are 430 and 220 kJ/mol for x = 0.05 and 0.10, respectively. Atomistic simulation demonstrated high stability of ternary defect clusters formed by the vacant sites in the A-sublattice, oxygen vacancies and W, cations, which leads to a very low level of mixed conductivity. © 2007, Elsevier Ltd

Oxygen permeability, stability and electrochemical behavior of Pr2NiO4+δ-based materials.

The high-temperature electronic and ionic transport properties, thermal expansion and stability of dense Pr2NiO4+δ Pr2Ni0.9Fe0.1O4+δ ceramics have been appraised in comparison with K2NiF4-type lanthanum nickelate. Under oxidizing conditions, the extensive oxygen uptake at temperatures below 1073-1223 K leads to reversible decomposition of Pr2NiO4-based solid solutions into Ruddlesden-Popper type Pr4Ni3O10 and praseodymium oxide phases. The substitution of nickel with copper decreases the oxygen content and phase transition temperature, whilst the incorporation of iron cations has opposite effects. Both types of doping tend to decrease stability in reducing atmospheres as estimated from the oxygen partial pressure dependencies of total conductivity and Seebeck coefficient. The steady-state oxygen permeability of Pr2NiO4+δ ceramics at 1173-1223 K, limited by both surface-exchange kinetics and bulk ionic conduction, is similar to that of La2NiO4+δ. The phase transformation on cooling results in considerably higher electronic conductivity and oxygen permeation, but is associated also with significant volume changes revealed by dilatometry. At 973-1073 K, porous Pr2Ni0.8Cu0.2O4+δ electrodes deposited onto lanthanum gallate-based solid electrolyte exhibit lower anodic overpotentials compared to Pr2Ni0.8Cu0.2O4+δ, whilst cathodic reduction decreases their performance. © 2007, Springer. The original publication is available at www.springerlink.co