A versatile synthesis method of dendrites-free segmented nanowires with a precise size control

We report an innovative strategy to obtain cylindrical nanowires combining well established and low-cost bottom-up methods such as template-assisted nanowires synthesis and electrodeposition process. This approach allows the growth of single-layer or multi-segmented nanowires with precise control over their length (from few nanometers to several micrometers). The employed techniques give rise to branched pores at the bottom of the templates and consequently dendrites at the end of the nanowires. With our method, these undesired features are easily removed from the nanowires by a selective chemical etching. This is crucial for magnetic characterizations where such non-homogeneous branches may introduce undesired features into the final magnetic response. The obtained structures show extremely narrow distributions in diameter and length, improved robustness and high-yield, making this versatile approach strongly compatible with large scale production at an industrial level. Finally, we show the possibility to tune accurately the size of the nanostructures and consequently provide an easy control over the magnetic properties of these nanostructures

Uniaxial Magnetization Performance of Textured Fe Nanowire Arrays Electrodeposited by a Pulsed Potential Deposition Technique

Textured ferromagnetic Fe nanowire arrays were electrodeposited using a rectangular-pulsed potential deposition technique into anodized aluminum oxide nanochannels. During the electrodeposition of Fe nanowire arrays at a cathodic potential of ??1.2 V, the growth rate of the nanowires was ca. 200 nm s?1. The aspect ratio of Fe nanowires with a diameter of 30?±?5 nm reached ca. 2000. The long axis of Fe nanowires corresponded with the direction when a large overpotential during the on-time pulse was applied, whereas it orientated to the direction under the potentiostatic condition with a small overpotential. By shifting the on-time cathode potential up to ??1.8 V, the texture coefficient for the (200) plane, TC200, reached up to 1.94. Perpendicular magnetization performance was observed in Fe nanowire arrays. With increasing TC200, the squareness of Fe nanowire arrays increased up to 0.95 with the coercivity maintained at 1.4 kOe at room temperature. This research result has opened a novel possibility of Fe nanowire arrays that can be applied for a new permanent magnetic material without rare-earth metals