Synthesis and research of polyfunctional silicon-containing amines – new promoters of adhesion

Currently, in order to obtain high-tech hybrid products, modern adhesives have high requirements for creating strong joints between dissimilar materials. It is known that adhesion depends on the compatibility of the adhesives with the surfaces of the materials. Amine compounds are the main hardeners for epoxy compositions. That is why, in this article, we synthesized silicon-containing amines based on polyfunctional aminoalkoxysiloxanes for epoxy compositions. Aminoalkoxysiloxanes were prepared by the interaction of 3-aminopropyltriethoxysilane with monoethanolamine in nitrogen at atmospheric pressure in the presence of a binary antioxidant and catalytic amounts of an alkali metal alcoholate. During the reaction in a homogeneous phase, the reaction mixture was heated to a temperature of 100-110 °C and distilled off to 90% of ethanol from the theoretically calculated amount. Further, the reaction was carried out at a reduced temperature of 10-20 mmHg pressure until the release of alcohol stops. At the same time, gravimetric control was carried out and the refractive index of the reaction mixture was measured. As a result, aminoalkoxysilanes were obtained in the form of light-yellow oily liquids. The structure of the obtained compounds was investigated by IR spectroscopy on an FSM-1202 Fourier spectrophotometer and 1H NMR spectroscopy on a high-resolution BrukerWM-250 NMR spectrometer. It was found that under the selected synthesis conditions, aminopropyltri-(2-aminoethoxy)silane is obtained with the highest yield of 97.6% at a molar ratio of 3-aminopropyltriethoxysilane AGM-9 with monoethanolamine 1:3

Study of the Effect of Polymeric Microspheres On the Properties of Oil and Petrol Resistant Rubber

Исследовано влияние полых полимерных микросфер Expancel 909 DU 80, Expancel 043 DUT 80, Expancel 920 DET 40d25, Expancel 920 DUT 40, Expancel 930 MB 120 и Lega Foam 120 MB на реометрические показатели резиновой смеси, физико- механические и эксплуатационные свойства маслобензостойкой резины. Резиновая смесь содержала: изопреновый СКИ‑3 и бутадиен- метилстирольный СКМС‑30АРК каучуки, вулканизирующий агент – серу; ускорители вулканизации – тиурам Д и тиазол 2МБС; активаторы вулканизации – цинковые белила, стеарин; наполнители – технический углерод N 220, технический углерод Т 900, мел природный; мягчитель – канифоль; пластификатор – дибутилфталат; замедлитель подвулканизации – N‑нитрозодифениламин. Резиновую смесь готовили на лабораторных вальцах ЛБ 320 160/160 при температуре валков 60–70 оС. Вулканизационные параметры резиновой смеси исследовались на реометре MDR 3000 Basic фирмы «Mon Tech» при 150 °C в течение 30 мин в соответствии с ASTM D 2084–79. Стандартные образцы для определения физико- механических показателей вулканизовали при температуре 150 °C в течение 30 мин в вулканизационном прессе типа P-V‑100–3RT‑2-PCD. Основные характеристики вулканизатов определяли согласно действующим в резиновой промышленности стандартам. Установлено, что резина, содержащая микросферы Expancel 043 DUT 80, обладает наилучшими физико- механическими свойствами, высокой износостойкостью и устойчивостью к воздействию агрессивных углеводородных средThe effect of hollow polymeric microspheres Expancel 909 DU 80, Expancel 043 DUT 80, Expancel 920 DET 40d25, Expancel 920 DUT 40, Expancel 930 MB 120 and Lega Foam 120 MB on the rheometric parameters of the rubber compound, physical and mechanical and operational properties of oil and petrol resistant rubber was studied. The rubber mixture contained: isoprene SKI‑3 and butadiene- methylstyrene SKMS‑30ARK caoutchoucs, vulcanizing agent – sulfur; vulcanization accelerators – thiuram D and thiazol 2MBS; vulcanization activators – zinc white, stearin; fillers – carbon black N 220, carbon black T 900, natural chalk; softener – rosin; plasticizer – dibutyl phthalate; scorch retarder – N‑nitrosodiphenylamine. The rubber mixture was prepared on laboratory rolls LB 320 160/160 at a roll temperature of 60–70 °C. The vulcanization parameters of the rubber compound were studied on a Mon Tech MDR 3000 Basic rheometer at 150 °C for 30 min in accordance with ASTM D 2084–79. Standard samples for determining physical and mechanical properties were vulcanized at a temperature of 150 °C for 30 min in a P-V‑100–3RT‑2-PCD type vulcanizing press. The main characteristics of the vulcanizates were determined according to the standards in force in the rubber industry. It has been established that rubber containing Expancel 043 DUT 80 microspheres has the best physical and mechanical properties, high wear resistance and resistance to aggressive hydrocarbon medi

Investigation of the Dynamic Properties of Seawater-Resistant Rubber

Исследовано влияние каучуков, транс-полинорборнена, полиизобутилена П‑200 и сэвилена на вулканизационные характеристики, физико-механические и динамические свойства резины, используемой для изготовления изделий, контактирующих с морской водой. Установлено, что разработанная резина с серной вулканизующей системой на основе каучуков СКМС‑30АРК, СКН‑4065 и БК‑1675 с добавками транс-полинорборнена и сэвилена 11808-340 обладает улучшенными физико-механическими показателями, стойкостью к воздействию морской воды и повышенными динамическими свойствамиThe influence of rubbers, trans-polynorbornene, polyisobutylene P-200 and sevilene on vulcanization characteristics, physical-mechanical and dynamic properties of rubber used for the manufacture of products in contact with sea water has been investigated. It has been established that the developed rubber with a sulfur vulcanizing system based on rubbers SKMS-30ARK, SKN-4065 and BK-1675 with additives of trans-polynorbornene and sevilene 11808-340 has improved physical and mechanical characteristics, resistance to sea water and increased dynamic propertie

Study of the Effect of Silica Filler Silica 1165 on the Properties of Rubber for Rail Fastening Gaskets

Исследовано влияние кремнекислотного наполнителя Silica 1165 взамен каолина и технического углерода N220 на пласто-эластические, реометрические, физико-механические, эксплуатационные и динамические свойства резины на основе каучуков общего назначения с целью разработки эффективных шумо- и вибропоглощающих резиновых прокладок рельсовых скреплений для железнодорожных путей. Установлено, что применение кремнекислотного наполнителя Silica 1165 в составе исследованной резины приводит к повышению ее стойкости к преждевременной вулканизации, удовлетворительным физико-механическим свойствам и увеличению вибропоглощающих свойств, что является определяющим фактором для подрельсовых прокладокThe effect of silica filler Silica 1165 instead of kaolin and carbon black N220 on the plasto-elastic, rheometric, physical-mechanical, operational and dynamic properties of rubber based on general-purpose caoutchoucs was investigated in order to develop effective noise and vibration-absorbing rubber gaskets of rail fasteners for railway tracks. It has been established that the developed rubber with a sulfur vulcanizing system based on SKMS-30ARK, SKI-3 и SKD caoutchoucs with Silica 1165 additives has improved plasto-elastic and rheometric indicators, satisfactory physical and mechanical properties, is characterized by an increase in the vibration-absorbing properties of rubber, which is the determining factor for under-rail pad