Study of the microstructure resulting from brazed aluminium materials used in heat exchangers

Re-solidification of AA4343 cladding after brazing as well as the related precipitation in the modified AA3003 core material have been investigated. Analysis of the re-solidified material showed that partial dissolution of the core alloy occurs in both the brazing joints and away of them. Far from the brazing joints, the dissolution is, however, limited and diffusion of silicon from the liquid into the core material leads to solid-state precipitation in the so-called “band of dense precipitates” (BDP). On the contrary, the dissolution is enhanced in the brazing joint to such an extent that no BDP could be observed. The intermetallic phases present in the resolidified areas as well as in the core material have been analyzed and found to be mainly cubic alpha-Al(Mn,Fe)Si. These results were then compared to predictions made with available phase diagram information

Comprehension of demoulding mechanisms at the formwork/oil/concrete interface

The implementation of concrete and its association with a release agent influence the aesthetics of the concrete facings. The mineral oils tend to be replaced by vegetable formulations, to reduce the impact of the substances spilled in the environment. From a technical point of view, it is important to characterize the action of these new formulations at the interface concrete/oil/formwork. Two performing techniques have been used to study the physicochemical processes, the tribometry and electrochemical impedance spectroscopy. The correlation of the results obtained allowed to improve the understanding of the mechanisms involved at the interface mould/oil, in connection with the use of an acidifier in the formulation

Influence of normal and radial contributions of local current density on local electrochemical impedance spectroscopy.

A new tri-electrode probe is presented and applied to local electrochemical impedance spectroscopy (LEIS) measurements. As opposed to two-probe systems, the three-probe one allows measurement not only of normal, but also of radial contributions of local current densities to the local impedance values. The results concerning the cases of the blocking electrode and the electrode with faradaic reaction are discussed from the theoretical point of view for a disk electrode. Numerical simulations and experimental results are compared for the case of the ferri/ferrocyanide electrode reaction at the Pt working electrode disk. At the centre of the disk, the impedance taking into account both normal and radial contributions was in good agreement with the local impedance measured in terms of only the normal contribution. At the periphery of the electrode, the impedance taking into account both normal and radial contributions differed significantly from the local impedance measured in terms of only the normal contribution. The radial impedance results at the periphery of the electrode are in good agreement with the usual explanation that the associated larger current density is attributed to the geometry of the electrode, which exhibits a greater accessibility at the electrode edge

Adherence measurements and corrosion resistance in primer/hot-dip galvanized steel systems

This paper focuses on the adherence during ageing of a primer (made of polyester resins crosslinked with melamine) applied onto hot-dip galvanized (HDG) steel for coil coating application and its influence on corrosion protection. A chromium-free surface treatment, composed of fluorotitanic acid, phosphoric acid, manganese phosphate, and vinylphenol was applied on the HDG steel to obtain high corrosion resistance and high adherence of a polyester and melamine primer. The influence of the manganese phosphate on the corrosion and adherence was investigated. To measure the adherence between the metal and the primer, a three-point flexure test was set up. The adherence was then linked with corrosion resistance during ageing, using electrochemical impedance spectroscopy

Electrochemical behavior of magnesium alloys AZ91D, AZCe2, and AZLa1 in chloride and sulfate solutions

The influence of Cl- and SO42- on the electrochemical behavior of AZ91D, AZCe2, and AZLa1 was studied. For all alloys, there was a current plateau in the anodic polarization curves in Na2SO4 solutions. In 0.5% NaCl solution, there was a small current plateau, whereas there was none in the 3.5% and 5% NaCl solutions. This indicated that SO42- is less aggressive than Cl-. The range of the current plateau decreased with increasing SO42- concentration. For all alloys, the high frequency capacitive loop in the Nyquist plots decreased with increasing concentration consistent with the decrease in corrosion resistance with increasing Cl- and SO42- concentration