Analysis of Crystal Structure of the Welds with Friction-stir Welding Method on the Retreating Side for Bimetallic Disimilar Aa6061-cu Using Neutron Diffraction Techniques

Crystal structure analysis has been performed on bimetallic disimilar Al-Cu. Neutron diffraction analysis shows that Al lattice parameter decrease from 4.09 Å to 4.05 Å while the Cu lattice parameter is relatively constant. This is due to the melting point ofAl is much lower than the melting point of Cu. Physically, during the Friction Stir Welding (FSW) process in the Stir Zone (SZ) or Nuget Welded Zone (NWZ) region, strong deformation occurs at temperatures around 500 oC. This leads to dynamic recrystallization where grains become more refined. At the Thermo Mechanically Affected Zone (TMAZ) region, atomic diffusion occurs due to a combination of strong plastic deformation at high temperatures. And for Heat Affected Zone (HAZ) area there are aluminium even with a very small percentage of weight, this is due to the exposure at a high temperature during the heating FSW process, similar with annnealing-like process, which leads to the dislocation disappears, dissolves and precipitates grain becomes rough when the temperature exceeds 250 oC

ANALISIS STRUKTUR KRISTAL HASIL LAS FRICTION-STIR WELDING PADA RETREATING SIDE BIMETAL DISIMILAR AA6061-Cu DENGAN TEKNIK DIFRAKSI NEUTRON

ANALISIS STRUKTUR KRISTAL HASIL LAS FRICTION-STIR WELDING PADA RETREATING SIDE BIMETAL DISIMILAR AA6061-Cu DENGAN TEKNIK DIFRAKSI NEUTRON. Telah dilakukan analisis struktur kristal pada paduan bimetal disimilar Al-Cu. Dari analisis difraksi neutron telah terjadi penurunan parameter kisi Al dari 4,09 Å menjadi 4,05 Å sedangkan parameter kisi Cu relatif konstan. Hal ini disebabkan titik lelehAl jauh lebih rendah dari titik leleh Cu. Secara fisis hal ini terjadi karena selama proses Friction Stir Welding (FSW) pada daerah Stir Zone (SZ) or Nuget Welded Zone (NWZ) terjadi deformasi yang kuat pada suhu sekitar 500 oC. Hal ini menyebabkan rekristalisasi secara dinamis, dimana butir menjadi lebih halus. Pada daerah Thermo Mechanically Affected Zone (TMAZ), terjadi difusi atomik yang disebabkan oleh kombinasi antara deformasi plastik yang kuat dengan suhu tinggi. Untuk daerah Heat Affected Zone (HAZ) masih terdapat aluminium dengan prosentase berat yang sangat kecil, hal ini disebabkan adanya paparan (exposure) pada suhu tinggi selama proses pemanasan FSW, mirip dengan proses annealing (annnealing-like proCess), yang menyebabkan dislokasi lenyap, presipitat melarut dan butir menjadi kasar apabila suhu melebihi 250 oC