In Situ X-ray Raman Scattering Spectroscopy of the Formation of Cobalt Carbides in a Co/TiO2 Fischer–Tropsch Synthesis Catalyst

We present in situ experiments to study the possible formation of cobalt carbides during Fischer–Tropsch synthesis (FTS) in a Co/TiO2 catalyst at relevant conditions of pressure and temperature. The experiments were performed by a combination of X-ray Raman scattering (XRS) spectroscopy and X-ray diffraction (XRD). Two different experiments were performed: (1) a Fischer–Tropsch Synthesis (FTS) reaction of an ∼14 wt % Co/TiO2 catalyst at 523 K and 5 bar under H2 lean conditions (i.e., a H2:CO ratio of 0.5) and (2) carburization of pure cobalt (as reference experiment). In both experiments, the Co L3-edge XRS spectra reveal a change in the oxidation state of the cobalt nanoparticles, which we assign to the formation of cobalt carbide (Co2C). The C K edge XRS spectra were used to quantify the formation of different carbon species in both experiments.Peer reviewe

Sweet, Sugar-Coated Hierarchical Platinum Nanostructures for Easy Support, Heterogenization and Separation

Metal nanoparticles are increasingly gaining interest in the field of heterogeneous catalysis. Here, we present a novel strategy for synthesizing sugar-coated platinum nanostructures (SC-Pt-NS) from the carbohydrates sucrose and D(-)-fructose. In the synthesis from a mixture of H2PtCl6 center dot 6H(2)O, the carbohydrate in an ionic liquid (IL) yielded primary particles of a homogeneous average size of similar to 10 nm, which were aggregated to hierarchical Pt nanostructures of similar to 40-65 nm and surrounded or supported by the carbohydrate. These sugar-coated platinum nanostructures present a facile way to support and heterogenize nanoparticles, avoid leaching and enable easier separation and handling. The catalytic activity of the SC-Pt-NS was shown in the hydrosilylation test reaction of phenylacetylene with triethylsilane, where very high turnover frequency (TOF) values of up to 87,200 h(-1) could be achieved, while the platinum metal leaching into the product was very low