Importanza delle rappresentazioni sociali nell'analisi delle comunità territoriali; il riduttivismo dell'economicismo e la necessità di considerare anche le risorse immateriali. La risorsa-tempo e la risorsa-spazio. Il mutamento sociale in Umbria e il cambiamento delle sue chiavi di lettura: dalla metafora della spugna (società apparentemente statica ma in grado di assorbire tensioni e contraddizioni) alla metafora del "patchwork" (complessità, differenzazione sociale e simbolica)

Hybrid ceramic self-healing coatings for corrosion protection of Al alloys in 3% NaCl solution

This work focuses on the development of sol–gel self-healing coatings for corrosion protection of Al alloys. The use of this method will help to reduce the costs associated with the coating as well as their environmental impact. Coatings were made of a titania matrix loaded with microparticles of poly(vinyl-alcohol) (PVA) containing cerium nitrate as an inhibitor. The PVA particles dissolve in water, so that the cerium nitrate deposits on the Al surface subjected to corrosion. The PVA microspheres were made via the emulsion method, and then loaded with cerium nitrate. The amount of cerium nitrate loaded in the microspheres was evaluated using UV–Vis. As a second step, the titania coating with embedded PVA microspheres loaded with cerium nitrate was deposited on an AA6082 substrate via a sol–gel route. The corrosion resistance of the coated samples was tested in NaCl solution. The coating microstructure, before and after the corrosion tests, was analysed with the use of an SEM (scanning electron microscope) and EDS (energy dispersive spectroscopy), while the corrosion resistance was investigated by EIS (electrochemical impedance spectroscopy). The results showed that the coatings were uniform and compact. They also showed the ability of the hybrid TiO2-based coating to provide protection for the AA6082 from corrosion. The coatings with an induced defect (scratch) were also analysed, and the EIS analysis of the coatings over time showed an increase in resistance, confirming the ability of the coating to heal itself

RIVESTIMENTI ANTI-CORROSIVI DI ALLUMINA DEPOSITATI MEDIANTE LETTO FLUIDO

In questo articolo vengono illustrati i risultati di prove di resistenza alla corrosione eseguite su campioni di alluminio AA 6082 T6 rivestiti con un film di Al2O3 depositato mediante letto fluido. Sono state preparate 4 serie di provini con diversi tempi di deposizione (tra 30 e 240 minuti). Le prove di corrosione sono state eseguite mediante Spettroscopia di Impedenza Elettrochimica (EIS), Rumore Elettrochimico (ENA) e Impedenza Elettrochimica Localizzata (LEIS). I risultati hanno evidenziato una migliore resistenza alla corrosione dei campioni trattati fino a 120 minuti, mentre prestazioni più scadenti sono state registrate per i campioni sottoposti a tempi di deposizione superiori

Extra-low dosage graphene oxide cementitious nanocomposites: a nano- to macroscale approach

The impact of extra-low dosage (0.01% by weight of cement) Graphene Oxide (GO) on the properties of fresh and hardened nanocomposites was assessed. The use of a minimum amount of 2-D nanofiller would minimize costs and sustainability issues, therefore encouraging the market uptake of nanoengineered cement-based materials. GO was characterized by X-ray Photoelectron Spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR), Atomic Force Microscopy (AFM), X-ray Diffraction (XRD), and Raman spectroscopy. GO consisted of stacked sheets up to 600 nm × 800 nm wide and 2 nm thick, oxygen content 31 at%. The impact of GO on the fresh admixtures was evaluated by rheology, flowability, and workability measurements. GO-modified samples were characterized by density measurements, Scanning Electron Microscopy (SEM) analysis, and compression and bending tests. Permeability was investigated using the boiling-water saturation technique, salt ponding test, and Initial Surface Absorption Test (ISAT). At 28 days, GO-nanocomposite exhibited increased density (+14%), improved compressive and flexural strength (+29% and +13%, respectively), and decreased permeability compared to the control sample. The strengthening effect dominated over the adverse effects associated with the worsening of the fresh properties; reduced permeability was mainly attributed to the refining of the pore network induced by the presence of GO

Citric acid aerospace stainless steel passivation: a green approach

Passivation is a common treatment to maximize the corrosion resistance of stainless steel. Nitric acid is generally used and involves several ecological problems, citric acid could be a promising and environmentally friendly alternative to nitric acid. In this work citric acid has been extracted from lemon waste using and eco- friendly procedure. The stainless steel samples have been treated in both nitric and citric acid (commercial and extracted) and corrosion test have been performed. The results show how citric acid can be used as substitute of nitric acid in passivation treatment

Extra-low dosage graphene oxide cementitious nanocomposites: A nano-to macroscale approach

Copyright: © 2021 by the authors. The impact of extra-low dosage (0.01% by weight of cement) Graphene Oxide (GO) on the properties of fresh and hardened nanocomposites was assessed. The use of a minimum amount of 2-D nanofiller would minimize costs and sustainability issues, therefore encouraging the market uptake of nanoengineered cement-based materials. GO was characterized by X-ray Photoelectron Spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR), Atomic Force Microscopy (AFM), X-ray Diffraction (XRD), and Raman spectroscopy. GO consisted of stacked sheets up to 600 nm × 800 nm wide and 2 nm thick, oxygen content 31 at%. The impact of GO on the fresh admixtures was evaluated by rheology, flowability, and workability measurements. GO-modified samples were characterized by density measurements, Scanning Electron Microscopy (SEM) analysis, and compression and bending tests. Permeability was investigated using the boiling-water saturation technique, salt ponding test, and Initial Surface Absorption Test (ISAT). At 28 days, GO-nanocomposite exhibited increased density (+14%), improved compressive and flexural strength (+29% and +13%, respectively), and decreased permeability compared to the control sample. The strengthening effect dominated over the adverse effects associated with the worsening of the fresh properties; reduced permeability was mainly attributed to the refining of the pore network induced by the presence of GO

New Materials and Technologies for Durability and Conservation of Building Heritage

The increase in concrete structures’ durability is a milestone to improve the sustainability of buildings and infrastructures. In order to ensure a prolonged service life, it is necessary to detect the deterioration of materials by means of monitoring systems aimed at evaluating not only the penetration of aggressive substances into concrete but also the corrosion of carbon-steel reinforcement. Therefore, proper data collection makes it possible to plan suitable restoration works which can be carried out with traditional or innovative techniques and materials. This work focuses on building heritage and it highlights the most recent findings for the conservation and restoration of reinforced concrete structures and masonry buildings