Modification of structure of the surface of steel (ХГС) as a result of influences of high-current electron beam

The steel surface (ХГС) was irradiated with a high-current electron beam. A high-current electron beam was obtained in the TEMP-A accelerator. Steel samples were made from drum mill balls. The balls had varying degrees of wear. The mechanical and microstructural characteristics were studied. Applied methods: measurement of hardness, tensile strength, fractographic and metallographic analysis. An increase in hardness was found for all samples. An increase in the surface hardness of the samples occurred as a result of the conversion of austenite to martensite and lower bainite. A significant effect on the increase in surface hardness of the samples is also exerted by the process of the appearance of carbides.Поверхня сталі (ХГС) була опромінена сильнострумовим електронним пучком. Сильнострумовий електронний пучок отримали в прискорювачі ТЕМП-А. Зразки сталі були виготовлені з куль барабанного млина. Кулі були різного ступеня зносу. Вивчалися механічні і мікроструктурні характеристики. Застосовували методики: вимірювання твердості, в'язкості на розривання, фрактографічний і металографічний аналізи. Для всіх зразків виявлено збільшення твердості. Збільшення твердості поверхні зразків відбувалося в результаті перетворення аустеніту в мартенсіт та нижній бейніт. Істотний вплив на збільшення твердості поверхні зразків також надає процес появи карбідів.Поверхность стали (ХГС) была облучена сильноточным электронным пучком. Сильноточный электронный пучок получили в ускорителе ТЕМП-А. Образцы стали были изготовлены из шаров барабанной мельницы. Шары имели различную степень износа. Изучались механические и микроструктурные характеристики. Применяли методики: измерение твердости, вязкости на разрыв, фрактографический и металлографический анализы. Для всех образцов обнаружено увеличение твердости. Увеличение твердости поверхности образцов происходило в результате преобразования аустенита в мартенсит и нижний бейнит. Существенное влияние на увеличение твердости поверхности образцов также оказывает процесс появления карбидов

Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam

9ХФМ steel was irradiated with a high-current electron beam. The high-current electron beam was obtained in the TEMP-A accelerator. The irradiation was performed for various samples of the material of a ball mill drum. Part of the samples were taken from the surface of the balls, which had different degrees of wear. Samples taken from the depth of the balls, which is equal to half the diameter, were also irradiated. Microhardness measurements, metallographic, and fractographic analysis were used to study mechanical and microstructural changes. In all cases, a change in hardness was detected. The degree of change in hardness is different for different samples. Based on fractographic analysis, using SEM microscopy, one of the mechanisms that contribute to increasing the surface hardness is determined. This mechanism is the cleaning of the surface of samples from impurities of phosphorus and sulfur using a high-current electron beam.Сталь 9ХФМ була опромінена сильнострумовим електронним пучком, який отримано в прискорювачі ТЕМП-А. Опромінення проводили для різних зразків матеріалу кулі барабанного млина. Частина зразків була взята з поверхонь куль, які мали різний ступінь зносу. Також опромінювали зразки, узяті з глибини куль, яка була рівна половині діаметра. Для вивчення механічних і мікроструктурних змін застосовували виміри мікротвердості, металографічний і фрактографічний аналізи. У всіх випадках виявлена зміна твердості та пластичності. Для різних зразків ступінь зміни твердості та пластичності різна. На основі фрактогрaфічного аналізу з використанням РЕМ-мікроскопії визначений один з механізмів, який сприяє підвищенню твердості поверхні. Цим механізмом є очищення поверхні зразків за допомогою сильнострумового пучка електронів від домішок фосфору і сірки.Сталь 9ХФМ была облучена сильноточным электронным пучком, который получен в ускорителе ТЕМПА. Облучение проводили для различных образцов материала шара барабанной мельницы. Часть образцов взята с поверхности шаров, которые имели различную степень износа. Также облучали образцы, взятые из глубины шаров, которая равна половине диаметра. Для изучения механических и микроструктурных изменений применяли измерения микротвердости, металлографический и фрактографический анализы. Во всех случаях обнаружено изменение твердости. Для различных образцов степень изменения твердости различна. На основе фрактогрaфического анализа с использованием РЭМ-микроскопии определен один из механизмов, который способствует повышению твердости поверхности. Этим механизмом является очистка поверхности образцов с помощью сильноточного пучка электронов от примесей фосфора и серы