Exchange bias in polycrystalline magnetite films made by ion-beam assisted deposition
Iron oxide films were produced using ion-beam-assisted deposition, and Raman spectroscopy and x-ray diffraction indicate single-phase magnetite. However, incorporation of significant fractions of argon in the films from ion bombardment is evident from chemical analysis, and Fe/O ratios are lower than expected from pure magnetite, suggesting greater than normal disorder. Low temperature magnetometry and first-order reversal curve measurements show strong exchange bias, which likely arises from defects at grain boundaries, possibly amorphous, creating frustrated spins. Since these samples contain grains ∼6 nm, a large fraction of the material consists of grain boundaries, where spins are highly disordered and reverse independently with external field
Exchange bias in polycrystalline magnetite films made by ion-beam assisted deposition
Iron oxide films were produced using ion-beam-assisted deposition, and Raman spectroscopy and x-ray diffraction indicate single-phase magnetite. However, incorporation of significant fractions of argon in the films from ion bombardment is evident from chemical analysis, and Fe/O ratios are lower than expected from pure magnetite, suggesting greater than normal disorder. Low temperature magnetometry and first-order reversal curve measurements show strong exchange bias, which likely arises from defects at grain boundaries, possibly amorphous, creating frustrated spins. Since these samples contain grains ∼6 nm, a large fraction of the material consists of grain boundaries, where spins are highly disordered and reverse independently with external field
Recommended from our members
Ion irradiation of Fe-Fe oxide core-shell nanocluster films: Effect of interface on stability of magnetic properties
A cluster deposition method was used to produce films of loosely aggregated nanoclusters (NCs) of Fe core-Fe3O4 shell or fully oxidized Fe3O4. Films of these NC on Si(100) or MgO(100)/Fe3O4(100) were irradiated to 1016 Si2+/cm2 near room temperature using an ion accelerator. Ion irradiation creates structural change in the NC film with corresponding chemical and magnetic changes which depend on the initial oxidation state of the cluster. Films were characterized using magnetometry (hysteresis, first order reversal curves), microscopy (transmission electron, helium ion), and x-ray diffraction. In all cases, the particle sizes increased due to ion irradiation, and when a core of Fe is present, irradiation reduces the oxide shells to lower valent Fe species. These results show that ion irradiated behavior of the NC films depends strongly on the initial nanostructure and chemistry, but in general saturation magnetization decreases slightly. © 2013 AIP Publishing LLC