Tribological characteristics of perfluoropolyether liquid lubricants under sliding conditions in high vacuum

Tribological characteristics of three PFPE's (Fomblin Z, Demnum, and Krytox) were studied under high vacuum using a four-ball apparatus with 440C steel specimens. Fomblin Z and Demnum exhibited initial scuffing-like high friction whereas Krytox did not. Steady state friction with Fomblin Z was the lowest among the three oils. Frictional values for Demnum and Krytox were almost the same. The lowest wear rate in air was provided by Krytox regardless of load, and low wear rates in vacuum at high load were achieved with Krytox and Demnum. Results are explained by reactivity and pressure-viscosity characteristics of the oils

Tribological Characteristics of Perfluoropolyether Liquid Lubricants Under Sliding Conditions in High Vacuum

Tribological characteristics of three PFPE\u27s (Fomblin Z, Demnum, and Krytox) were studied under high vacuum using a four-ball apparatus with 440C steel specimens. Fomblin Z and Demnum exhibited initial scuffing-like high friction whereas Krytox did not. Steady state friction with Fomblin Z was the lowest among the three oils. Frictional values for Demnum and Krytox were almost the same. The lowest wear rate in air was provided by Krytox regardless of load, and low wear rates in vacuum at high load were achieved with Krytox and Demnum. Results are explained by reactivity and pressure-viscosity characteristics of the oils

XPS analysis of 440C steel surfaces lubricated with perfluoropolyethers under sliding conditions in high vacuum

This work presents the results of the X-Ray Photoelectron Spectroscopy (XPS) analysis of AISI 440C ball surfaces lubricated with perfluoropolyether (PFPE) oils after friction experiments under sliding conditions at high load in air and vacuum environments. The PFPE lubricants tested were Demnum S100, Fomblin Z-25, and Krytox 143AB. It was found that all the PFPE lubricants were degraded by sliding contact causing the formation of inorganic fluorides on the metallic surfaces and a layer of organic decomposition products. KRYTOX 143AB was the least reactive of the three lubricants tested. It was also found that metal fluoride formed at off-scar areas. This suggests the formation of reactive species, such as COF2 or R(sub f)COF, during sliding experiments, which can diffuse through the lubricant film and react with the metallic surfaces away from the contact region. Comparison of reference specimens before sliding with those that had undergone the sliding tests showed that the amount of non-degraded PFPE remaining on the surface of the balls after the sliding experiments was greater than that of the balls without sliding

A vacuum four-ball tribometer to evaluate liquid lubricants for space applications

The design and operation of a vacuum tribometer, based on the four-ball configuration, is described. This tribometer evaluates the tribological characteristics of liquid lubricants for space applications. Operating conditions include: room temperature, loads to approximately 1000N, speeds to approximately 500 rpm, and pressures of approximately 10(exp -6)Pa. Tests can also be run at atmospheric pressure with air or nitrogen. Some typical test results are included