Tooth Discoloration Resulting from a Nano Zinc Oxide-Eugenol Sealer

Introduction: A desirable quality of any endodontic sealer is its ability to be tooth color friendly. Therefore the aim of the present study was to evaluate the tooth discoloration potential of a nano zinc oxide-eugenol (NZOE) sealer. Methods and Materials: In order to evaluate tooth discoloration, the pulp chamber of 60 human maxillary central and lateral incisors were filled with one of the sealers, naming AH-26 (resin-based sealer), Pulpdent sealer (ZOE-based) and a NZOE experimental sealer. Color measurements was assessed at the baseline (before placement of sealers) (T0), 24 h (T1) and 72 h (T2) h, 1-week (T3), and 1-month (T4) after the placement of sealers using the Easy Shade spectrophotometer. Data were analyzed in SPSS software using one-way ANOVA, and repeated measured ANOVA. Results: No significant differences were observed when the paired comparison test was performed (P>0.05). Conclusion: The tested nZOE sealer had similar tooth discoloration potential in comparison with AH-26 and ZOE sealer.Keywords: Nano Particle; Root Canal Sealer; Tooth Discoloration; Spectrophotometry; Zinc-Oxide Eugenol

In Vitro Cytotoxicity of a New Nano Root Canal Sealer on Human Gingival Fibroblasts

Introduction: The aim of this in vitro study was to evaluate the cytotoxicity of a new nano zinc-oxide eugenol (NZOE) sealer on human gingival fibroblasts (HGFs) compared with Pulpdent (micro-sized ZOE sealer) and AH-26 (resin-based sealer). Methods and Materials: The Pulpdent, AH-26, and NZOE sealers were prepared and exposed to cell culture media immediately after setting, and 24 h and one week after setting. Then, the primary cultured HGFs were incubated for 24 h with different dilutions (1:1 to 1:32) of each sealer extract. Cell viability was evaluated by methyl thiazolyl diphenyl tetrazolium bromide (MTT) assay. The results were compared using two-way analysis of variance followed by Tukey’s post hoc test. The level of significance was set at 0.05. Results: All sealer extracts, up to 32 times dilutions, showed cytotoxicity when exposed to HGF immediately after setting. The extracts obtained 24 h or one week after setting showed lower cytotoxicity than extracts obtained immediately after setting. At all setting times, NZOE showed lower cytotoxicity than Pulpdent and AH-26. While one-week extracts of NZOE had no significant effect on the viability of HGF at dilutions 1:4 to 1:32, both Pulpdent and AH-26 decreased the cell viability at dilutions of 1:4 and 1:8. Conclusion: NZOE exhibited lower cytotoxicity compared to Pulpdent and AH-26 on HGF and has the potential to be considered as a new root canal filling material.Keywords: Cytotoxicity; Human Gingival Fibroblast; MTT assay; Nano; Seale

Cytotoxicity of a New Nano Zinc-Oxide Eugenol Sealer on Murine Fibroblasts

Introduction: The aim of this study was to evaluate the cytotoxicity of a new nano zinc-oxide eugenol (NZOE) sealer in comparison with AH-26 and Pulpdent root canal sealers. Methods and Materials: The L929 mouse fibroblast cells were cultivated and incubated for 24, 48 or 72 h with different dilutions (1/1, 1/2, 1/4, 1/8, 1/16 and 1/32) of culture media previously exposed to either of the test sealers naming NZOE, AH-26 or Pulpdent. At the end of incubation period, the effect of sealers on cell viability was evaluated using Mosmann’s Tetrazolium Toxicity (MTT) colorimetric assay. The data was compared using the one-way analysis of variance (ANOVA) followed by the Tukey’s post hoc test for multiple comparisons. Results: After 24, 48 or 72 h, both NZOE and Pulpdent sealers inhibited cell viability at 1/1, 1/2 and 1/8 dilutions. Within the 24 and 48 h, the AH-26 sealer reduced the cell viability at all dilutions except the 1/32 solution; however after 72 h even the 1/32 dilution was cytotoxic. Conclusion: The biocompatibility of the nano zinc-oxide eugenol sealer was comparable to Pulpdent sealer and lower than AH-26.Keywords: Cytotoxicity; MTT Assay; Nanoparticles; Root Canal Sealer; Zinc-Oxide Eugenol