Plasma Treatment of Agave

Composites based on low-density polyethylene (LDPE) were prepared with Agave fiber powder (AFP) that was coated by plasma polymerization process using ethylene gas. Treated and pristine AFP were analyzed by infrared spectroscopy, scanning electron microscopy, and contact water angle for the assessment of surface properties. The polymer composites were prepared by melt mixing using 0, 5, 10, and 20 wt% of AFP and their mechanical and thermal properties were measured. Dispersion evaluation in water confirmed that the AFP treated changed from hydrophilic to hydrophobic behavior and it was also corroborated with water contact angle tests. The addition of treated and untreated AFP (200 mesh) at 20 wt% promotes an increase of Young’s modulus of the composites of up to 60% and 32%, respectively, in relation to the neat matrix. Also, an increase of crystallinity of LDPE was observed by the addition of treated and untreated AFP; however no significant effect on the crystallization temperature was observed in LDPE containing AFP

Fully Bio-Based Elastomer Nanocomposites Comprising Polyfarnesene Reinforced with Plasma-Modified Cellulose Nanocrystals

This article proposes a process to prepare fully bio-based elastomer nanocomposites based on polyfarnesene and cellulose nanocrystals (CNC). To improve the compatibility of cellulose with the hydrophobic matrix of polyfarnesene, the surface of CNC was modified via plasma-induced polymerization, at different powers of the plasma generator, using a trans-β-farnesene monomer in the plasma reactor. The characteristic features of plasma surface-modified CNC have been corroborated by spectroscopic (XPS) and microscopic (AFM) analyses. Moreover, the cellulose nanocrystals modified at 150 W have been selected to reinforce polyfarnesene-based nanocomposites, synthesized via an in-situ coordination polymerization using a neodymium-based catalytic system. The effect of the different loading content of nanocrystals on the polymerization behavior, as well as on the rheological aspects, was evaluated. The increase in the storage modulus with the incorporation of superficially modified nanocrystals was demonstrated by rheological measurements and these materials exhibited better properties than those containing pristine cellulose nanocrystals. Moreover, we elucidate that the viscoelastic moduli of the elastomer nanocomposites are aligned with power– law model systems with characteristic relaxation time scales similar to commercial nanocomposites, also implying tunable mechanical properties. In this foreground, our findings have important implications in the development of fully bio-based nanocomposites in close competition with the commercial stock, thereby producing alternatives in favor of sustainable materials

Surface Modification of Sodium Montmorillonite Nanoclay by Plasma Polymerization and Its Effect on the Properties of Polystyrene Nanocomposites

Sodium montmorillonite nanoclay (Na+-MMT) was modified by plasma polymerization with methyl methacrylate (MMA) and styrene (St) as monomers and was denominated as Na+-MMT/MMA and Na+-MMT/St, respectively. This plasma modified nanoclay was used as reinforcement for polystyrene (PS) nanocomposites that were prepared by melt mixing. Pristine and modified Na+-MMT nanoclay were analyzed by the dispersion in various solvents, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). The results confirmed a change in hydrophilicity of the modified Na+-MMT, as well as the presence of a polymeric material over its surface. The pristine PS/Na+-MMT and modified PS/Na+-MMT/MMA and PS/Na+-MMT/St nanocomposites were studied with X-ray diffraction (XRD), differential scanning calorimetry (DSC), and TGA, as well as mechanical properties. It was found that the PS/Na+-MMT/St nanocomposites presented better thermal properties and an improvement in Young’s modulus (YM) in compared to PS/Na+-MMT/MMA nanocomposites

Surface Modification of Carbon Nanofibers and Graphene Platelets Mixtures by Plasma Polymerization of Propylene

Carbon nanofibers (CNFs), graphene platelets (GPs), and their mixtures were treated by plasma polymerization of propylene. The carbon nanoparticles (CNPs) were previously sonicated in order to deagglomerate and increase the surface area. Untreated and plasma treated CNPs were analyzed by dynamic light scattering (DLS), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, and thermogravimetric analysis (TGA). DLS analysis showed a significant reduction of average particle size, due to the sonication pretreatment. Plasma polymerized propylene was deposited on the CNPs surface; the total amount of polymerized propylene was from 4.68 to 6.58 wt-%. Raman spectroscopy indicates an increase in the sp3 hybridization of the treated samples, which suggest that the polymerized propylene is grafted onto the CNPs

Cold plasma copolymer with antimicrobial activity deposited on three different substrates

Abstract A good strategy to prevent early deposition of bacteria that can form biofilms is the application of antimicrobial coatings to existing surfaces, however this field has been little explored and coatings are often non uniform in thickness. A homogeneous film of R-Carvone-Octadiene (ppCop) was deposited on different substrates (coverslip, minced coverslip and fabric) by cold plasma copolymerization to study the influence of the substrate on antimicrobial activity and show clues about the influence of octadiene on copolymerization. The ppCop showed better antimicrobial activity results on the substrate with higher effective contact area, highlighting the influence of this variable on antimicrobial activity. The ppCop deposited on minced coverslip showed an inhibition of E. coli and S. aureus bacteria by 48.69 ±0.08% and 49.31 ±0.58% respectively, with an average roughness of 14.1±0.02 nm and a static water contact angle of 79± 0.4°. The ppCop showed no cytotoxicity to the human cell line