Behaviour of methylmethacrylate-acrylonitrile random copolymers in dilute solution

Studies on the dilute solution properties of methylmethacrylate-acrylonitrile random copolymers of three different compositions, 0.236, 0.5 and 0.74 mole fraction (m.f.) of acrylonitrile (AN) designated as MAa, MAb and MAc, respectively, have been made in good solvents and theta solvents. MAa has been studied in benzene (Bz) and ethylacetate (EAc). MAb in acetonitrile (MeCN), dimethyl sulphoxide (DMSO) and a binary solvent mixture of Bz and dimentyl formamide (DMF) in the volume ratio 6.5:1 designated as BM1 and MAc in MeCN, DMSO and Bz + DMF in the volume ratio 1.667:1 designated as BM2. The Mark-Houwink exponent ‘a’ reveals that Bz is a theta solvent for MAa at 20°C. For MAb and MAc, BM1 and BM2, respectively have ‘a’ values of 0.5 at all three temperatures studied (30°, 40° and 50°C). It is not clear whether they represent theta states or preferential adsorption plays a role complicating the behaviour in solution. The values of A2 are very low in MeCN considering that it is a very good solvent for the copolymer, ‘a’ values for MAb and MAc being 0.75 and 0.7, respectively

Large polarization gradients and temperature-stable responses in compositionally-graded ferroelectrics

A range of modern applications require large and tunable dielectric, piezoelectric or pyroelectric response of ferroelectrics. Such effects are intimately connected to the nature of polarization and how it responds to externally applied stimuli. Ferroelectric susceptibilities are, in general, strongly temperature dependent, diminishing rapidly as one transitions away from the ferroelectric phase transition (TC). In turn, researchers seek new routes to manipulate polarization to simultaneously enhance susceptibilities and broaden operational temperature ranges. Here, we demonstrate such a capability by creating composition and strain gradients in Ba1-xSrxTiO3 films which result in spatial polarization gradients as large as 35 μC cm-2 across a 150 nm thick film. These polarization gradients allow for large dielectric permittivity with low loss (ɛr≈775, tan δ<0.05), negligible temperature-dependence (13% deviation over 500 °C) and high-dielectric tunability (greater than 70% across a 300 °C range). The role of space charges in stabilizing polarization gradients is also discussed