2 research outputs found
Assessment of Degree of Conversion and Volumetric Shrinkage of Novel Self-Adhesive Cement
The degree of monomer conversion and polymerization shrinkage are two of the main reasons for potential adhesion failure between the tooth structure and the restoration substrate. To evaluate the degree of conversion and polymerization shrinkage of a newly developed self-adhesive resin cement, the degree of conversion (DC) was measured using FTIR under different activation modes, temperatures, and times. Volumetric shrinkage was tested using the AcuVol video imaging method. The experimental cement showed a higher DC than other cements under self-curing. The DC of the experimental cement was higher than that of other cements, except SpeedCem Plus under light curing. The experimental cement had a higher DC than other cements, except SpeedCem Plus in some conditions under dual curing. All self-adhesive cements had a higher DC at 37 °C than at 23 °C under self-curing, and there was no statistical difference between 23 °C and 37 °C under light curing. All self-adhesive cements showed a significantly higher DC at 10 min than at 5 min under self-curing. There was no statistical difference between 5 min and 10 min for most cements under dual curing. All self-adhesive cements statistically had the same volumetric shrinkage under light curing and self-curing. The newly developed self-adhesive resin cement exhibited a higher degree of conversion and similar volumetric shrinkage compared to these commercial self-adhesive resin cements
Recommended from our members
Multiscale mechanical characterization of biobased photopolymers towards sustainable vat polymerization 3D printing
In vat polymerization (VP) 3D printing, there is an urgent need to expand characterization efforts for resins derived from natural resources to counter the increasing consumption of fossil fuels required to synthesize conventional monomers. Here, we apply multiscale mechanical characterization techniques to interrogate a 3D printed biobased copolymer along a controlled range of monomer ratios. We varied the concentration of two dissimilar monomers to derive structural information about the polymer networks. Current research primarily considers the macroscale, but recent understanding of the process-induced anisotropy in 3D printed layers suggests a multiscale approach is critical. By combining typical macroscopic techniques with micro- and nanoscale analogues, clear correlations in the processing-structure-property relationships appeared. We observed that measured moduli were always greater via surface-localized methods, but property differences between formulations were easier to identify. As researchers continue to develop novel sustainable biopolymers that match or exceed the performance of commercial resins, it is vital to understand the multiscale relationships between the VP process, the structure of the formed polymer networks, and the resultant properties