Effects of low intensity pulsed ultrasound with and without increased cortical porosity on structural bone allograft incorporation

<p>Abstract</p> <p>Background</p> <p>Though used for over a century, structural bone allografts suffer from a high rate of mechanical failure due to limited graft revitalization even after extended periods <it>in vivo</it>. Novel strategies that aim to improve graft incorporation are lacking but necessary to improve the long-term clinical outcome of patients receiving bone allografts. The current study evaluated the effect of low-intensity pulsed ultrasound (LIPUS), a potent exogenous biophysical stimulus used clinically to accelerate the course of fresh fracture healing, and longitudinal allograft perforations (LAP) as non-invasive therapies to improve revitalization of intercalary allografts in a sheep model.</p> <p>Methods</p> <p>Fifteen skeletally-mature ewes were assigned to five experimental groups based on allograft type and treatment: +CTL, -CTL, LIPUS, LAP, LIPUS+LAP. The +CTL animals (n = 3) received a tibial ostectomy with immediate replacement of the resected autologous graft. The -CTL group (n = 3) received fresh frozen ovine tibial allografts. The +CTL and -CTL groups did not receive LAP or LIPUS treatments. The LIPUS treatment group (n = 3), following grafting with fresh frozen ovine tibial allografts, received ultrasound stimulation for 20 minutes/day, 5 days/week, for the duration of the healing period. The LAP treatment group (n = 3) received fresh frozen ovine allografts with 500 μm longitudinal perforations that extended 10 mm into the graft. The LIPUS+LAP treatment group (n = 3) received both LIPUS and LAP interventions. All animals were humanely euthanized four months following graft transplantation for biomechanical and histological analysis.</p> <p>Results</p> <p>After four months of healing, daily LIPUS stimulation of the host-allograft junctions, alone or in combination with LAP, resulted in 30% increases in reconstruction stiffness, paralleled by significant increases (p < 0.001) in callus maturity and periosteal bridging across the host/allograft interfaces. Longitudinal perforations extending 10 mm into the proximal and distal endplates filled to varying degrees with new appositional bone and significantly accelerated revitalization of the allografts compared to controls.</p> <p>Conclusion</p> <p>The current study has demonstrated in a large animal model the potential of both LIPUS and LAP therapy to improve the degree of allograft incorporation. LAP may provide an option for increasing porosity, and thus potential <it>in vivo </it>osseous apposition and revitalization, without adversely affecting the structural integrity of the graft.</p

An Ultrasound Assisted Anchoring Technique (BoneWelding® Technology) for Fixation of Implants to Bone – A Histological Pilot Study in Sheep

The BoneWelding® Technology offers new opportunities to anchor implants within bone. The technology melted the surface of biodegradable polymer pins by means of ultrasound energy to mould material into the structures of the predrilled bone. Temperature changes were measured at the sites of implantation in an in vitro experiment. In the in vivo part of the study two types of implants were implanted in the limb of sheep to investigate the biocompatibility of the method. One implant type was made of PL-DL-lactide (PLA), the second one was a titanium core partially covered with PLA. Healing period was 2 and 6 months, with 3 sheep per group. Bone samples were evaluated radiologically, histologically and histomorphometrically for bone remodeling and inflammatory reactions. Results demonstrated mild and short temperature increase during insertion. New bone formed at the implant without evidence of inflammatory reaction. The amount of adjacent bone was increased compared to normal cancellous bone. It was concluded that the BoneWelding® Technology proved to be a biocompatible technology to anchor biodegradable as well as titanium-PLA implants in bone

Effect of rehabilitation exercise durations on the dynamic bone repair process by coupling polymer scaffold degradation and bone formation

Implantation of biodegradable scaffold is considered as a promising method to treat bone disorders, but knowledge of the dynamic bone repair process is extremely limited. In this study, based on the representative volume cell of a periodic scaffold, the influence of rehabilitation exercise duration per day on the bone repair was investigated by a computational framework. The framework coupled scaffold degradation and bone remodeling. The scaffold degradation was described by a function of stochastic hydrolysis independent of mechanical stimulation, and the bone formation was remodeled by a function of the mechanical stimulation, i.e., strain energy density. Then, numerical simulations were performed to study the dynamic bone repair process. The results showed that the scaffold degradation and the bone formation in the process were competitive. An optimal exercise duration per day emerged. All exercise durations promoted the bone maturation with a final Young's modulus of 1.9 ± 0.3 GPa. The present study connects clinical rehabilitation and fundamental research, and is helpful to understand the bone repair process and further design bone scaffold for bone tissue engineering

Microstructure and biomechanical characteristics of bone substitutes for trauma and orthopaedic surgery

Abstract. BACKGROUND: Many (artificial) bone substitute materials are currently available for use in orthopaedic trauma surgery. Objective data on their biological and biomechanical characteristics, which determine their clinical application, is mostly lacking. The aim of this study was to investigate structural and in vitro mechanical properties of nine bone substitute cements registered for use in orthopaedic trauma surgery in the Netherlands. METHODS: Seven calcium phosphate cements (BoneSource®, Calcibon®, ChronOS®, Eurobone®, HydroSet™, Norian SRS®, and Ostim®), one calcium sulphate cement (MIIG® X3), and one bioactive glass cement (Cortoss®) were tested. Structural characteristics were measured by micro-CT scanning. Compression strength and stiffness were determined following unconfined compression tests. RESULTS: Each bone substitute had unique characteristics. Mean total porosity ranged from 53% (Ostim®) to 0.5% (Norian SRS®). Mean pore size exceeded 100 μm only in Eurobone® and Cortoss® (162.2 ± 107.1 μm and 148.4 ± 70.6 μm, respectively). However, 230 μm pores were found in Calcibon®, Norian SRS®, HydroSet™, and MIIG® X3. Connectivity density ranged from 27/cm3 for HydroSet™ to 0.03/cm3 for Calcibon®. The ultimate compression strength was highest in Cortoss® (47.32 MPa) and lowest in Ostim® (0.24 MPa). Young's Modulus was highest in Calcibon® (790 MPa) and lowest in Ostim® (6 MPa). CONCLUSIONS: The bone substitutes tested display a wide range in structural properties and compression strength, indicating that they will be suitable for different clinical indications. The data outlined here will help surgeons to select the most suitable products currently available for specific clinical indications

Tissue responses to molecularly reinforced polylactide-co-glycolide implants

Plates for internal fixation fabricated from biodegradable polymers degrade via an autocatalytic route. When they are used in bone implants of significant size and thickness, hollowing of the implant may occur while the overall dimensions appear unchanged. We hypothesized that incorporation of a cross-linked polypropylene fumarate matrix into polylactide-co-glycolide bone plates may provide an internal molecular network which prevents implant collapse. Cross-linking reagents of varying hydrophilicity including N-vinylpyrrolidone (VP), hydroxyethylmethacrylate (HEMA), and ethyleneglycol dimethacrylate (EGDMA) were employed. With the objective of determining the most biocompatible and structurally sound composition for molecular reinforcement, we investigated tissue responses in both subcutaneous and orthotopic rodent implantation models in relation to maintenance of implant integrity by histologic, histomorphometric, and stereomicroscopic analysis. Results showed that tissue responses were correlated with dimensional stability of the implants. The most favorable results were seen with the hydrophobic cross-linker EGDMA; this may have been related to the initial reduction of the water uptake by the implant. Cross-linking of polypropylene fumarate with EGDMA within a polylactide-co-glycolide bone plate may offer a means to maintain excellent biocompatibility while improving dimensional stability of biodegradable bone plates