86 research outputs found
Crystallization and preliminary crystallographic analysis of dUTPase from the helper phage Φ11 of Staphylococcus aureus
Staphylococcus aureus superantigen-carrying pathogenicity islands (SaPIs) have a
determinant role in spreading virulence genes among bacterial populations that constitute a
major health hazard. Repressor (Stl) proteins are responsible for transcriptional regulation of
pathogenicity island genes. Recently, a derepressing interaction between the repressor Stl
SaPIbov1 with dUTPase from the Φ11 helper phage was suggested [Tormo-Mas et al. (2010).
Nature 465, 779-782]. Towards elucidating the molecular mechanism of this interaction, this
study reports expression, purification, and X-ray analysis of Φ11 dUTPase that contains a
phage-specific polypeptide segment not present in other dUTPases. Crystals were obtained
using the hanging-drop vapor-diffusion method at room temperature. Data were collected
from one type of crystal to 2.98 Å resolution. The crystal of Φ11 dUTPase belonged to the
cubic space group I23, with unit-cell parameters a=98.16 Å, α=β=γ= 90.00o
The electrical conductivity of living tissue: A parameter in the bioelectrical inverse problem
Tetoválótűhegyek károsodásának vizsgálata
A tetoválás napjainkban egyre elfogadottabbá válik a társadalom különböző szintjein, ennek egyik elősegítője az, hogy a testdíszítésen túl a kozmetikaipar is egyre szélesebb körben használja pl. sminktetoválások vagy bőrhibák, műtéti hegek elfedésére. A tetoválótűk, annak ellenére, hogy az emberi szövetekkel és akár vérrel is közvetlen kontaktusba kerülnek, nem esnek az orvostechnikai eszköz rendelet hatása alá, így a forgalomba hozatalukhoz nem szükséges számos anyagvizsgálati és biokompatibilitási teszt elvégzése. Kutatásunk fókuszában az állt, hogy a tetoválás során miképp károsodik a tű, valamint a tűket összefogó forrasztás, hogyan alakul ez az idő előrehaladtával, ugyanis a kopott tűvég nemcsak a tetoválás minőségét ronthatja el, hanem fokozhatja a bőr roncsolódását és növekedhet a bőrbe jutó allergén anyagok mennyisége is
Damage Analysis of Tattoo Needle Tips
Tattooing is becoming more and more accepted at different levels of society today. A contributor to this is that besides body decoration, the cosmetics industry is increasingly using it for make-up tattoos and to hide skin imperfections and surgical scars. Tattoo needles, despite being in direct contact with human tissues and even with blood, are not subject to current Medical Device Regulation, so they do not require a number of material and biocompatibility tests in order to be placed on the market. The focus of our research was on how the needle and the soldering of the needles are damaged during tattooing, and how this develops over time, as a worn needle tip can not only degrade the quality of the tattoo, but also increase skin breakdown and the amount of dissolving allergenic substances
Investigation of Bimodal Aluminium Matrix Syntactic Foams Filled with Ceramic Hollow Spheres
In this study bimodal A413 matrix syntactic foams filled with ceramic hollow spheres (CHSs) were produced and examined by computer tomography (CT) and quasi-static mechanical testing to determine the mixing properties of the hollow spheres and the strength of the metal foam. Two hollow spheres of different nominal diameters (d1 = 2.4 mm and d2 = 7.0 mm) were used in equal volume ratio. The produced metal foams have a density of 1.61±0.03 g/cm3, with smaller inclusions and some defective hollow spheres in the structure. The foams have an average compressive strength of 120 MPa and a specific mechanical energy absorbing capacity of 43.5 J/cm3. As a result of the upsetting tests, the matrix material is separated from the CHSs, breaking the connection between them
Edzett üveg dinamikus és nagy hőmérsékletű, kvázistatikus vizsgálata
A mindennapokban használt üvegek törése sok esetben okoz károkat és sérüléseket, mivel nehezen megbecsülhető eltérő körülmények között a törési tulajdonsága és a károsodás végbemenetele. Ennek közelebbi megismerése céljából kutatásunk során edzett üveg tulajdonságait vizsgáltuk. Az üveg próbatestek kétféle roncsolásos anyagvizsgálaton estek át: szobahőmérsékleten és nagy hőmérsékleten végzett hárompontos hajlításnak és szobahőmérsékletű dinamikus vizsgálatnak, melyben nagy sebességű acélgolyó becsapódásának tettük ki a mintákat. Megállapítottuk, hogy nagy hőmérsékleten végzett terhelés hatására a próbatesteknek a hőmérséklet növelésével arányosan egyre élesebb a töretfelületük, illetve dinamikus behatás következtében körkörös repedésterjedéssel kagylós jellegű töretkép keletkezik, amely megakadályozza a radiális repedések terjedését, így csak kis területen megy végbe károsodás
Structural and Mechanical Investigation of Class I Biomimetic Composite Dental Filling by X-ray Computed Tomography, Scanning Electron Microscopy, and Microtensile Bond Strength Testing
Nowadays, short fiber-reinforced composites are broadly used in modern restorative dentistry. The tensile strength, Young's modulus, density, and polymerization shrinkage of these materials are developed to mimic the original teeth tissue best. The shrinkage, however, will occur during any polymerization process, which can cause residual stress and gap formation between the tooth and the filling. These can lead to the propagation of cracks, reduction in the adhesive bond strength, or even cause separation in the restoration. During this research, a biomimetic dental restoration was created on a surgically removed third molar with EverX short-fiber reinforced dental composite by bulk-filling technique. The restored tooth sample was examined by X-ray computed tomography to obtain a 3D image of the whole restoration. The volume of the used adhesive, the material discontinuities, and internal cavities were determined. A cut-out slice was further investigated by scanning electron microscopy to examine the adhesive layer thickness, the gap formation, and the quality of the filling. Finally, microtensile specimens were machined to evaluate the bond strength between the tooth dentin and the filling material
- …