Tribological performance and corrosion behavior of CoCrMo alloy

The present work focuses on the Tribological properties and corrosion behavior evaluation of sintered CoCrMo alloy. The CoCrMo alloy was elaborated by Powder metallurgy process at various sintering temperatures (1200°C, 1250°C and 1300°C). The structural properties were characterized by X-ray diffraction and scanning electron microscopy. The tribological characteristics were measured using a dry disc-ball tribometer. The corrosion behavior of the samples was studied using different electrochemical tests in a simulated physiological environment (Hank’s solution). The obtained results show that higher sintering temperatures have a positive impact on the tribological behavior as well as the corrosion resistance of CoCrMo alloys. The sintered samples at 1300°C showed a better resistance to friction wear and a lower corrosion rate

Performances tribologique et électrochimique de l’alliage TiNi poreux

Ce travail vise l’étude de l’effet de la porosité sur le comportement tribologique et électrochimique de l’alliage TiNi poreux pour des applications biomédicales. L’alliage TiNi poreux a été élaboré par le procédé de frittage en phase solide à la température de 850°C. En effet, l’analyse microstructurale par MEB et EDS confirme bien que lorsque la pression de compactage varie il se produit un changement de la morphologie des pores et des fractions des phases formées. L’étude du glissement à sec de notre matériau a permis de mettre en évidence que la présence de la porosité interconnectée améliore leur comportement tribologique. Cependant l’étude électrochimique a révélé que quelque soit le taux de porosité les échantillons présentent un caractère passif. Les paramètres électrochimiques dépendent dans une large mesure du pourcentage de pore, leur morphologie et leur distribution.Mots-clés: biomatériaux, porosité, tribologie, résistance à la corrosion, impédanceEnglish Title: Tribological and electrochemical performances of porous TiNi alloyEnglish AbstractThis work aims to study the effect of porosity on the tribological and electrochemical behavior of the porous TiNi alloy for biomedical applications. The porous TiNi alloy was developed by the solid phase sintering process at the temperature of 850°C. Indeed, the microstructural analysis by SEM and EDS confirms that when the compaction pressure varies there is a change in the morphology of the pores and fractions of the phases formed. The study of the dry sliding of our material made it possible to highlight that the presence of the interconnected porosity improves their tribological behavior. However, the electrochemical study revealed that whatever the porosity rate, the samples have a passive character. The electrochemical parameters depend to a large extent on the percentage of pore, their morphology and their distribution.Keywords: biomaterials, porosity, tribology, corrosion resistance, impedanc

Effet de la température de frittage sur le comportement mécanique et tribologique de l’alliage TiNi poreux

Le frittage en phase solide des poudres élémentaires de titane et de nickel a été utilisé pour élaborer l’alliage TiNi poreux. Dans ce travail, on a étudié l’effet de la température de frittage sur les comportements mécanique, tribologique et électrochimique de cet alliage. L’analyse par la diffraction des rayons X, la microscopie électronique à balayage (MEB) et l’analyse EDS révèlent la formation de la phase TiNi majoritaire pour tous les échantillons frittés aux différentes températures. L’échantillon fritté à 950 °C présente une dureté élevée, un module d’Young et un taux d’usure plus faibles que celui fritté à 850 °C. Les techniques : polarisation à circuit ouvert, potentiodynamique, et spectroscopie d’impédance électrochimique ont été utilisées pour vérifier l’influence de la température de frittage sur les paramètres électrochimiques de l’alliage dans des conditions physiologiques reproduisant celles rencontrées dans le corps humain (phosphate buffered saline solution). Les résultats des investigations montrent que l’alliage TiNi poreux présente un caractère passif et la cinétique de corrosion dépend dans une large mesure de la porosité ainsi que de la température de frittage