Intrinsic Josephson Effects in the Magnetic Superconductor RuSr2GdCu2O8

We have measured interlayer current transport in small sized RuSr2GdCu2O8 single crystals. We find a clear intrinsic Josephson effect showing that the material acts as a natural superconductor-insulator-ferromagnet-insulator-superconductor superlattice. So far, we detected no unconventional behavior due to the magnetism of the RuO2 layers.Comment: 4 pages, 5 figures, to appear in Phys. Rev. Let

Synthesis effects on the magnetic and superconducting properties of RuSr2GdCu2O8

A systematic study on the synthesis of the Ru-1212 compound by preparing a series of samples that were annealed at increasing temperatures and then quenched has been performed. It results that the optimal temperature for the annealing lies around 1060-1065 C; a further temperature increase worsens the phase formation. Structural order is very important and the subsequent grinding and annealing improves it. Even if from the structural point of view the samples appear substantially similar, the physical characterization highlight great differences both in the electrical and magnetic properties related to intrinsic properties of the phase as well as to the connection between the grains as inferred from the resistive and the Curie Weiss behaviour at high temperature as well as in the visibility of ZFC anf FC magnetic signals.Comment: 17 pages, 12 figures. Proc. Int. Workshop " Ruthenate and rutheno-cuprate materials: theory and experiments", Vietri, October 2001. To be published on LNP Series, Springer Verlag, Berlin, C. Noce, A. Vecchione, M. Cuoco, A. Romano Eds, 200

Decoupling of superconducting layers in magnetic superconductor RuSr_{2}GdCu_{2}O_{8}

We propose the model for magnetic properties of the magnetic superconductor RuSr$_{2}$GdCu$_{2}$O$_{8}$, which incorporates the theory of the superconducting/ferromagnetic multilayers. The transition line $T_{d}(h)$, on which the Josephson coupled superconducting planes are decoupled, i.e. $j_{c}(T_{d})=0$, is calculated as a function of the exchange energy $h$. As the result of this decoupling a nonmonotonic behavior of magnetic properties, like the lower critical field $H_{c1}$, Josephson plasma frequency, etc. is realized near (or by crossing) the $T_{d}(h)$ line. The obtained results are used in analyzing the newly discovered antiferromagnetic ruthenocuprate RuSr$_{2}$GdCu$_{2}$O$_{8}$ with possible weak ferromagnetic order in the RuO planes.Comment: 12 pages, 3 figs embede

A Transport and Microwave Study of Superconducting and Magnetic RuSr2EuCu2O8

We have performed susceptibility, thermopower, dc resistance and microwave measurements on RuSr2EuCu2O8. This compound has recently been shown to display the coexistence of both superconducting and magnetic order. We find clear evidence of changes in the dc and microwave resistance near the magnetic ordering temperature (132 K). The intergranular effects were separated from the intragranular effects by performing microwave measurements on a sintered ceramic sample as well as on a powder sample dispersed in an epoxy resin. We show that the data can be interpreted in terms of the normal-state resistivity being dominated by the CuO2 layers with exchange coupling to the Ru moments in the RuO2 layers. Furthermore, most of the normal-state semiconductor-like upturn in the microwave resistance is found to arise from intergranular transport. The data in the superconducting state can be consistently interpreted in terms of intergranular weak-links and an intragranular spontaneous vortex phase due to the ferromagnetic component of the magnetization arising from the RuO2 planes.Comment: 20 pages including 6 figures in pdf format. To be published in Phys. Rev.

Metal-to-insulator transition and magnetic ordering in CaRu_{1-x}Cu_xO_3

CaRuO_3 is perovskite with an orthorhombic distortion and is believed to be close to magnetic ordering. Magnetic studies of single crystal and polycrystalline CaRu_{1-x}Cu_xO_3 (0\le x \le 15 at.%Cu) reveal that spin-glass-like transition develops for x\le 7 at.%Cu and obtained value for effective magnetic moment p_{eff}=3.55 mu_B for x=5 at.% Cu, single crystal, indicates presence of Ru^{5+}. At higher Cu concentrations more complex magnetic behaviors are observed. Electrical resistivity measured on polycrystalline samples shows metal-to-insulator transition (MIT) at 51 K for only 2 at.% Cu. Charge compensation, which is assumed to be present upon Cu^{2+/3+} substitution, induces appearance of Ru^{5+} and/or creation of oxygen vacancies in crystal structure. Since the observed changes in physical properties are completely attributable to the charge compensation, they cannot be related to behaviors of pure compound where no such mechanism is present. This study provides the criterion for "good" chemical probes for studying Ru-based perovskites.Comment: 12 pages, 7 figure

Superconducting properties of RuSr2GdCu2O8 studied by SQUID magnetometry

For polycrystalline RuSr2GdCu2O8 (Ru-1212), distinct peaks have been reported in d.c. magnetization in the superconducting state of the sample. Sr2GdRuO6 (Sr-2116), the precursor for the preparation of Ru-1212, shows similar peaks in the same temperature regime. Based on measurements performed on both bulk and powdered samples of Ru-1212 and Sr-2116, we exclude the possibility, that the observed behavior of the magnetization of Ru-1212 is due to Sr-2116 impurities. The effect is related to the superconductivity of Ru-1212, but it is not an intrinsic property of this compound. We provide evidence that the observation of magnetization peaks in the superconducting state of Ru-1212 is due to flux motion generated by the movement of the sample in an inhomogeneous field, during the measurement in the SQUID magnetometer. We propose several tests, that help to decide, whether the features observed in a SQUID magnetization measurement of Ru-1212 represent a property of the compound or not.Comment: 22 pages, 9 figure

Evidence for Possible Phase-Separations in RuSr2(Gd,Ce)2Cu2O10-delta

An unusual thermal-magnetic hysteresis was observed between a minor magnetic transition around 120 K and the main one at 80 K in superconducting RuSr2(R,Ce)2Cu2O10-delta (Ru1222R) samples, where R = Gd or Eu, down to a submicron length-scale. The observation suggests a possible phase-separation and is consistent with the very small but universal demagnetizing factor observed, which is difficult to reconcile with the canted spin-structure previously proposed. In such a scenario, the unusual superconducting properties of the Ru-based cuprates can also be understood naturally.Comment: 8 pages, 3 figures, submitted to Phys. Rev. B, "Rapid Communications" (September 26, 2001

Decoupled CuO_2 and RuO_2 layers in superconducting and magnetically ordered RuSr_2GdCu_2O_8

Comprehensive measurements of dc and ac susceptibility, dc resistance, magnetoresistance, Hall resistivity, and microwave absorption and dispersion in fields up to 8 T have been carried out on RuSr_2GdCu_2O_8 with the aim to establish the properties of RuO_2 and CuO_2 planes. At ~130 K, where the magnetic order develops in the RuO_2 planes, one observes a change in the slope of dc resistance, change in the sign of magnetoresistance, and the appearance of an extraordinary Hall effect. These features indicate that the RuO_2 planes are conducting. A detailed analysis of the ac susceptibility and microwave data on both, ceramic and powder samples show that the penetration depth remains frequency dependent and larger than the London penetration depth even at low temperatures. We conclude that the conductivity in the RuO_2 planes remains normal even when superconducting order is developed in the CuO_2 planes below \~45 K. Thus, experimental evidence is provided in support of theoretical models which base the coexistence of superconductivity and magnetic order on decoupled CuO_2 and RuO_2 planes.Comment: 11 pages, 11 figures, submitted to PR

Josephson Plasma in RuSr2GdCu2O8

Josephson plasma in RuSr$_{2}$GdCu$_{2}$O$_{8}$, Ru$_{1-x}$Sr$_{2}$GdCu$_{2+x}$O$_{8}$ (x = 0.3), and RuSr$_{2}$Eu$_{2-x}$Ce$_{x}$Cu$_{2}$O$_{10}$ (x = 0.5) compounds is investigated by the sphere resonance method. The Josephson plasma is observed in a low-frequency region (around 8.5 cm$^{-1}$ at T $\ll$ $T_{c}$) for ferromagnetic RuSr$_{2}$GdCu$_{2}$O$_{8}$, while it increases to 35 cm$^{-1}$ for non-ferromagnetic Ru$_{1-x}$Sr$_{2}$GdCu$_{2+x}$O$_{8}$ (x = 0.3), which represents a large reduction in the Josephson coupling at ferromagnetic RuO$_{2}$ block layers. The temperature dependence of the plasma does not shift to zero frequency ({\it i.e.} $j_{c}$ = 0) at low temperatures, indicating that there is no transition from the 0-phase to the $\pi$-phase in these compounds. The temperature dependence and the oscillator strength of the peak are different from those of other non-magnetic cuprates, and the origins of these anomalies are discussed.Comment: to appear in Phys. Rev.B Rapid Com

Study of the crystal structure, superconducting and magnetic properties of Ru1-xFexSr2GdCu2O8

Samples of the Ru1-xFexSr2GdCu2O8 system with x = 0, 0.025, 0.05, 0.075, 0.1 and 0.2, were prepared and their structural, superconducting and magnetic properties were studied. Rietveld refinement of the X-ray diffraction patterns show that the Fe substitution occurs in both Ru and Cu sites. An increase of Fe concentration produces no significant changes in the bond angle Ru-O(3)-Ru, which is a measure of the rotation of the RuO6 octahedra around the c-axis, and also in the bond angle Ru-O(1)-Cu, which is a measure of the canting of the RuO6 octahedra. On the other hand, the bond angle Cu-O(2)-Cu, which is a measure of the buckling of the CuO2 layer, has a slight tendency to decrease with the increase of the Fe content. We found thet both ferromagnetic and superconducting transition temperatures are reduced with the increase of Fe concentration. Analisys related to the decay of the superconducting and ferromagnetic states is presented.Comment: 9 pages, 7 figure