Modification of multi-profile surfaces by compression plasma flows action of quasistationary high-current plasma accelerator

The results of investigations into the action of compression plasma flows generated by the gas-discharge twostage quasistationary high-current plasma accelerator (QHPA) on multi-profile details are presented. Efficiency of the QHPA application to hardening treatment of samples from low- and medium-carbon steels with sufficient for practical purposes depth and microhardness of modified surface layer is shown

Modification of coating-substrate systems under the action of compression plasma flow

The results of studying changes in physical and mechanical properties of coating-substrate systems subjected to the compression plasma flow are presented. The possibility for doping the substrate both with pre-deposited coating components and with plasma-forming substance during liquid-phase mixing and resolidification of near-surface layers melted by the compression plasma flow is shown.Представлено результати досліджень зміни фізико-механічних властивостей систем покриття-підкладка при впливі на них компресійним плазмовим потоком. Продемонстровано можливість легування матеріалу підкладки як компонентом попередньо нанесеного покриття, так і робочою речовиною плазми, у процесі рідкофазного перемішування і перезатвердіння розплавлених під дією компресійного плазмового потоку приповерхніх шарів.Представлены результаты исследований изменения физико-механических свойств систем покрытие- подложка при воздействии на них компрессионным плазменным потоком. Продемонстрирована возможность легирования материала подложки как компонентом предварительно нанесенного покрытия, так и рабочим веществом плазмы, в процессе жидкофазного перемешивания и перезатвердевания расплавленных под действием компрессионного плазменного потока приповерхностных слоев

Nanostructured formations and coatings created on the surface of materials exposed to compression plasma flows

The paper presents the results of investigations on changing silicon and aluminium morphology under the action of compression plasma flows generated by the quasi-stationary plasma accelerator (magnetoplasma compressor type). The feasibility of spraying nanostructured metal films by compression flows was demonstrated. The resulting single-layer coating consists of spherical particles measuring 50 to 200 nm. Such particles bonded to each other cover a surface relief including flat areas and regular structures developing during plasma action. The state and composition of a sample surface were studied by SEM- and EXD-methodsПредставлено результати досліджень зміни морфології поверхні пластин кремнію й алюмінію при впливі на них компресійними плазмовими потоками, що генеруються квазістаціонарним плазмовим прискорювачем типу магнітоплазмовий компресор. Продемонстровано можливість нанесення на підкладки наноструктурних металевих покрить за допомогою компресійних потоків.Представлены результаты исследований изменения морфологии поверхности пластин кремния и алюминия при воздействии на них компрессионными плазменными потоками, генерируемыми квазистационарным плазменным ускорителем типа магнитоплазменный компрессор. Продемонстрирована возможность нанесения на подложки наноструктурных металлических покрытий с помощью компрессионных потоков