26 research outputs found
Stress corrosion cracking in Al-Zn-Mg-Cu aluminum alloys in saline environments
Copyright 2013 ASM International. This paper was published in Metallurgical and Materials Transactions A, 44A(3), 1230 - 1253, and is made
available as an electronic reprint with the permission of ASM International. One print or electronic copy may
be made for personal use only. Systematic or multiple reproduction, distribution to multiple locations via
electronic or other means, duplications of any material in this paper for a fee or for commercial purposes, or
modification of the content of this paper are prohibited.Stress corrosion cracking of Al-Zn-Mg-Cu (AA7xxx) aluminum alloys exposed to saline environments at temperatures ranging from 293 K to 353 K (20 °C to 80 °C) has been reviewed with particular attention to the influences of alloy composition and temper, and bulk and local environmental conditions. Stress corrosion crack (SCC) growth rates at room temperature for peak- and over-aged tempers in saline environments are minimized for Al-Zn-Mg-Cu alloys containing less than ~8 wt pct Zn when Zn/Mg ratios are ranging from 2 to 3, excess magnesium levels are less than 1 wt pct, and copper content is either less than ~0.2 wt pct or ranging from 1.3 to 2 wt pct. A minimum chloride ion concentration of ~0.01 M is required for crack growth rates to exceed those in distilled water, which insures that the local solution pH in crack-tip regions can be maintained at less than 4. Crack growth rates in saline solution without other additions gradually increase with bulk chloride ion concentrations up to around 0.6 M NaCl, whereas in solutions with sufficiently low dichromate (or chromate), inhibitor additions are insensitive to the bulk chloride concentration and are typically at least double those observed without the additions. DCB specimens, fatigue pre-cracked in air before immersion in a saline environment, show an initial period with no detectible crack growth, followed by crack growth at the distilled water rate, and then transition to a higher crack growth rate typical of region 2 crack growth in the saline environment. Time spent in each stage depends on the type of pre-crack (“pop-in” vs fatigue), applied stress intensity factor, alloy chemistry, bulk environment, and, if applied, the external polarization. Apparent activation energies (E a) for SCC growth in Al-Zn-Mg-Cu alloys exposed to 0.6 M NaCl over the temperatures ranging from 293 K to 353 K (20 °C to 80 °C) for under-, peak-, and over-aged low-copper-containing alloys (~0.8 wt pct), they are typically ranging from 20 to 40 kJ/mol for under- and peak-aged alloys, and based on limited data, around 85 kJ/mol for over-aged tempers. This means that crack propagation in saline environments is most likely to occur by a hydrogen-related process for low-copper-containing Al-Zn-Mg-Cu alloys in under-, peak- and over-aged tempers, and for high-copper alloys in under- and peak-aged tempers. For over-aged high-copper-containing alloys, cracking is most probably under anodic dissolution control. Future stress corrosion studies should focus on understanding the factors that control crack initiation, and insuring that the next generation of higher performance Al-Zn-Mg-Cu alloys has similar longer crack initiation times and crack propagation rates to those of the incumbent alloys in an over-aged condition where crack rates are less than 1 mm/month at a high stress intensity factor
In situ Evolution of Trivalent Chromium Process Passive Film on Al in a Corrosive Aqueous Environment
Thermodynamics of the Under-Potential Deposition of Hydrogen on Polycrystalline Platinum in Aqueous Trifluoromethanesulfonic Acid Solution
Adsorção de íons sulfato em ZrO2.nH2O preparado pelo método da precipitação convencional e da precipitação em solução homogênea Adsorption of sulfate ions in ZrO2.nH2O prepared by conventional precipitation and homogeneous solution methods
Este trabalho visa a preparação, caracterização e estudo da adsorção de íons sulfato em óxido de zircônio hidratado preparado pelos métodos da precipitação convencional e da precipitação em solução homogênea. Os materiais obtidos foram caracterizados por difração de raios X, análise termogravimétrica, microscopia eletrônica de varredura e análise de área superficial específica pelo método BET. Através da constante Q0, relacionada com a capacidade de adsorção máxima, observou-se que o ZrO2.nH2O/PSH possui maior capacidade de adsorção para íons sulfato que o ZrO2.nH2O/PC. Pelos resultados de ΔG, observou-se que os íons sulfato foram adsorvidos através de reações energeticamente favoráveis para toda a faixa de concentração estudada.<br>This work reports the preparation, characterization and adsorption study of sulfate on hydrous zirconium oxides prepared by conventional and homogeneous solution precipitation methods. The materials prepared were characterized by X-ray diffraction, thermogravimetric analysis, scanning electron microscopy and surface area measurements. Through the Q0 constant, related with the capacity of maximum adsorption, it was observed that the ZrO2.nH2O/PSH presented better adsorption capacity than ZrO2.nH2O/PC. By results of ΔG, it was observed that sulfate ions had been adsorbed through favorable reactions for all studied concentration ranges