Mimotope ELISA for Detection of Broad Spectrum Antibody against Avian H5N1 Influenza Virus

Science and Technology Foundation of Fujian Province [2009YZ0002]; National Natural Science Foundation of China [30901077]; National High Technology Research and Development Program [2010AA022801]Background: We have raised a panel of broad spectrum neutralizing monoclonal antibodies against the highly pathogenic H5N1 avian influenza virus, which neutralize the infectivity of, and afford protection against infection by, most of the major genetic groups of the virus evolved since 1997. Peptide mimics reactive with one of these broad spectrum H5N1 neutralizing antibodies, 8H5, were identified from random phage display libraries. Method: The amino acid residues of the most reactive 12mer peptide, p125 (DTPLTTAALRLV), were randomly substituted to improve its mimicry of the natural 8H5 epitope. Result: 133 reactive peptides with unique amino acid sequences were identified from 5 sub-libraries of p125. Four residues (2,4,5.9) of the parental peptide were preserved among all the derived peptides and probably essential for 8H5 binding. These are interspersed among four other residues (1,3,8,10), which exhibit restricted substitution and probably could contribute to binding, and another four (6,7,11,12) which could be randomly substituted and probably are not essential for binding. One peptide, V-1b, derived by substituting 5 of the latter residues is the most reactive and has a binding constant of 3.16x10(-9) M, which is 38 fold higher than the affinity of the parental p125. Immunoassay produced with this peptide is specifically reactive with 8H5 but not also the other related broad spectrum H5N1 avian influenza virus neutralizing antibodies. Serum samples from 29 chickens infected with H5N1 avian influenza virus gave a positive result by this assay and those from 12 uninfected animals gave a negative test result. Conclusion: The immunoassay produced with the 12 mer peptide, V1-b, is specific for the natural 8H5 epitope and can be used for detection of antibody against the broad spectrum neutralization site of H5N1 avian influenza virus

Performance of Detecting IgM Antibodies against Enterovirus 71 for Early Diagnosis

Enterovirus 71 (EV71) infection is more likely to induce severe complications and mortality than other enteroviruses. Methods for detection of IgM antibody against EV71 had been established for years, however, the performance of the methods in the very early diagnosis of EV71 infection had not been fully evaluated, which is especially meaningful because of the short incubation period of EV71 infection. In this report, the performance of an IgM anti-EV71 assay was evaluated using acute sera collected from 165 EV71 infected patients, 165 patients infected with other enteroviruses, and more than 2,000 sera from healthy children or children with other infected diseases. The results showed a 90% sensitivity in 20 patients who were in their first illness day, and similar sensitivity remained till 4 days after onset. After then the sensitivity increased to 95% to 100% for more than one month. The specificity of the assay in non-HFMD children is 99.1% (95% CI: 98.6–99.4), similar as the 99.9% specificity in healthy adults. The cross-reaction rate in patients infected with other non-EV71 enteroviruses was 11.4%. In conclusion, the data here presented show that the detection of IgM anti-EV71 by ELISA affords a reliable, convenient, and prompt diagnosis of EV71 infection

Quantifying the Evolution of Vascular Barrier Disruption in Advanced Atherosclerosis with Semipermeant Nanoparticle Contrast Agents

Acute atherothrombotic occlusion in heart attack and stroke implies disruption of the vascular endothelial barrier that exposes a highly procoagulant intimal milieu. However, the evolution, severity, and pathophysiological consequences of vascular barrier damage in atherosclerotic plaque remain unknown, in part because quantifiable methods and experimental models are lacking for its in vivo assessment.To develop quantitative nondestructive methodologies and models for detecting vascular barrier disruption in advanced plaques.Sustained hypercholesterolemia in New Zealand White (NZW) rabbits for >7-14 months engendered endothelial barrier disruption that was evident from massive and rapid passive penetration and intimal trapping of perfluorocarbon-core nanoparticles (PFC-NP: ∼250 nm diameter) after in vivo circulation for as little as 1 hour. Only older plaques (>7 mo), but not younger plaques (<3 mo) demonstrated the marked enhancement of endothelial permeability to these particles. Electron microscopy revealed a complex of subintimal spongiform channels associated with endothelial apoptosis, superficial erosions, and surface-penetrating cholesterol crystals. Fluorine ((19)F) magnetic resonance imaging and spectroscopy (MRI/MRS) enabled absolute quantification (in nanoMolar) of the passive permeation of PFC-NP into the disrupted vascular lesions by sensing the unique spectral signatures from the fluorine core of plaque-bound PFC-NP.The application of semipermeant nanoparticles reveals the presence of profound barrier disruption in later stage plaques and focuses attention on the disrupted endothelium as a potential contributor to plaque vulnerability. The response to sustained high cholesterol levels yields a progressive deterioration of the vascular barrier that can be quantified with fluorine MRI/MRS of passively permeable nanostructures. The possibility of plaque classification based on the metric of endothelial permeability to nanoparticles is suggested

Effect of niobium and titanium addition on the hot ductility of boron containing steel

Hot ductility of boron containing steel (B steel) with adding Nb (0.03 wt.%) (B-Nb steel) and B-Nb steel with adding Ti (0.0079 wt.%) (B-Nb-Ti steel) was quantified using hot tensile tests. The specimens were solution-treated at 1350 degrees C and cooled at 20 degrees C s(-1) to tensile test temperature (T) in the range of 750 <= T <= 1050 degrees C. After that, they were strained to failure at a strain rate of 2.5 x 10(-3) s(-1). For the B-Nb steel, severe hot ductility loss was observed at 850 <= T <= 950 degrees C, which covered the low temperature in which austenite (gamma) single-phase exists, and the high temperature at which gamma and ferrite (alpha) coexist. Ductility loss in the B-Nb steel was caused by the presence of a network of BN precipitates, rather than by Nb(C, N) precipitates at the gamma grain boundaries. In contrast, hot ductility of the B-Nb-Ti steel was remarkably improved at 850 <= T <= 950 degrees C. In the B-Nb-Ti steel, BN precipitates preferentially on TiN particles, resulting in increased BN precipitation in the gamma grain interior and a decrease in the network of BN precipitates at the gamma grain boundaries. These changes reduce strain localization at the gamma grain boundaries and therefore increase the hot ductility of the steel. (C) 2011 Elsevier B.V. All rights reserved.X112535sciescopu

Cooling Rate Dependence of Boron Distribution in Low Carbon Steel

The behavior of boron (B) segregation to austenite grain boundaries in low carbon steel was studied using particle tracking autoradiography (PTA) and secondary ion mass spectroscopy (SIMS). An effective time method was used to compare the cooling rate (CR) dependence of this segregation during continuous cooling and its time dependence during isothermal holding. Comparison of these segregation behaviors has confirmed that the CR dependence of B segregation agrees well with its time dependence and is mainly a result of the phenomenon of nonequilibrium segregation. Based on the CR dependence of B segregation, the continuous cooling transformation behavior of B-bearing steel as compared with B-free steel was also investigated using dilatometry and microstructural observations. The addition of a small amount of B to low carbon steel retarded significantly the austenite-to-ferrite transformation and finally expanded the range of cooling programs that result in the formation of bainitic microstructures. Analysis of the B distribution has confirmed that this retardation effect of B on ferrite transformation is attributed to the CR dependence of B segregation to austenite grain boundaries during cooling after austenitization.open111115sciescopu

Facile Synthesis of Nb2O5@Carbon Core-Shell Nanocrystals with Controlled Crystalline Structure for High-Power Anodes in Hybrid Supercapacitors.

Hybrid supercapacitors (battery-supercapacitor hybrid devices, HSCs) deliver high energy within seconds (excellent rate capability) with stable cyclability. One of the key limitations in developing high-performance HSCs is imbalance in power capability between the sluggish Faradaic lithium-intercalation anode and rapid non-Faradaic capacitive cathode. To solve this problem, we synthesize Nb2O5@carbon core-shell nanocyrstals (Nb2O5@C NCs) as high-power anode materials with controlled crystalline phases (orthorhombic (T) and pseudohexagonal (TT)) via a facile one-pot synthesis method based on a water-in-oil microemulsion system. The synthesis of ideal T-Nb2O5 for fast Li(+) diffusion is simply achieved by controlling the microemulsion parameter (e.g., pH control). The T-Nb2O5@C NCs shows a reversible specific capacity of ∼180 mA h g(-1) at 0.05 A g(-1) (1.1-3.0 V vs Li/Li(+)) with rapid rate capability compared to that of TT-Nb2O5@C and carbon shell-free Nb2O5 NCs, mainly due to synergistic effects of (i) the structural merit of T-Nb2O5 and (ii) the conductive carbon shell for high electron mobility. The highest energy (∼63 W h kg(-1)) and power (16 528 W kg(-1) achieved at ∼5 W h kg(-1)) densities within the voltage range of 1.0-3.5 V of the HSC using T-Nb2O5@C anode and MSP-20 cathode are remarkable