Aqueous Solution Preparation, Structure, and Magnetic Properties of Nano-Granular ZnxFe3−xO4 Ferrite Films

This paper reports a simple and novel process for preparing nano-granular ZnxFe3−xO4 ferrite films (0 ≤ x ≤ 0.99) on Ag-coated glass substrates in DMAB-Fe(NO3)3-Zn(NO3)2 solutions. The deposition process may be applied in preparing other cations-doped spinel ferrite films. The Zn content x in the ZnxFe3−xO4 films depends linearly on the Zn2+ ion concentration ranging from 0.0 to 1.0 mM in the aqueous solutions. With x increasing from 0 to 0.99, the lattice constant increases from 0.8399 to 0.8464 nm; and the microstructure of the films changes from the non-uniform nano-granules to the fine and uniform nano-granules of 50–60 nm in size. The saturation magnetization of the films first increases from 75 emu/g to the maximum 108 emu/g with x increasing from 0 to 0.33 and then decreases monotonously to 5 emu/g with x increasing from 0.33 to 0.99. Meanwhile, the coercive force decreases monotonously from 116 to 13 Oe

Remarkable capacity retention of nanostructured manganese oxide upon cycling as an electrode material for supercapacitor

Electrochemical capacity retention of nearly X-ray amorphous nanostructured manganese oxide (nanoMnO2) synthesized by mixing directly KMnO4 with ethylene glycol under ambient conditions for supercapacitor studies is enhanced significantly. Although X-ray diffraction (XRD) pattern of nanoMnO2 shows poor crystallinity, it is found that by Mn K-edge X-ray absorption near edge structure (XANES) measurement that the nanoMnO2 obtained is locally arranged in a δ-MnO2-type layered structure composed of edge-shared network of MnO6 octahedra. Field emission scanning electron microscopy and XANES measurements show that nanoMnO2 contains nearly spherical shaped morphology with δ-MnO2 structure, and 1D nanorods of α-MnO2 type structure (powder XRD) in the annealed (600 °C) sample. Volumetric nitrogen adsorption−desorption isotherms, inductively coupled plasma analysis, and thermal analysis are carried out to obtain physicochemical properties such as surface area (230 m2 g−1), porosity of nanoMnO2 (secondary mesopores of diameter 14.5 nm), water content, composition, etc., which lead to the promising electrochemical properties as an electrode for supercapacitor. The nanoMnO2 shows a very high stability even after 1200 cycles with capacity retention of about 250 F g−1

MnOx/carbon nanotube/reduced graphene oxide nanohybrids as high-performance supercapacitor electrodes

Nanohybrids consisting of both carbon and pseudocapacitive metal oxides are promising as high-performance electrodes to meet the key energy and power requirements of supercapacitors. However, the development of high-performance nanohybrids with controllable size, density, composition and morphology remains a formidable challenge. Here, we present a simple and robust approach to integrating manganese oxide (MnOx) nanoparticles onto flexible graphite paper using an ultrathin carbon nanotube/reduced graphene oxide (CNT/RGO) supporting layer. Supercapacitor electrodes employing the MnOx/CNT/RGO nanohybrids without any conductive additives or binders yield a specific capacitance of 1070 F g−1 at 10 mV s−1, which is among the highest values reported for a range of hybrid structures and is close to the theoretical capacity of MnOx. Moreover, atmospheric-pressure plasmas are used to functionalize the CNT/RGO supporting layer to improve the adhesion of MnOx nanoparticles, which results in theimproved cycling stability of the nanohybrid electrodes. These results provide information for the utilization of nanohybrids and plasma-related effects to synergistically enhance the performance of supercapacitors and may create new opportunities in areas such as catalysts, photosynthesis and electrochemical sensors

Facile Route to an Efficient NiO Supercapacitor with a Three-Dimensional Nanonetwork Morphology

NiO nanostructures with three distinct morphologies were fabricated by a sol-gel method and their morphology-dependent supercapacitor properties were exploited. The nanoflower- shaped NiO with a distinctive three-dimensional (3D) network and the highest pore volume shows the best supercapacitor properties. The nanopores in flower-shaped nanostructures, offering advantages in contact with and transport of the electrolyte, allow for 3D nanochannels in NiO structure, providing longer electron pathways. The XPS and EIS data of the NiO nanostructure confirm that the flower-shaped NiO, which has the lowest surface area among the three morphologies, was effectively optimized as a superior electrode and yielded the greatest pseudocapacitance. This study indicates that forming a 3D nanonetwork is a straightforward means of improving the electrochemical properties of a supercapacitor.close503