    Semi-vitrified porous kyanite mullite ceramics: Young modulus, microstructure and pore size evolution

    Get PDF
    Microporous porcelain formulations are successfully carried out through sintering processing. During the thermal treatment of ceramic products, it was found that the addition of kyanite together with ϕ- and γ-Al2O3 allowed to enhance interconnected pores network with micrometric size from 0.1 to 9 µm in a semi-vitrified composite. Between 1200 and 1350 °C, the mullitization of kyanite hindered the extension of vitrification and the growth of acicular mullite from the transformation of metakaolin. The main pores size decreased from 4.33 to 1.54 µm for the formulation containing 32 wt% of kyanite. In this interval the specific pore area increased from 0.64 to 8.75 m2 g−1 due to the total conversion of the kyanite to fibrous and acicular mullite that reduced the voids provided by the earlier mullitization. The improvement in the mullitization without extensive vitrification and grain growth and the reduction of the pores size with the increase in the specific pore area contributed to the formation of a microporous matrix with the Young's modulus increased from 7 to > 20 GPa. The microstructure of the microporous porcelain, their specific pore area and pores size as well as the interconnection of pores was found innovative for the applications in the field of engineering filtration where high mechanical strength, strain, stiffness and pressure resistance are required
    corecore