Pentlandite rocks as sustainable and stable efficient electrocatalysts for hydrogen generation

The need for sustainable catalysts for an efficient hydrogen evolution reaction is of significant interest for modern society. Inspired by comparable structural properties of [FeNi]-hydrogenase, here we present the natural ore pentlandite (Fe4.5Ni4.5S8) as a direct ‘rock’ electrode material for hydrogen evolution under acidic conditions with an overpotential of 280 mV at 10 mA cm−2. Furthermore, it reaches a value as low as 190 mV after 96 h of electrolysis due to surface sulfur depletion, which may change the electronic structure of the catalytically active nickel–iron centres. The ‘rock’ material shows an unexpected catalytic activity with comparable overpotential and Tafel slope to some well-developed metallic or nanostructured catalysts. Notably, the ‘rock’ material offers high current densities (≤650 mA cm−2) without any loss in activity for approximately 170 h. The superior hydrogen evolution performance of pentlandites as ‘rock’ electrode labels this ore as a promising electrocatalyst for future hydrogen-based economy

Influence of the Fe:Ni Ratio and Reaction Temperature on the Efficiency of (Fe_xNi_1–x)₉S₈ Electrocatalysts Applied in the Hydrogen Evolution Reaction

Inspired by our recent finding that Fe4.5Ni4.5S8 rock is a highly active electrocatalyst for HER, we set out to explore the influence of the Fe:Ni ratio on the performance of the catalyst. We herein describe the synthesis of (FexNi1–x)9S8 (x = 0–1) along with a detailed elemental composition analysis. Furthermore, using linear sweep voltammetry, we show that the increase in the iron or nickel content, respectively, lowers the activity of the electrocatalyst toward HER. Electrochemical surface area analysis (ECSA) clearly indicates the highest amount of active sites for a Fe:Ni ratio of 1:1 on the electrode surface pointing at an altered surface composition of iron and nickel for the other materials. Specific metal–metal interactions seem to be of key importance for the high electrocatalytic HER activity, which is supported by DFT calculations of several surface structures using the surface energy as a descriptor of catalytic activity. In addition, we show that a temperature increase leads to a significant decrease of the overpotential and gain in HER activity. Thus, we showcase the necessity to investigate the material structure, composition and reaction conditions when evaluating electrocatalysts