62 research outputs found
Aluminum/zirconium alloys obtained by Al underpotential deposition onto Zr from low temperature AlCl3+NaCl molten salts
Contrary to the widely accepted hypothesis that it is not possible, aluminum underpotential deposition (UPD) onto zirconium from a low temperature (200, 250 and 300 Ā°C) equimolar chloroaluminate melt was recorded. Furthermore, it was shown that aluminum UPD facilitates alloy formation between the deposited aluminum monolayer and the zirconium substrate by interdiffusion. The aluminum/zirconium alloys formed at temperatures substantially lower than those needed for thermal preparation of the same alloys were Al3Zr2 and Al3Zr. The experimental techniques linear sweep voltammetry, potential step, scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction were used for the characterization of the obtained electrode surfaces
Aluminium electrodeposition onto glassy carbon from deep eutectic system made of AlCl3+urea
Electrochemical deposition of aluminium onto glassy carbon from deep eutectic solvent (DES), made
of the AlCl3+urea, at 25-50Ā°C have been investigated. The deposition was performed in potentiostatic
mode. The morphology of the obtained deposits were characterized using scanning electron
microscopy (SEM) and energy dispersive spectroscopy (EDS). Critical overpotential of aluminium
deposition decreased from around ā 0.150 V at 25Ā°C to around ā 0.100 V at 50Ā°C. All recorded
currents were small but would substantially increase with increasing working temperature (from 0.01
mA cm-2 up to 0.25 mA cm-2). The deposits obtained showed variety of morphological shapes
depending on the working temperature and potential applied. All the deposits were made of very
small crystallites grouped randomly into more or less separate agglomerates. Density of the
crystallites distribution over the substrate and complicity of the crystal forms increased with the
potential applied.
Electrodeposition/dissolution of aluminium in used electrolyte onto used substrate obviously
promises positive results if research aiming at reversible systems of such composition working at
temperatures very close to room temperature.Ispitivano je elektrohemijsko taloženje aluminijuma na staklastom ugljeniku iz eutektiÄke smeÅ”e
(DES), AlCl3+urea, na temperaturama od 25-50Ā°C. Elektrotaloženje je izvoÄeno potenciostatski.
Morfologija dobijenih taloga je analizirana skenirajuÄom elektronskom mikroskopijom (SEM) i
energetsko disperzivnom spektroskopijom (EDS). KritiÄne prenapetosti elektrotaloženja aluminijuma
kretale su se od oko ā 0.150 V pri 25Ā°C do oko ā 0.100 V pri 50Ā°C. Zabeležene gustine struje bile su
male, ali su njihove vrednosti znaÄajno rasle sa poveÄanjem radne temperature (od 0.01 mA cm-2 do
0.25 mA cm-2 uz poveÄanje temperature od 25Ā°C do 50Ā°C). Dobijeni talozi pokazali su raznovrsne
morfoloŔke oblike Ŕto je zavisilo od primenjene temperature i potencijala. Svi talozi sastojali su se od
veoma malih kristala objedinjenih u aglomerate koji su bili nasumiÄno rasporeÄeni po povrÅ”ini radne
electrode. Gustina rasporeda kristalita po povrÅ”ini elektrode i njihova pojedinaÄna raznovrsnost po
obliku rasle su sa poveÄanjem primenjenog potencijala.
Elektrohemijsko taloženje/rastvaranje aluminijuma u upotrebljenom elektrolitu i na upotrebljenoj
podlozi obeÄava pozitivne rezultate u istraživanjima usmerenim na reverzibilne sisteme istog ili
sliÄnog sastava koji bi trebalo da rade na temperaturama veoma bliskim sobnoj
Al-Pd alloy formation by aluminium underpotential deposition onto palladium from chloroaluminate melt
The possibility of electrochemical underpotential deposition of aluminium onto palladium from equimolar AlCl3+NaCl melts at temperatures between 200 Ā° and 300 Ā°C was investigated. Electrochemical techniques used were cyclic voltammetry, chronoamperometry, potentiodynamic polarization and open circuit measurements. The results were analyzed by SEM, EDX and XRD. It was found that Š°luminium deposits underpotentially onto palladium at around 0.200 V vs. Al from the chloroaluminate melt used. It was established that under the given conditions, Al underpotential deposition onto the palladium substrate can result in AlPd and Al3Pd4 alloy synthesis by solid-state interdiffusion. The surface alloys synthetized are well adhering, microcrystalline deposits, having highly developed surface area suitable for applications such as hydrogen purification filters
Alloy formation by mg under-potential deposition on al from nitrate melts
Magnesium was underpotentially deposited on aluminium electrodes from magnesium nitrate-ammonium nitrate melts at temperatures ranging from 390 to 500 K. The electrochemical techniques used were linear sweep voltammetry and potential step. Electrodes were studied by scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD). It was found that reduction processes of nitrate, nitrite and water (when present), in the underpotential range studied, took part simultaneously with magnesium underpotential deposition. Consequently, magnesium UPD reduction and stripping voltammetry peaks were not pronounced and well defined. Nevertheless, EDS, EDX and XRD measurements showed evidence of Mg2Al3, MgAl2 and Al12Mg17 alloys formed by underpotential deposition of magnesium onto aluminium substrate
Electrochemical Deposition of Aluminium on Aluminium from Ureabased Electrolyte
Electrochemical deposition/dissolution of aluminium to/from aluminium in deep eutectic solvent
(DES), made of the AlCl3+urea, at temperatures of 25 to 60Ā°C have been investigated. The depositions were performed in potentiostatic modes. The morphology of the obtained deposits was characterized using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).
Critical overpotential of aluminium deposition increased from around ā 0.120 V at 25Ā°C to
around ā 0.050 V at 50Ā°C. All recorded currents were generally speaking small, but would substantially increase with increasing working temperature (from 0.01 mA cm-2 up to 0.25 mA cm-2). Current/time transients recorded at overpotentials over ā 0.100 V vs. Al indicate continuous three-dimensional nucleation and growth. Epitaxial growth over aluminium substrate was not observed under applied experimental conditions.
Electrodeposition/dissolution processes of aluminium under chosen conditions were reversible,
reproducible and slow (relatively small current densities, bellow 0.3 mA cm-2). Polarization curves
recorded noticeable dependence of aluminium deposition/dissolution reversible potential on temperature applied.
The deposits obtained showed variety of morphological shapes (needles, rods, flakes, Fig.1)
depending on the working temperature and potential applied. All the deposits were made of crystallites grouped randomly into more or less separate agglomerates which were positioned over lower layer of densely populated much smaller crystallites. Lower layer showed good adherence to the substrate and exhibited high surface area. Density of the crystallites distribution over the substrate and complicity of the crystal forms increased with the potentials applied
Aluminium electrodeposition onto glassy carbon from deep eutectic system made of AlCl3+urea
Electrochemical deposition of aluminium onto glassy carbon from deep eutectic solvent (DES), made
of the AlCl3+urea, at 25-50Ā°C have been investigated. The deposition was performed in potentiostatic
mode. The morphology of the obtained deposits were characterized using scanning electron
microscopy (SEM) and energy dispersive spectroscopy (EDS). Critical overpotential of aluminium
deposition decreased from around ā 0.150 V at 25Ā°C to around ā 0.100 V at 50Ā°C. All recorded
currents were small but would substantially increase with increasing working temperature (from 0.01
mA cm-2 up to 0.25 mA cm-2). The deposits obtained showed variety of morphological shapes
depending on the working temperature and potential applied. All the deposits were made of very
small crystallites grouped randomly into more or less separate agglomerates. Density of the
crystallites distribution over the substrate and complicity of the crystal forms increased with the
potential applied.
Electrodeposition/dissolution of aluminium in used electrolyte onto used substrate obviously
promises positive results if research aiming at reversible systems of such composition working at
temperatures very close to room temperature.Ispitivano je elektrohemijsko taloženje aluminijuma na staklastom ugljeniku iz eutektiÄke smeÅ”e
(DES), AlCl3+urea, na temperaturama od 25-50Ā°C. Elektrotaloženje je izvoÄeno potenciostatski.
Morfologija dobijenih taloga je analizirana skenirajuÄom elektronskom mikroskopijom (SEM) i
energetsko disperzivnom spektroskopijom (EDS). KritiÄne prenapetosti elektrotaloženja aluminijuma
kretale su se od oko ā 0.150 V pri 25Ā°C do oko ā 0.100 V pri 50Ā°C. Zabeležene gustine struje bile su
male, ali su njihove vrednosti znaÄajno rasle sa poveÄanjem radne temperature (od 0.01 mA cm-2 do
0.25 mA cm-2 uz poveÄanje temperature od 25Ā°C do 50Ā°C). Dobijeni talozi pokazali su raznovrsne
morfoloŔke oblike Ŕto je zavisilo od primenjene temperature i potencijala. Svi talozi sastojali su se od
veoma malih kristala objedinjenih u aglomerate koji su bili nasumiÄno rasporeÄeni po povrÅ”ini radne
electrode. Gustina rasporeda kristalita po povrÅ”ini elektrode i njihova pojedinaÄna raznovrsnost po
obliku rasle su sa poveÄanjem primenjenog potencijala.
Elektrohemijsko taloženje/rastvaranje aluminijuma u upotrebljenom elektrolitu i na upotrebljenoj
podlozi obeÄava pozitivne rezultate u istraživanjima usmerenim na reverzibilne sisteme istog ili
sliÄnog sastava koji bi trebalo da rade na temperaturama veoma bliskim sobnoj
Galvanostatsko elektrohemijsko taloženje aluminijuma na aluminijumu iz rastopa AlCl3+NaCl
The processes of galvanostatic electrochemical deposition of aluminium onto aluminium from
chloroaluminate melt made of equimolar AlCl3+NaCl mixture at 200Ā°C have been investigated. The
obtained deposits were characterized using scanning electron microscopy (SEM) and energy
dispersive spectroscopy (EDS).
Galvanostatic Al deposition from the used melt onto aluminium substrate with smaller current
densities (2-5 mA cm-2) gave relatively close-packed and well adhering deposits. Aluminium deposits
obtained galvanostatically with current densities larger than 5 mA cm-2 are less compact, more
crystalline and less adhering to the aluminium substrate. Al deposits obtained with 10 and 12.5 mA
cm-2 were voluminous, very crystalline and poorly adhering to the working electrode substrate. These
deposits were made of very small crystallites grouped randomly into more or less separate
agglomerates
Magnesium underpotential deposition from nitrate melts and alloy formation with platinum substrate
This paper investigates magnesium underpotential deposition on platinum electrodes from magnesium nitrate-ammonium nitrate melts at temperatures ranging from 400 to 500 K. Electrochemical techniques used were linear sweep voltammetry and potential step. Electrode surfaces were studied by Scanning electron microscopy (SEM), Atomic force microscopy (AFM), Energy dispersive spectrometry (EDS), energy dispersive X-Ray spectroscopy (EDX) and X-Ray diffraction (XRD). In the underpotential range studied, it was found that magnesium underpotential deposition took part simultaneously with reduction processes of nitrate and nitrite. EDS and XRD measurements showed clear evidence of MgPt3, Mg3Pt alloys being formed
Morphology of aluminium electrodeposited on aluminium from AlCl3+urea solvate ionic liquid
The ionic liquid, made of urea and AlCl3, known as deep eutectic solvent (DESs) has already shown to be lowācost electrolyte suitable for aluminum electrodeposition. By applying appropriate potentiostatic or galvanostatic electrolysis regime, aluminium is successfully electrodeposited from the deep eutectic solvent onto aluminium substrate at nearly room temperatures. Morphologies of the produced deposits were characterized by scanning electron microscopy (SEM) and chemical composition by energy-dispersive X-ray (EDX) analysis. The electrodeposited aluminium displayed different morphology depending on the deposition conditions applied
Formation of niobium oxides by electrolysis from acidic aqueous solutions on glassy carbon
In this study niobium oxide films were formed without peroxo-precursors from three different mixed acidic aqueous solutions on glassy carbon. Linear sweep voltammetry and potential step were techniques used for electrochemical experiments. The simultaneous and consecutive electrochemical reduction of water, nitrate and sulphate ions provided an alkaline environment with oxygen in the near vicinity of the working cathode, which in combination with the present niobium ions, produced niobium oxides and/or oxyhydroxides on the glassy carbon substrate. The formed deposits were analyzed using scanning electron microscopy and energy dispersive spectroscopy and appear to consist of NbO, NbO2 and Nb2O5. Both the niobium and acid concentration of the electrolytes used influenced the morphology and particle size of the deposits. The formation of niobium-fluoride and hydrogen-niobiumoxide complexes is addressed
- ā¦