Modificación de tejido de poliéster mediante la fabricación de compuestos de nano-cobre

This research introduces a new method of polyester fabric surface modification in order to achieve distinctive features. The copper sulfate, sodium hydroxide and cetyl trimethylammonium bromide (CTAB) were used to synthesize copper nanoparticles, and loaded on the polyester fabric surface. The optimal sample was considered by SEM-EDX, FT-IR and XRD devices. SEM images showed copper nanoparticles in shape of nano-plates with 150 to 600 nm in length and thickness of about 30 nm. The best results obtained on the modified fabric processed at boil for 120 min. According to the results of experiments CuO and Cu0 were synthesized on the fabric.This research introduces a new method of polyester fabric surface modification in order to achieve distinctive features. The copper sulfate, sodium hydroxide and cetyl trimethylammonium bromide (CTAB) were used to synthesize copper nanoparticles, and loaded on the polyester fabric surface. The optimal sample was considered by SEM-EDX, FT-IR and XRD devices. SEM images showed copper nanoparticles in shape of nano-plates with 150 to 600 nm in length and thickness of about 30 nm. The best results obtained on the modified fabric processed at boil for 120 min. According to the results of experiments CuO and Cu0 were synthesized on the fabric

Usage of alkaline glucose for Synthesis Copper Nano particle on Polyester Fabric

In this study, Nano copper from the chemical reaction between copper salt and sodium hydroxide was produced. Interestingly, simultaneous synthesis of Nano-copper chemical method and depositing Nano materials on the fabric's surface. The glucose is used as a stabilizer. An important feature of this study is, simplicity, availability, low cost and etc. The results create Nano-copper with a thickness of 30-40 nanometers on the surface of the fabric is shown. The treated fabrics could be used in diverse areas such as defense, aerospace, electronics, medical and health industries