Terahertz Emission of Gallium Arsenide on Textured p-type Silicon (100) Substrates Grown via Molecular Beam Epitaxy

This study presents the terahertz (THz) emission of molecular beam epitaxy (MBE)-grown Gallium Arsenide (GaAs) on surface textured p-type Silicon (p- Si) (100) substrates. Surface texturing was achieved by anisotropic wet chemical etching using 5% wt Potassium Hydroxide (KOH): Isopropyl alcohol (IPA) (50:1) solution for 15, 30, 45, and 60 minutes. Reflectivity measurements for the textured p-Si(100) substrates indicated that the overall texturing increases with longer etching times. Raman spectroscopy of the post-growth samples confirmed GaAs growth. The THz emission intensities were the same order of magnitude. The GaAs grown on p-Si(100) textured for 60 minutes exhibited the most intense THz emission attributed to the increased absorption from a larger surface-to-volume ratio due to surface texturing. All GaAs on textured p-Si(100) samples had frequency bandwidth of ~2.5 THz

Growth of Gold-assisted Gallium Arsenide Nanowires on Silicon Substrates via Molecular Beam Epitaxy

Gallium arsenide nanowires were grown on silicon (100) substrates by what is called the vapor-liquid-solid (VLS) growth mechanism using a molecular beam epitaxy (MBE) system. Good quality nanowires with surface density of approximately 108 nanowires per square centimeter were produced by utilizing gold nanoparticles, with density of 1011 nanoparticles per square centimeter, as catalysts for nanowire growth. X-ray diffraction measurements, scanning electron microscopy, transmission electron microscopy and Raman spectroscopy revealed that the nanowires are epitaxially grown on the silicon substrates, are oriented along the [111] direction and have cubic zincblende structure