Investigation of the reactivity of AlCl3 and CoCl2 toward molten alkali-metal nitrates in order to synthesize CoAl2O4

Cobalt aluminate CoAl2O4 powder, constituted of nano-sized crystallites, is prepared, involving the reactivity of AlCl3 and CoCl2 with molten alkali-metal nitrates. The reaction at 450 °C for 2 h leads to a mixture of spinel oxide Co3O4 and amorphous γ-Al2O3. It is transformed into the spinel oxide CoAl2O4 by heating at 1000 °C. The powders are mainly characterized by XRD, FTIR, ICP, electron microscopy and diffraction, X-EDS and diffuse reflection. Their properties are compared to those of powders obtained by solid state reactions of a mechanical mixture of chlorides or oxides submitted to the same thermal treatment

Fe–Cr/Al2O3 metal-ceramic composites: Nature and size of the metal particles formed during hydrogen reduction

Fe-Cr/Al2O3 metal-ceramic composites prepared by hydrogen reduction at different temperatures and for different periods have been investigated by a combined use of Mössbauer spectroscopy, x-ray diffraction, transmission electron microscopy, and energy-dispersive x-ray spectroscopy in order to obtain information on the nature of the metallic species formed. Total reduction of Fe3+ does not occur by increasing the reduction time at 1320 K from 1 to 30 h, and the amount of superparamagnetic metallic species is essentially constant (about 10%). Temperatures higher than 1470 K are needed to achieve nearly total reduction of substitutional Fe3+. Interestingly, iron favors the reduction of chromium. The composition of the Fe-Cr particles is strongly dependent on their size, the Cr content being higher in particles smaller than 10 nm