Ultrasonic Transducers made from Freeze-Cast Porous Piezoceramics

Porous and composite piezoelectric ceramics are of interest for underwater ultrasonic transducers due to their improved voltage sensitivity and acoustic matching with water, compared with their dense counterparts. Commonly, these materials are fabricated by dice-and-fill of sintered blocks of polycrystalline piezoceramic, which results in a high volume of waste. The freeze-casting technique offers a low waste and scalable alternative to the dice-and-fill method to produce porous piezoceramics with highly orientated, anisometric pores. In this article, we have fabricated underwater ultrasonic transducers from freeze-cast lead zirconate titanate (PZT) with a range of porosities. The porous PZT samples were characterized in terms of their piezoelectric and dielectric properties before being encapsulated for acoustic performance testing in water. Off resonance, the on-axis receive sensitivity of the manufactured devices was approximately-200 ± 10 dB re 1 V μ Pa; the transmit voltage response (TVR) was in the range of approximately 115 ± 5 dB re 1 μ Pa/V at 60 kHz to 132.5 ± 2.5 dB re 1 μ Pa/{V} at 180 kHz. The most porous transducer devices (0.51, 0.43, and 0.33 pore fraction) exhibited primarily a thickness mode resonance, whereas the least porous transducers (0.29 pore fraction and dense benchmark) exhibited an undesired radial mode, which was observed as an additional resonant peak in the electrical impedance measurements and lateral off-axis lobes in the acoustic beampatterns. Our results show that the acoustic sensitivities and TVRs of the porous freeze-cast transducers are comparable to those of a dense pressed transducer. However, the freeze-cast transducers with porosity exceeding 0.30 pore fraction were shown to achieve an effective structure with aligned porosity that suppressed undesired radial mode resonances.</p

Freeze cast porous barium titanate for enhanced piezoelectric energy harvesting

Energy harvesting is an important developing technology for a new generation of self-powered sensor networks. This paper demonstrates the significant improvement in the piezoelectric energy harvesting performance of barium titanate by forming highly aligned porosity using freeze casting. Firstly, a finite element model demonstrating the effect of pore morphology and angle with respect to poling field on the poling behaviour of porous ferroelectrics was developed. A second model was then developed to understand the influence of microstructure-property relationships on the poling behaviour of porous freeze cast ferroelectric materials and their resultant piezoelectric and energy harvesting properties. To compare with model predictions, porous barium titanate was fabricated using freeze casting to form highly aligned microstructures with excellent longitudinal piezoelectric strain coefficients, d 33. Both model and experimental data indicated that introducing porosity provides a large reduction in the permittivity () of barium titanate, which leads to a substantial increase in energy harvesting figure of merit, , with a maximum of 3.79 pm2 N-1 for barium titanate with 45 vol.% porosity, compared to only 1.40 pm2 N-1 for dense barium titanate. Dense and porous barium titanate materials were then used to harvest energy from a mechanical excitation by rectification and storage of the piezoelectric charge on a capacitor. The porous barium titanate charged the capacitor to a voltage of 234 mV compared to 96 mV for the dense material, indicating a 2.4-fold increase that was similar to that predicted by the energy harvesting figures of merit

The development of a physical model of an advanced gas cooled reactor core: Outline of the feasibility study

The ageing issues of the Advanced Gas Cooled Reactor (AGR) cores need addressing to maintain their safe and reliable operation, hence the requirement for the computer models of the cores used for the seismic resilience assessments to be conservative and to represent larger percentages of damaged graphite components. The current models have undergone limited experimental validation for high levels of degradation, so there is a need to validate those numerical models and also to enhance the understanding of core dynamics by physical modelling and testing. This paper outlines the feasibility study of a quarter scale model rig of an AGR core developed by the University of Bristol. The damage scenarios to be considered in demonstrating the core seismic tolerability were defined. The principles of scale modelling were put under scrutiny in parallel with several practical aspects of material selection and component design and manufacturing. Several variants of physical models of different size and shape were proposed and their merits with respect to their feasibility and outcomes were discussed. Aspects of instrumentation design are presented together with relevant measurement results. The rig is a viable experimental tool whose outputs can be employed directly in computer model validation

Porous ferroelectrics for energy harvesting applications

This paper provides an overview of energy harvesting using ferroelectric materials, with a particular focus on the energy harvesting capabilities of porous ferroelectric ceramics for both piezo- and pyroelectric harvesting. The benefits of introducing porosity into ferro- electrics such as lead zirconate titanate (PZT) has been known for over 30 years, but the potential advantages for energy harvesting from both ambient vibrations and temperature fluctuations have not been studied in depth. The article briefly discusses piezoelectric and pyro- electric energy harvesting, before evaluating the potential benefits of porous materials for increasing energy harvesting figures of merits and electromechanical/electrothermal coupling factors. Established processing routes are evaluated in terms of the final porous structure and the resulting effects on the electrical, thermal and mechanical properties

Manufacture and characterization of porous ferroelectrics for piezoelectric energy harvesting applications

Porous ferroelectric materials have been evaluated for their piezoelectric energy harvesting capabilities. Macro-porous barium titanate (BaTiO3) ceramics were fabricated with a range of porosities using the burned out polymer spheres process. The pore fraction was tailored by mixing a pore forming agent with BaTiO3 powder in varying amounts by weight before cold-pressing and pressureless sintering. Introducing porosity into the ferroelectric significantly increased the energy harvesting figure of merit, with a maximum of 2.85pm2/N obtained at ∼40% relative density compared with ∼1.0 pm2/N for the dense material. The results demonstrate that introducing porosity into a piezoelectric potentially provides an effective route to improving the vibration energy harvesting capability of these materials.</p

Freeze cast porous barium titanate for enhanced piezoelectric energy harvesting

Energy harvesting is an important developing technology for a new generation of self-powered sensor networks. This paper demonstrates the significant improvement in the piezoelectric energy harvesting performance of barium titanate by forming highly aligned porosity using freeze casting. Firstly, a finite element model demonstrating the effect of pore morphology and angle with respect to poling field on the poling behaviour of porous ferroelectrics was developed. A second model was then developed to understand the influence of microstructure-property relationships on the poling behaviour of porous freeze cast ferroelectric materials and their resultant piezoelectric and energy harvesting properties. To compare with model predictions, porous barium titanate was fabricated using freeze casting to form highly aligned microstructures with excellent longitudinal piezoelectric strain coefficients, d 33. The freeze cast barium titanate with 45 vol.% porosity had a d 33 = 134.5 pC N-1 compared to d 33 = 144.5 pC N-1 for dense barium titanate. The d 33 coefficients of the freeze cast materials were also higher than materials with uniformly distributed spherical porosity due to improved poling of the aligned microstructures, as predicted by the models. Both model and experimental data indicated that introducing porosity provides a large reduction in the permittivity () of barium titanate, which leads to a substantial increase in energy harvesting figure of merit, , with a maximum of 3.79 pm2 N-1 for barium titanate with 45 vol.% porosity, compared to only 1.40 pm2 N-1 for dense barium titanate. Dense and porous barium titanate materials were then used to harvest energy from a mechanical excitation by rectification and storage of the piezoelectric charge on a capacitor. The porous barium titanate charged the capacitor to a voltage of 234 mV compared to 96 mV for the dense material, indicating a 2.4-fold increase that was similar to that predicted by the energy harvesting figures of merit.</p

Concerning the Etiology of Syrah Decline: A Fresh Perspective on an Old and Complex Issue Facing the Global Grape and Wine Industry

Syrah decline, first identified in Southern France in the 1990s, has become a major concern in the global grape and wine industry. This disease mainly affects Syrah (Shiraz) grapevines. Characteristic symptoms include the bright and uniform reddening of leaves throughout the canopy in late summer or early fall; the appearance of abnormalities on the trunk, mainly at the graft union (swelling, pits, grooves, and necrosis); and a reduction in vine vigor, yield and berry quality. Diseased vines may die a few years after disease onset. Damages to the vine are even more pronounced in cool climate regions such as Ontario (Canada), where the affected vines are subjected to very cold and prolonged winters, leading to large numbers of vine deaths. Despite the extensive efforts of the global grape research community over the past few decades, the etiology of this disease remains unclear. In this study, we conducted extensive analyses of viruses in declining Syrah vines identified in commercial vineyards in the Niagara region (Ontario, Canada) through high-throughput sequencing, PCR, RT-PCR and the profiling of genetic variants of select viruses. Multiple viruses and viral strains, as well as three viroids, were identified. However, an unequivocal causal relationship cannot be established between Syrah decline and any of these viruses, although the possibility that certain virus or genetic variants, or both in combination, may contribute to the disease cannot be excluded. Gleaning all information that is available to date, we feel that the traditional approach and an insistence on finding a single cause for such a complex disorder in a woody perennial fruit crop involving grafting will prove to be futile. We hope that this study offers new conceptual perspectives on the etiology of this economically important but enigmatic disease complex that affects the global grape and wine industry