Studi Pengaruh Penyinaran Lampu Ultraviolet pada Kinerja Fotodegradasi Metilen Biru Berfotokatalis TiO2

Telah dilakukan penelitian mengenai pengaruh penyinaran lampu ultraviolet pada kinerja fotodegradasi metilen biru menggunakan fotokatalis TiO2 yang dilapiskan pada Polipropilena (PP). Proses pabrikasi material PP/TiO2 dilakukan dengan teknik deposisi thermal milling. Temperatur kostan yang digunakan dalam proses milling adalah 175 selama 60 menit. Material PP/TiO2 digunakan sebagai material penyangga pada fotodegradasi metilen biru (MB). Proses fotokatalisis berlangsung selama 40 jam dengan sinar lampu UV sebagai suber foton dan penambahan bahan fotokatalis yang disinari UV dan tanpa disinari UV (kondisi gelap). Konsentrasi awal metilen biru yang digunakandengan perbandingan katalis PP/TiO2 sebanyak 14 g (1:1). Alat uji yang digunakan Spektrofotometer UV-Vis. Berdasarkan hasil penelitian, menunjukkan semikonduktor TiO2 yang dilapiskan dipermukaan butiran PP berpengaruh pada laju fotodegradasi larutan pewarna MB yang terlihat dari terjadinya perubahan warna secara gradual yang menandakan terjadinya proses fotodegradasi, serta adanya penurunan puncak spektrum absorbansi MB dan dengan adanya material fotokatalis yang disinari lampu UV jauh lebih efektif dibandingkan tanpa disinari UV. Pada proses ini tidak terlihat adanya residu dan laju fotodegradasi optimal pada lama penyinaran selama 32 jam yang menghasilkan penurunan konsetrasi MB sekitar 68% dari konsentrasi awalnya.  Kata Kunci : Metilen biru, lampu Ultraviolet, thermal milling, fotokatalis, PP, TiO

Production of Ceramic Membrane Based on Acid- and Alkali-Activated Metakaolinite as Cooling Material for Monocrystalline Silicon Solar Cell

Ceramic membrane based on acid- and alkali-activated metakaolinite has been produced. It was tested as a cooling material for monocrystalline silicon solar cells. Membrane was made by several stages, such as calcination of natural kaolinite at 600 oC for 6 hours to obtain metakaolinite, activation of metakaolinite by concentrated HCl and KOH, and preparation of ceramic membrane. Kaolinite, metakaolinite, and activated metakaolinite were characterized by X-ray diffraction (XRD), X-ray fluorescence (XRF), Fourier Transform Infra-red (FTIR), and gas sorption analyzer (GSA). Diffractogram of XRD showed that there was a structural change between activated metakaolinite and natural kaolinite. XRF analysis indicated that the Si/Al of HCl activated metakaolinite was three times higher than natural kaolinite. Activated metakaolinite was made into membrane by adding a binder, then heated at 800 °C for 6 hours. PV cells with and without cooling material were then analyzed their electrical performances. It was found that the maximum energy conversion yield of PV cells without using cooling material was 2.30%, while the maximum energy conversion yield of PV cells with cooling material of meta-kaolinite activated by HCl and KOH were respectively 2.72% and 2.94%