Chemical shrinkage of low water to cement (w/c) ratio CEM I and CEM III cement pastes incorporating silica fume and filler

Chemical shrinkage (CS) is the reason behind early age cracking, a common problem for concrete with low water to cement ratios (w/c < 0.35) known as Ultra-High- and High-Performance Concrete (U-HPC). However, to avoid the crack development initiated by autogenous shrinkage, a precise measurement of CS is required, as the values obtained can determine the correct amount of internal curing agent to be added in the mixture to avoid crack formation. ASTM C1608 is the standardized method for performing CS tests. In this study, recommendations are provided to improve the reliability of results obtained with this standard method, such as good compaction of samples and the use of superplasticizer (SP) for low w/c ratios (≤0.2). Cement pastes with CEM I and CEM III have been tested at different w/c ratios equal to 0.2, 0.3 and 0.4 with and without the addition of superplasticizer. CS results following ASTM-C1608 dilatometry showed that the presence of mineral additions such as silica fume and filler reduced the chemical shrinkage, while CS increased with increasing w/c. Low w/c ratio pastes of CEM III had slightly higher CS rates than CEM I, while the opposite was noticed at higher w/c. SEM images illustrated the importance of a careful compaction and SP use

Mechanical regains due to self-healing in cementitious materials: experimental measurements and micro-mechanical model

International audienc

Modelling of autogenous healing in ultra high performance concrete

International audienc

Design of polymeric capsules for self-healing concrete

International audienceUp to now, glass capsules, which cannot resist the mixing process of concrete, have been mostly used in lab-scale proof-of-concept to encapsulate polymeric agents in self-healing concrete. This study presents the design of polymeric capsules which are able to resist the concrete mixing process and which can break when cracks appear. Three different polymers with a low glass transition temperature T g have been extruded: Poly(lactic acid) (PLA) (T g = 59 °C), Polystyrene (PS) (Tg = 102 °C) and Poly(methyl methacrylate/n-butyl methacrylate) (P(MMA/n-BMA)) (Tg = 59 °C). After heating the capsules prior to mixing with other components of the mix, to shift from a brittle state to a rubbery state, their survival ratio considerably increased. Moreover, a part of the capsules, which previously survived the concrete mixing process, broke with crack appearance. Although some optimization is still necessary concerning functional life of encapsulated adhesives, this seems to be a promising route