LAJU KOROSI RETAK TEGANGAN DALAM LARUTAN ASAM DAN BASA DENGAN SWEET GAS PADA PIPA BAJA KARBON DENGAN DEFLEKSI YANG SAMA

Exploration of natural gas or steam exploration offshore or landing and exploration in the petroleum industry offshore or on land that generally will be followed by corrosive substances including sweet gas (eg H2S and CO2), so that the impact of corrosion cracking events will result so that carbon steel pipes will result in a breakdown, the production process will stop. This study uses a three-point loading method. Each of the three test samples is inserted into the chamber which contains an acid solution and alkaline solution. The results of the research data show that the corrosion rate will be greater along with the length of time exposure for the same deflection. For test samples in alkaline solutions, the results of the study show that the corrosion rate will decrease with the length of exposure time for the same deflection due to the presence of salt attached to the test sample. And based on microstructure test results both in the environment of acidic conditions or alkaline conditions that occur is corrosion of transgranular stress cracks and intergranular stress crack corrosion.Eksplorasi gas alam ataupun eksplorasi uap dilepas pantai ataupun didaratan serta eksplorasi di industri minyak bumi di lepas pantai atau di daratan bahwa pada umumnya akan diikuti dengan zat korosif termasuk sweet gas (misalnya H2S dan CO2), sehingga akan berdampak akibatnya terjadi peristiwa korosi retak tegangan sehingga pipa baja karbon akan mengakibatkan pecah maka proses produksi akan terhenti. Penelitian ini menggunakan metoda tiga titik pembebanan. Masing-masing tiga sampel uji dimasukkan ke ruang chamber yang berisi larutan asam dan larutan basa. Hasil data penelitian menunjukkan bahwa laju korosinya akan semakin besar seiring dengan lamanya waktu paparan untuk defleksi yang sama. Untuk sampel uji dalam larutan basa, hasil penelitian menunjukkan bahwa laju korosinya akan menurun seiring dengan lamanya waktu paparan untuk defleksi yang sama karena dengan adanya garam yang menempel pada sampel uji. Dan berdasarkan hasil uji mikrostruktur baik pada lingkungan kondisi asam atau kondisi basa yang terjadi adalah korosi retak tegangan transgranular dan korosi retak tegangan intergranular

LAJU KOROSI RETAK TEGANGAN DALAM LARUTAN ASAM DAN BASA DENGAN SWEET GAS PADA PIPA BAJA KARBON DENGAN DEFLEKSI YANG SAMA

Exploration of natural gas or steam exploration offshore or landing and exploration in the petroleum industry offshore or on land that generally will be followed by corrosive substances including sweet gas (eg H2S and CO2), so that the impact of corrosion cracking events will result so that carbon steel pipes will result in a breakdown, the production process will stop. This study uses a three-point loading method. Each of the three test samples is inserted into the chamber which contains an acid solution and alkaline solution. The results of the research data show that the corrosion rate will be greater along with the length of time exposure for the same deflection. For test samples in alkaline solutions, the results of the study show that the corrosion rate will decrease with the length of exposure time for the same deflection due to the presence of salt attached to the test sample. And based on microstructure test results both in the environment of acidic conditions or alkaline conditions that occur is corrosion of transgranular stress cracks and intergranular stress crack corrosion.Eksplorasi gas alam ataupun eksplorasi uap dilepas pantai ataupun didaratan serta eksplorasi di industri minyak bumi di lepas pantai atau di daratan bahwa pada umumnya akan diikuti dengan zat korosif termasuk sweet gas (misalnya H2S dan CO2), sehingga akan berdampak akibatnya terjadi peristiwa korosi retak tegangan sehingga pipa baja karbon akan mengakibatkan pecah maka proses produksi akan terhenti. Penelitian ini menggunakan metoda tiga titik pembebanan. Masing-masing tiga sampel uji dimasukkan ke ruang chamber yang berisi larutan asam dan larutan basa. Hasil data penelitian menunjukkan bahwa laju korosinya akan semakin besar seiring dengan lamanya waktu paparan untuk defleksi yang sama. Untuk sampel uji dalam larutan basa, hasil penelitian menunjukkan bahwa laju korosinya akan menurun seiring dengan lamanya waktu paparan untuk defleksi yang sama karena dengan adanya garam yang menempel pada sampel uji. Dan berdasarkan hasil uji mikrostruktur baik pada lingkungan kondisi asam atau kondisi basa yang terjadi adalah korosi retak tegangan transgranular dan korosi retak tegangan intergranular