Natural aging and reversion behavior of Al-Cu-Li-Ag-Mg alloy Weldalite (tm) 049

This study was initiated to understand the natural aging and reversion behavior of Weldalite (trademark) 049 in tempers without cold work. Of particular interest are: (1) the microstructural basis for the high strength in the T4 condition; (2) an explanation of the reversion phenomenon; and (3) the effect of re-aging at room temperature after a reversion treatment. Mechanical properties were measured and transmission electron microscopy (TEM) analysis performed at various stages of microstructural development during aging, reversion, and subsequent re-aging

Structure and properties during aging of an Al-Cu-Li-Ag-Mg alloy, Weldalite (tm) 049

An Al-Cu-Li-Ag-Mg alloy, Weldalite (trademark) 049, was recently introduced as an ultra-high strength alloy (7000 MPa yield strength in artificially aged tempers) with good weldability. In addition, the alloy exhibits an extraordinary natural aging response (440 MPa yield strength (YS) in the unstretch condition) and a high ductility reversion condition which may be useful as a cold-forming temper. In contrast to other Al-Li alloys, these properties can essentially be obtained with or without a stretch or other coldworking operation prior to aging. Preliminary studies have revealed that the T4 temper (no stretch, natural age) is strengthened by a combination of GP zones and delta prime (Al3Li). The T6 temper (no stretch, aged at 180 C to peak strength) was reported to be strengthened primarily by T(sub 1) phase (Al2CuLi) with a minor presence of a theta prime like (Al2Cu) phase. On the other hand, a similar but lower solute containing alloy was reported to contain omega, (stoichiometry unknown), theta prime, and S prime in the peak strength condition. The purpose of this study is to further elucidate the strengthening phases in Weldalite (trademark) 049 in the unstretched tempers, and to follow the development of the microstructure from the T4 temper through reversion (180 C for 5 to 45 minutes) to the T6 temper