9 research outputs found
Superconducting Tl-Ba-Ca-Cu-O films by sputtering
Superconducting Tl-Ba-Ca-Cu-O thin films 0.2–1.0 µm thick have been prepared on MgO(100) and SrTiO3 (100) substrates by dc diode sputtering using a single oxide target. Films containing primarily the Tl2Ba2Ca1Cu2O8 phase were obtained with a Tc (R =0) at 102 K and a transport Jc of 104 A/cm2 at 90 K. For the nearly pure phase Tl2Ba2Ca2Cu3O10 films, the Tc\u27s (R =0) are higher at 116 K and the transport Jc\u27s at 100 K are of 105 A/cm2. Both types of films show a strong preferred orientation with the c axis perpendicular to the film plane. The rocking curve of the Tl2Ba2Ca2Cu3O10 films is 0.32° wide and the typical grain size is over 10 µm
Superconducting Tl-Ba-Ca-Cu-O films by sputtering
Superconducting Tl-Ba-Ca-Cu-O thin films 0.2–1.0 µm thick have been prepared on MgO(100) and SrTiO3 (100) substrates by dc diode sputtering using a single oxide target. Films containing primarily the Tl2Ba2Ca1Cu2O8 phase were obtained with a Tc (R =0) at 102 K and a transport Jc of 104 A/cm2 at 90 K. For the nearly pure phase Tl2Ba2Ca2Cu3O10 films, the Tc\u27s (R =0) are higher at 116 K and the transport Jc\u27s at 100 K are of 105 A/cm2. Both types of films show a strong preferred orientation with the c axis perpendicular to the film plane. The rocking curve of the Tl2Ba2Ca2Cu3O10 films is 0.32° wide and the typical grain size is over 10 µm