Evaluation of Centrifuged Bone Marrow on Bone Regeneration Around Implants in Rabbit Tibia

Objective: To evaluate the bone regeneration of cervical defects produced around titanium implants filled with blood clot and filled with centrifuged bone marrow (CBM) by means of histomorphometric analysis.Materials and Methods: Twelve rabbits received 2 titanium implants in each right tibia, with the upper cortical prepared with a 5-mm drill and the lower cortex with a 3-mm-diameter drill. Euthanasia was performed to allow analysis at 7, 21, and 60 days after operation. The samples were embedded in light curing resin, cut and stained with alizarin red and Stevenel blue for a histomorphometric analysis of the bone-to-implant contact (BIC) and the bone area around implant (BA). The values obtained were statistically analyzed using the nonparametric Kruskal-Wallis test (P = 0.05).Results: At 60 days postoperation, the groups had their cervical defects completely filled by neo-formed bone tissue. There was no statistically significant difference between the groups regarding BIC and BA during the analyzed periods.Conclusion: There was no difference in the bone repair of periimplant cervical defects with or without the use of CBM. (Implant Dent 2012;21:481-485

Effect of bleaching agents and soft drink on titanium surface topography

The effects of carbamide peroxide, hydrogen peroxide and cola soft drink on the topographic modifications of commercially-pure titanium (CP-Ti) and Ti-6Al-4V were investigated. Ti discs were divided into 18 groups (n=4) based on the solution treatment and Ti type. Specimens were immersed in 3 mL of each solution for 4 h per day (for the remaining 20 h, discs were left dry or immersed in artificial saliva) for 15 days. For control, specimens were immersed in only artificial saliva. Ti surfaces were examined using scanning electron (SEM) and atomic force (AFM) microscopes and their surface roughness (in mu m) and surface chemical modifications were investigated. Data were analyzed by ANOVA and Tukey's test (=0.05). Groups immersed in 35% hydrogen peroxide showed the highest roughness (Ra) (171.65 +/- 4.04 for CP-Ti and 145.91 +/- 14.71 for Ti-6Al-4V) (p0.05). SEM and AFM revealed dramatic changes in the specimens surfaces immersed in the 35% hydrogen peroxide, mainly for CP-Ti. No detectable chemical modifications on the Ti surface were observed. Bleaching agents promoted significant changes in Ti topography, which could affect the longevity of implants treatments. (c) 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 102B: 22-30, 2014.Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq

Histometric analysis and topographic characterization of cp Ti implants with surfaces modified by laser with and without silica deposition

Biologic behavior of the bone tissue around implants with four different surfaces was evaluated. The surfaces were: modified by laser (LS); modified by laser with sodium silicate deposition (SS); and commercially available surfaces modified by acid etching (AS) and machined surface (MS). Topographic characterization of the surfaces was performed by scanning electron microscopy (SEM)- energy dispersive X-ray spectrometry (EDX) before experimental surgery. Thirty rabbits received 60 implants in their right and left tibias, 1 implant of each surface being placed in each tibia. The analyzed periods were 4,8, and 12 weeks postoperatively. Histometric analysis was performed evaluating bone interface contact (SIC) and bone area (BA). The results obtained were submitted to the analysis of variance and the Tukey t-test. The elemental mapping was evaluated by means of SEM at 4 weeks postoperatively. The topographic characterization showed differences between the analyzed surfaces. Generally, the BIC and BA of LS and SS implants were statistically higher than those of AS and MS in most of the analyzed periods. Elemental mapping showed high peaks of calcium and phosphorous in all groups. Based on the present methodology, it may be concluded that experimental modifications LS and SS accelerated the stages of the bone tissue repair process around the implants, providing the highest degree of osseointegration. (C) 2014 Wiley Periodicals, Inc.Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP