Study of the effects of gaseous environments on the hot corrosion of superalloy materials

The effect of the gaseous corrodent NaCl on the high temperature oxidation and sodium sulfate induced hot corrosion behavior of alumina formers, chromia formers, and the superalloy B-1900 was examined. Isothermal experiments were conducted at 900 C and 1050 C in air in the presence and absence of NaCl vapors. Microstructural changes in oxide morphology and increased rates of oxidation were observed when NaCl(g) was present. It is hypothesized that the accelerated rates of oxidation are the result of removal of aluminum from the scale substrate interface and the weakening of the scale substrate bonds. The aluminum removed was redeposited on the surfaces in the form of alumina whiskers. For the superalloy B-1900, alumina whiskers are also formed, and the alloy oxidizes at catastrophic rates. In the case of Ni-25Cr alloy, NaCl vapors interact with the scale depleting it of chromium

Study of the effects of gaseous environmental on the hot corrosion of superalloy materials

Studies have been conducted to examine the effect of low concentrations of NaCl(g) on the high temperature oxidation behavior of complex superalloys and potential coating formulations modified by silicon and reactive element (i.e., yttrium and hafnium) additions. Depending on alloy composition, a variety of effects were thermogravimetrically produced. Aluminum free alloys such as MAR-M509 and Hastelloy X with molybdenum and tungsten in solid solution showed accelerated (or breakaway) kinetics similar to that observed for Ni-Cr alloys. For IN-792, an alloy high in chromium and low in aluminum, molybdenum and tungsten present in solid solution does not adversely affect oxidation kinetics in the presence of NaCl(g). On the other hand, nickel-base alloys high in aluminum and molybdenum are catastrophically attacked by NaCl-bearing atmospheres. Silicon additions were, in general, observed to slightly improve the oxidation resistance of Ni, Ni-40Cr and CoCrAlY compositions in NaCl(g)-bearing atmospheres. To the degree that processes responsible for Al2O3 whisker formation deleteriously affect protective scale adherence, the addition of yttrium or hafnium can inhibit such whisker growth