Mechanical properties of the GX12CrMoVNbN91 (GP91) cast steel after different heat treatments

The paper presents results of research on the influence of multistage heat treatment of different types on the microstructure and properties of high-chromium martensitic GX12CrMoVNbN9-1 (GP91) steel. The material under investigation were samples taken out from a test coupon. Heat treatment of GP91 cast steel was performed at the parameters of temperature and time typical of treatment for multi-ton steel casts. The research has proved that in the as-cast state the GP91 cast steel was characterized by a coarse grain microstructure of lath martensite with precipitations of carbides such as: M₂₃C₆, M3C and NbC. The cast steel microstructure in the as-cast state ensured the required standard mechanical properties. Heat treatment of GP91 cast steel contributed to the obtainment of a fine grain microstructure of high tempered lath martensite with numerous precipitations of M₂₃C₆ and MX carbides of diverse size. The GP91 cast steel structure received by heat treatment made it possible to obtain high plastic properties, mainly impact strength, maintaining strength properties (yield strength (YS)) on the level of the required minimum.Представлено результаты исследований влияния различного вида многоэтапной термообработки на микроструктуру и свойства высокохромовой мартенситной литой стали GX12CrMoVNbN9-1 (GP91). Для исследований взято образцы, получённые из пробного слитка. Термообработку литой стали GP91 осуществляли в температурновременных параметрах, соответствующих обработке многотонного литья стали. Исследования показали, что в литом состоянии сталь GP91 имеет крупнозернистую микроструктуру пластинчатого мартенсита с содержанием карбидов типа M₂₃C₆, M3C и NbC, которая соответствует требуемым механическим свойствам по стандарту. С помощью термообработки литой стали GP91 получено мелкозернистую микроструктуру высокоотпущенного пластинчатого мартенсита с многочисленными вкраплениями типа M₂₃C₆ и МX различного размера. Структура литой стали GP91 после термообработки получила высокие пластические характеристики, преимущественно упругости, со свойствами прочности (границы пластичности) приближенные к требуемому минимуму.Подано результати досліджень впливу різного виду багатоетапної термо- обробки на мікроструктуру і властивості високохромової мартенситної литої сталі GX12CrMoVNbN9-1 (GP91). Для досліджень взято зразки, отримані з пробного злитка. Термообробку литої сталі GP91 здійснювали в температурно-часових параметрах, характерних для обробки багатотонного лиття сталі. Дослідження показали, що в литому стані сталь GP91 має грубозернисту мікроструктуру пластинчастого мартенситу із вмістом карбідів типу M₂₃C₆, M3C і NbC, яка відповідає механічним властивостям за стандартом. За допомогою термообробки литої сталі GP91 отримано дрібнозернисту мікроструктуру високовідпущеного пластинчастого мартенситу з чисельними вкрапленнями типу M₂₃C₆ і МX різного розміру. Структура литої сталі GP91 після термообробки одержала високі пластичні характеристики, переважно пружності, з властивостями міцності (межі пластичності) наближені до необхідного мінімуму

Is there an ideal way to initiate antiplatelet therapy with aspirin? A crossover study on healthy volunteers evaluating different dosing schemes with whole blood aggregometry

<p>Abstract</p> <p>Background</p> <p>Guidelines recommend an early initiation of aspirin treatment in patients with acute cerebral ischemia. Comparative studies on the best starting dose for initiating aspirin therapy to achieve a rapid antiplatelet effect do not exist. This study evaluated the platelet inhibitory effect in healthy volunteers by using three different aspirin loading doses to gain a model for initiating antiplatelet treatment in acute strokes patients.</p> <p>Methods</p> <p>Using whole blood aggregometry, this study with a prospective, uncontrolled, open, crossover design examined 12 healthy volunteers treated with three different aspirin loading doses: intravenous 500 mg aspirin, oral 500 mg aspirin, and a course of 200 mg aspirin on two subsequent days followed by a five-day course of 100 mg aspirin. Aspirin low response was defined as change of impedance exceeding 0 Ω after stimulation with arachidonic acid.</p> <p>Results</p> <p>Sufficient antiplatelet effectiveness was gained within 30 seconds when intravenous 500 mg aspirin was used. The mean time until antiplatelet effect was 74 minutes for 500 mg aspirin taken orally and 662 minutes (11.2 hours) for the dose scheme with 200 mg aspirin with a high inter- and intraindividual variability in those two regimes. Platelet aggregation returned to the baseline range during the wash-out phase within 4 days.</p> <p>Conclusion</p> <p>Our study reveals that the antiplatelet effect differs significantly between the three different aspirin starting dosages with a high inter- and intraindividual variability of antiplatelet response in our healthy volunteers. To ensure an early platelet inhibitory effect in acute stroke patients, it could be advantageous to initiate the therapy with an intravenous loading dose of 500 mg aspirin. However, clinical outcome studies must still define the best way to initiate antiplatelet treatment with aspirin.</p

Wpływ temperatury starzenia na mikrostrukturę i właściwości mechaniczne staliwa GX12CrMoVNbN9-1 (GP91

Increase in the steam parameters, the so-called supercritical parameters, resulted not only in the growth of efficiency of power units, or reduction in the emission of pollutants into the atmosphere, but also it has contributed to the development of heat-resisting steels and cast steels. One of the newly developed and implemented cast steels in the power industry is martensitic GX12CrMoVNbN9-1 (GP91) cast steel, created on the basis of chemical composition of P91 steel. The cast steel of a microstructure and properties similar to the base material replaces in the power industry the grades of steel used previously which do not meet the increasingly high requirements. A study has been made with regard to the effects of ageing at 550 and 600 degree Celsjus and time up to 6000 hrs on the changes in microstructure and mechanical properties of GX12CrMoVNbN9-1 (GP91) cast steel. A detailed microstructural research and the analysis of secondary phases was carried out using the electron microscopy technique, whilst the research on mechanical properties included a hardness test, static tensile test and impact strength measurement. The microstructural observations showed that the lath martensite microstructure was maintained after 6000 hrs. The coarsening of M23C6 carbides was revealed. Ageing of the investigated cast steel resulted in a slight decrease in the strength properties (Rp0:2, TS and HV30), i.e. of around 6%, which was accompanied by a significant decrease in impact strength KV. Moreover, in the microstructure of investigated cast steel there were the processes of recovery and polygonization of the matrix observed.Wzrost parametrów pary do tzw. parametrów nadkrytycznych skutkował nie tylko wzrostem sprawności bloków energetycznych, czy też zmniejszeniem emisji zanieczyszczeń do atmosfery, ale również przyczynił się do rozwoju stali i staliw żarowytrzymałych. Jednym z nowoopracowanych i wdrożonych do energetyki staliw było martenzytyczne staliwo GX12CrMoVNbN9-1 (GP91), które powstało na bazie składu chemicznego stali P91. Staliwo to o mikrostrukturze i właściwościach zbliżonych do materiału bazowego zastępuje w energetyce dotychczas stosowane gatunki staliw, które nie spełniają coraz to wyższych wymagań. W pracy przedstawiono badania wpływu starzenia w temperaturze 550 i 600 stopni Celsjusza oraz czasach wytrzymania do 6000 godzin na zmiany w mikrostrukturze i właściwościach mechanicznych staliwa GX12CrMoVNbN9-1 (GP91). Badania mikrostruktury staliwa GP91 w stanie wyjściowym oraz po starzeniu przeprowadzono za pomocą mikroskopii świetlnej i elektronowej. Wpływ temperatury i czasu starzenia na właściwości badanego staliwa określono za pomocą pomiaru twardości, statycznej próby rozciągania oraz próby udarności. Przeprowadzone badania wykazały: proces zdrowienia i poligonizacji osnowy oraz koagulacje wydzieleń M23C6. Zmiany w mikrostrukturze zachodzące w czasie starzenia w niewielkim stopniu wpłynęły na właściwości wytrzymałościowe (HV30, Rp0;2, Rm), natomiast przyczyniły sie do znacznego spadku udarności KV badanego staliwa

Wpływ naprawczego złącza spawanego na trwałość rurociągu pary ze stali Cr-Mo eksploatowanego powyżej obliczeniowego czasu pracy

The aim of the paper was to examine the influence of repair welded joints on the service life of steam pipelines for over 220 000 hours of service in creep conditions. The research included the study of the microstructure using scanning microscopy, the tests on mechanical properties at room and elevated temperature, determining the nil ductility transition temperature, and short-time creep tests to determine the residual life of the material. The tests allowed determining the time of further safe operation of elements of the steam pipeline with a repair welded joint, with reference to the base material, and the welded joint after service. The assessment of residual life and disposable residual life, and at the same time determining the possible time of further safe operation, has an essential meaning in the case of elements serviced considerably beyond the calculated working time.Celem pracy było zbadanie wpływu naprawczych złączy spawanych na trwałość eksploatacyjną rurociągów pary przez ponad 220 000 godzin eksploatacji warunkach pełzania. Wykonano badania mikrostruktury z wykorzystaniem mikroskopii skaningowej, badania właściwości mechanicznych w temperaturze pokojowej i podwyższonej, wyznaczono temperaturę przejścia w stan kruchy, przeprowadzono skrócone próby pełzania celem wyznaczenia trwałości resztkowej materiału. Przeprowadzone badania pozwoliły na wyznaczenie czasu dalszej bezpiecznej eksploatacji elementów rurociągu pary z wykonanym naprawczym złączem spawanym w odniesieniu do materiału rodzimego i złącza spawanego po eksploatacji. Ocena trwałości resztkowej i resztkowej trwałości rozporządzalnej, a tym samym oszacowanie lub wyznaczenie możliwego czasu dalszej bezpiecznej eksploatacji ma zasadnicze znaczenie w przypadku eksploatacji elementów znacznie poza obliczeniowy czas pracy