EBIC investigation of hydrogenation of crystal defects in EFG solar silicon ribbons

Changes in the contrast and resolution of defect structures in 205 Ohm-cm EFG polysilicon ribbon subjected to annealing and hydrogenation treatments were observed in a JEOL 733 Superprobe scanning electron microscope, using electron beam induced current (EBIC) collected at an A1 Schottky barrier. The Schottky barrier was formed by evaporation of A1 onto the cleaned and polished surface of the ribbon material. Measurement of beam energy, beam current, and the current induced in the Schottky diode enabled observations to be quantified. Exposure to hydrogen plasma increased charge collection efficiency. However, no simple causal relationship between the hydrogenation and charge collection efficiency could be inferred, because the collection efficiency also displayed an unexpected thermal dependence. Good quality intermediate-magnification (1000X-5400X) EBIC micrographs of several specific defect structures were obtained. Comparison of grown-in and stress-induced dislocations after annealing in vacuum at 500 C revealed that stress-induced dislocations are hydrogenated to a much greater degree than grown-in dislocations. The theoretical approximations used to predict EBIC contrast and resolution may not be entirely adequate to describe them under high beam energy and low beam current conditions

Creep of web ribbons

Results are reported for work in high-temperature deformatin of dendritic web ribbons, and oxygen measurement in the material

EBIC/TEM investigations of process-induced defects in EFG silicon ribbon

Electron bombardment induced conductivity and scanning transmission electron microscopy observations on unprocessed and processed edge-defined film-fed growth ribbon show that the phosphorus diffused junction depth is not uniform, and that a variety of chemical impurities precipitate out during processing. Two kinds of precipitates are found (1) 10 nm or less in size, located at the dislocation nodes in sub-boundary like dislocation arrangements formed during processing and (2) large precipitates, the chemical composition of which has been partially identified. These large precipitates emit dense dislocations tangles into the adjacent crystal volume

TEM observations on grain boundaries in sintered silicon, part 1

Grain boundaries in silicon with a predetermined orientation were prepared by the sintering of two single crystals. A combination of standard transmission electron microscopy and lattice imaging was used to investigate the structure of the boundaries produced. Low angle grain boundaries on (100) and (111) planes, and twin boundaries on (111) planes are discussed in detail

Carbon, oxygen and their interaction with intrinsic point defects in solar silicon ribbon material: A speculative approach

Some background information on intrinsic point defects is provided and on carbon and oxygen in silicon in so far as it may be relevant for the efficiency of solar cells fabricated from EFG ribbon material. The co-precipitation of carbon and oxygen and especially of carbon and silicon self interstitials are discussed. A simple model for the electrical activity of carbon-self-interstitial agglomerates is presented. The self-interstitial content of these agglomerates is assumed to determine their electrical activity and that both compressive stresses (high self-interstitial content) and tensile stresses (low self-interstitial content) give rise to electrical activity of the agglomerates. The self-interstitial content of these carbon-related agglomerates may be reduced by an appropriate high temperature treatment and enhanced by a supersaturation of self-interstitials generated during formation of the p-n junction of solar cells. Oxygen present in supersaturation in carbon-rich silicon may be induced to form SiO, precipitates by self-interstitials generated during phosphorus diffusion. It is proposed that the SiO2-Si interface of the precipates gives rise to a continuum of donor stables and that these interface states are responsible for at least part of the light inhancement effects observed in oxygen containing EFG silicon after phosphorus diffusion

Processed-induced defects in EFG ribbons

The defect structure of processed edge defined film-fed growth (EFG) silicon ribbons was studied using a variety of electron microscopic techniques. Comparison between the present results and previous studies on as-grown ribbons has shown that solar cell processing introduces additional defects into the ribbons. The creation of point defects during high temperature phosphorus diffusion induces dislocation climb, resulting in the formation of dislocation helices in the diffused layer

TEM and SEM (EBIC) investigations of silicon bicrystals

The electrical and structural properties of low and medium angle tilt grain boundaries in silicon bicrystals were studied in order to obtain insight into the mechanisms determining the recombination activity. The electrical behavior of these grain boundaries was studied with the EBIC technique. Schottky barriers rather than p-n junctions were used to avoid annealing induced changes of the structure and impurity content of the as-grown crystals. Transmission electron spectroscopy reveals that the 20 deg boundary is straight, homogeneous, and free of extrinsic dislocations. It is concluded that, in the samples studied, the electrical effect of grain boundaries appears to be independent of the boundary misorientation. The dominant influence appears to be impurity segregation effects to the boundary. Cleaner bicrystals are required to study intrinsic differences in the electrical activity of the two boundaries

The structure of 110 tilt boundaries in large area solar silicon

The models of Hornstra and their connection to the repeating group description of grain boundaries (7-10) are discussed. A model for the Sigma = 27 boundary containing a zig-zag arrangement of dislocations is constructed and it is shown that zig-zag models can account for the contrast features observed in high resolution transmission electron micrographs of second and third order twin boundaries in silicon. The boundaries discussed are symmetric with a 110 tilt axis and a (110) boundary plane in the median lattice (the median plane). The median lattice is identical in structure and halfway in orientation between the crystal lattices either side of the boundary

Equilibrium mobility in IGZO TFT: Existence of the intermediate boolchand phase?

This talk will consider the applicability of modern topological constraint theory of glass developed by Boolchand, Thorp and Phillips (BTP) to IGZO and ask if it might explain the high (compared to spins) H content of a-Si:H. Please click Additional Files below to see the full abstract

EBIC/TEM investigations of defects in solar silicon ribbon materials

Transmission electron microscopy was used to investigate the defect structure of edge defined film growth (EFG) material, web dentritic ribbons (WEB), and ribbon to ribbon recrystallized material (RTR). The most common defects in all these materials are coherent first order twin boundaries. These coherent twins can be very thin, a few atomic layers. Bundles of the twins which contain odd numbers of twins will in optical images appear as a seemingly single first twin boundary. First-order coherent twin boundaries are not electrically active, except at locations where they contain intrinsic (grain boundary) dislocations. These dislocations take up small deviations from the ideal twin relation and play the same role in twin boundaries as conventional and play the some role in twin boundaries as conventional edge and screw dislocations in small angle tilt and twist boundaries