Bond Strength of Epiphany Sealer Prepared with Resinous Solvent

This study evaluated in vitro the bond strength of Epiphany sealer prepared with resinous solvent of Epiphany system (Thinning resin) by using a push-out test. Forty maxillary canines were sectioned transversally below the cementoenamel junction to provide 4-mm-thick dentin disks that were centered in aluminum rings and embedded in acrylic resin. Root canals were prepared with tapered diamond bur. Intraradicular dentin was treated with 1% NaOCl for 30 minutes, 17% ethylenediaminetetraacetic acid for 5 minutes, and flushed with distilled water for 1 minute. The specimens were randomly distributed into 4 groups (n = 10) according to the filling material: GI, Epiphany without photoactivation; GII, Epiphany prepared with solvent without photoactivation; Gill, Epiphany followed by photoactivation; and GIV, Epiphany prepared with solvent followed by photoactivation. After the setting time, the specimens were submitted to the push-out test. The highest mean value (14.91 +/- 2.82 MPa) was obtained with Epiphany prepared with solvent followed by photoactivation (GIV), which was statistically different (P < .01) from the other groups. Groups I (8.15 +/- 2.47 MPa), II (9.46 +/- 2.38 MPa), and III (9.80 +/- 2.51 MPa) had inferior bond strength values and were statistically similar among themselves (P > .01). The resinous solvent of Epiphany system increased the bond strength of Epiphany sealer to dentin walls when followed by photoactivation. (J Endod 2009;35: 251-255

Influence of root dentin treatment on the push-out bond strength of fibre-reinforced posts

Abstract This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols

Effects of various irrigation/aspiration protocols on cleaning of flattened root canals

This study aimed to evaluate, by means of scanning electron microscopy (SEM), the cleaning of flattened root canals, varying irrigation/aspiration protocols during biomechanical preparation. Thirdy human mandibular incisors were distributed into three groups (n = 10) according to the aspiration/irrigation protocols: conventional, conventional + brush, and apical negative pressure irrigation. Irrigation procedure was performed with 5 mL of 1% NaOCl at each change of instrument; final irrigation was conducted with 17% EDTA for 5 min. After biomechanical preparation, the roots were sectioned and prepared for SEM analysis. The images obtained were evaluated under 35× and 1,000× magnification by three calibrated examiners, following a double-blind design. All data were analyzed using Kruskal–Wallis and Dunn’s post hoctests (α = 0.05). Canals wherein the conventional method and apical negative pressure irrigation were employed revealed less debris, statistically different from the conventional + brush group (p 0.05), both for the presence of debris and smear layer. In conclusion, although none of the studied irrigation/aspiration protocols have completely cleaned flattened root canals, apical negative pressure irrigation was more effective in smear layer removal, whereas the conventional + brush protocol was the least effective in removing the debris and smear layer

Influence of solvents on the bond strength of resin sealer to intraradicular dentin after retreatment

Abstract This study evaluated the removal of filling material with ProTaper Universal Rotary Retreatment system (PTR) combined with solvents and the influence of solvents on the bond strength (PBS) of sealer to intraradicular dentin after canal reobturation. Roots were endodontically treated and distributed to five groups (n = 12). The control group was not retreated. In the four experimental groups, canals were retreated with PTR alone or in combination with xylol, orange oil, and eucalyptol. After filling material removal, two specimens of each group were analysed by SEM and µCT to verify the presence of filling remnants on root canal walls. The other roots were reobturated and sectioned in 1-mm-thick dentin slices that were subjected to the push-out test. Data were analysed by two-way ANOVA and Tukey’s test (α = 0.05). SEM and µCT analysis revealed that all retreatment techniques left filling remnants on canal walls. The control group (3.47 ± 1.21) presented significantly higher (p 0.05), and differed significantly from the group with eucalyptol (1.89 ± 0.63). The solvents reduced the PBS of the sealer to dentin and no retreatment technique promoted complete removal of filling material