An evaluation of the fatigue crack growth and fracture toughness properties of beryllium-copper alloy CDA172

A series of fracture mechanics tests, using the Be-Cu alloy CDA172 in the round rod product form, was conducted in a lab air environment at room temperature. Tensile data is presented in both the L and C directions and K sub Ic data in both the C-R and C-L orientations. Fracture toughness values were derived from M(T) (center cracked), PS(T) (surface cracked) and CC01 (corner cracked) specimens of varying thickness. Fatigue crack growth data were obtained for the C-R orientation at stress ratio of 0.1, 0.4, and 0.7 and for the C-L orientation at stress ratios of 0.1, 0.3, 0.4, and 0.7

Behavior of surface and corner cracks subjected to tensile and bending loads in Ti-6Al-4V alloy

The behavior of part-through flaws with regard to failure under monotonic loading and their growth under fatigue loading was studied experimentally and analytically. Comparisons are made of experimental values of toughness obtained using surface and corner cracked specimens with those obtained using standard test specimens, and also experimental growth cycles were compared with numerical predictions using the NASA/FLAGRO computer program. Tests were conducted on various types of surface and corner cracks under tensile and bending loads. Room temperature lab air provided the test environment. The material used in this study was the Ti-6Al-4V alloy in the solution treated and aged (STA) and stress relieved condition. Detailed tabulation of the fracture toughness data and results of life prediction using the NASA/FLAGRO program are presented. Fatigue crack growth rates for the part-through cracked specimens are compared with a base curve fitted from the data obtained using standard specimens. The fatigue loading used in the crack growth testing was constant-amplitude sinusoidal type

Ion sputter textured graphite

A specially textured surface of pyrolytic graphite exhibits extremely low yields of secondary electrons and reduced numbers of reflected primary electrons after impingement of high energy primary electrons. An ion flux having an energy between 500 eV and 1000 eV and a current density between 1.0 mA/sq cm and 6.0 mA/sq cm produces surface roughening or texturing which is in the form of needles or spines. Such textured surfaces are especially useful as anode collector plates in high efficiency electron tube devices

Ion sputter textured graphite electrode plates

A specially textured surface of pyrolytic graphite exhibits extremely low yields of secondary electrons and reduced numbers of reflected primary electrons after impingement of high energy primary electrons. Electrode plates of this material are used in multistage depressed collectors. An ion flux having an energy between 500 iV and 1000 iV and a current density between 1.0 mA/sq cm and 6.0 mA/sq cm produces surface roughening or texturing which is in the form of needles or spires. Such textured surfaces are especially useful as anode collector plates in high tube devices

Flaw growth behavior in thick welded plates of 2219-T87 aluminum at room and cryogenic temperatures

Axial load fatigue and fracture tests were conducted on thick welded plates of 2219-T87 aluminum alloy to determine the tensile strength properties and the flaw growth behavior in electron beam, gas metal arc, and pulse current gas tungsten arc welds for plates 6.35 centimeters (2.5 in.) thick. The tests were conducted in room temperature air and in liquid nitrogen environments. Specimens were tested in both the as-welded and the aged after welding conditions. The experimental crack growth rate were correlated with theoretical crack growth rate predictions for semielliptical surface flaws

Cosmic ray diffusion fronts in the Virgo cluster

The pair of large radio lobes in the Virgo cluster, each about 23 kpc in radius, have curiously sharp outer edges where the radio-synchrotron continuum flux declines abruptly. However, just adjacent to this sharp transition, the radio flux increases. This radio limb-brightening is observed over at least half of the perimeter of both lobes. We describe slowly propagating steady state diffusion fronts that explain these counterintuitive features. Because of the natural buoyancy of radio lobes, the magnetic field is largely tangent to the lobe boundary, an alignment that polarizes the radio emission and dramatically reduces the diffusion coefficient of relativistic electrons. As cosmic ray electrons diffuse slowly into the cluster gas, the local magnetic field and gas density are reduced as gas flows back toward the radio lobe. Radio emission peaks can occur because the synchrotron emissivity increases with magnetic field and then decreases with the density of non-thermal electrons. A detailed comparison of steady diffusion fronts with quantitative radio observations may reveal information about the spatial variation of magnetic fields and the diffusion coefficient of relativistic electrons. On larger scales, some reduction of the gas density inside the Virgo lobes due to cosmic ray pressure must occur and may be measurable. Such X-ray observations could reveal important information about the presence of otherwise unobservable non-thermal components such as relativistic electrons of low energy or proton cosmic rays.Comment: 11 pages, 5 figures, Accepted by Ap

Data base for crack growth properties of materials

A computerized data base of crack growth properties of materials was developed for use in fracture control analysis of rocket engine components and other NASA space hardware. The software system has files of basic crack growth rate data, other fracture mechanics material properties such as fracture toughness and environmental crack growth threshold values, and plotting and fitting routines for deriving material properties for use in fracture control analysis. An extensive amount of data was collected and entered, and work is continuing on compiling additional data. The data base and software codes are useful both for fracture control analysis and for evaluation or development of improved crack growth theories

On the Crack Bifurcation and Fanning of Crack Growth Data

Crack growth data obtained from ASTM load shedding method for different R values show some fanning especially for aluminum alloys. It is believed by the authors and it has been shown before that the observed fanning is due to the crack bifurcation occurs in the near threshold region which is a function of intrinsic properties of the alloy. Therefore, validity of the ASTM load shedding test procedure and results is confirmed. However, this position has been argued by some experimentalists who believe the fanning is an artifact of the test procedure and thus the obtained results are invalid. It has been shown that using a special test procedure such as using compressively pre-cracked specimens will eliminate the fanning effect. Since not using the fanned data fit can result in a significantly lower calculated cyclic life, design of a component, particularly for rotorcraft and propeller systems will considerably be impacted and therefore this study is of paramount importance. In this effort both test procedures i.e. ASTM load shedding and the proposed compressive pre-cracking have been used to study the fatigue crack growth behavior of compact tension specimens made of aluminum alloy 2524-T3. Fatigue crack growth paths have been closely observed using SEM machines to investigate the effects of compression pre-cracking on the crack bifurcation behavior. The results of this study will shed a light on resolving the existing argument by better understanding of near threshold fatigue crack growth behavior

Crack Growth Behavior in the Threshold Region for High Cycle Fatigue Loading

This paper describes the results of a research program conducted to improve the understanding of fatigue crack growth rate behavior in the threshold growth rate region and to answer a question on the validity of threshold region test data. The validity question relates to the view held by some experimentalists that using the ASTM load shedding test method does not produce valid threshold test results and material properties. The question involves the fanning behavior observed in threshold region of da/dN plots for some materials in which the low R-ratio data fans out from the high R-ratio data. This fanning behavior or elevation of threshold values in the low R-ratio tests is generally assumed to be caused by an increase in crack closure in the low R-ratio tests. Also, the increase in crack closure is assumed by some experimentalists to result from using the ASTM load shedding test procedure. The belief is that this procedure induces load history effects which cause remote closure from plasticity and/or roughness changes in the surface morphology. However, experimental studies performed by the authors have shown that the increase in crack closure is a result of extensive crack tip bifurcations that can occur in some materials, particularly in aluminum alloys, when the crack tip cyclic yield zone size becomes less than the grain size of the alloy. This behavior is related to the high stacking fault energy (SFE) property of aluminum alloys which results in easier slip characteristics. Therefore, the fanning behavior which occurs in aluminum alloys is a function of intrinsic dislocation property of the alloy, and therefore, the fanned data does represent the true threshold properties of the material. However, for the corrosion sensitive steel alloys tested in laboratory air, the occurrence of fanning results from fretting corrosion at the crack tips, and these results should not be considered to be representative of valid threshold properties because the fanning is eliminated when testing is performed in dry air